Evalluation of Biocompatibility on the Self-developed Alloy: Ni-Cr-Ti Alloy

Author: FangZuo
Tutor: ZhanDeSong
School: China Medical University
Course: Clinical Stomatology
Keywords: Ni - Cr - Ti alloy Ni - Cr alloy biocompatibility haemolysis mucosa irritation
CLC: R783.1
Type: Master's thesis
Year: 2006
Downloads: 47
Quote: 0
Read: Download Dissertation

Abstract


ObjectiveIn this study the haemolysis test was performed firstly, then the oral mucous membrane irritation test was performed as the test before clinical application. This study was to evaluate the biocompatibility on the self - developed Ni - Cr — Ti alloy and the Ni — Cr alloy in vitro.Material and Methods1. Haemolysis testthe self - developed Ni - Cr - Ti alloy was fashioned into 2. Ocm * 1. 0cm * 1. Ocm rectangle piece. Put them separately in the cuvette with 10ml physiological saline solution as the test group, and the group in distilled water was teken as the control group. Then put 0. 2ml the anticoagulant rabbit blood into each cuvette. After it was centrifugated by centrifugal, we took the serum. Then mensurated the magnitude of light that was absorbed in 540nm wavelength by spectrophotometer and calculated the rate of haemolysis.2. Oral mucous membrane irritation testThis two alloys were taken as the test materials, and PVC (PolyvinylChlo-ride) as positive control, and porcelain as negative control. All the materials were maken into wafer with 6mm diameter and 0. 5mm thickness. These wafers were fixed to the oral cheek pouch mucosa. 14 days after the operation, it was detected wether there was erosion, ulcer, hyperaemia, edema. Then the whole mucous membrane layer was taken and sliced, observed in microscope.

Related Dissertations

  1. , Ni-Cr , high stability , a thin film resistor,O484.42
  2. Bond Characteristics Between Porcelain and Ni-cr Alloy Fabricated by Laser Rapid Forming,R783
  3. Solution and Aging 00Cr25Ni35AlTi microstructure and properties of,TG156
  4. Experimental Study of the Bonding Characterization of Dental Porcelain to Ni-Cr-Ti Alloys in the Shear Test,R783.1
  5. Researches on the Attrition Resistance of the Gold-paste Layer and the Layer Application Effects on the Cementation for PFM,R783.3
  6. In Vitro Study on the Ion Release from Two Ni-Cr Dental Alloys,R783.1
  7. Study on the Relationship of Ni-Cr Alloy and Artifact of MRI,R445.2
  8. An Electrochemical Study on Corrosion Behaviors of Ni-Cr Alloy, Ni-Cr Alloy with Electroplated Au Film and Au Alloy in Artificial Saliva,R783
  9. New Type of Te-Ni-Cr Alloy of the High-temperature Oxidation Resistance,TG146.15
  10. The Clinical Aesthetic Study of Three PFM,R783
  11. The Contrastive Research on the Corrosion Resistance of Ni-Cr Alloy with Different Coatings,R783.1
  12. The Corrosion Resistance of Ni-Cr Alloy, Ni-Cr Alloy with Titanium and Alloys after Surface Treatment,R783.1
  13. Study on the Interface Behavior for the Porcelain Fused to Ni-Cr Alloy,R318.08
  14. The Influence on the Nickel Ion Release of Ni-Cr Alloy Plated with Nano-amorphous Diamond Film,R783
  15. Study on the Corrosion Behavior of the New Type of Te- Ni-Cr Alloy,TG174.3
  16. A Study of the Relationship between Ultrasound Images of Masicatory Muscle and Caraniofical Morphlogy of Young Males with Nomal Occlusion,R783.5
  17. Experiments Study of BIO-OSS on PRP Composite Repairing Bone Defect around Metal Nail of Pure Titanium,R783.6
  18. Root Resorption of Upper Centre Incisor with Compensation in Skeletal Class Ⅱ and Ⅲ Malocclusions,R783.5
  19. Several Low Flat Mandibular Alveolar Ridge to Improve Denture Retention Methods of Clinical Experience,R783.6
  20. The Dual-phase Treatment of Skeletal Class Ⅲ Malocclusion.,R783.5
  21. The Combined Treatment of Complex Adult Angleclass Ⅱ Division 1,R783.5

CLC: > Medicine, health > Oral Sciences > Oral orthotics > Dental Materials Science
© 2012 www.DissertationTopic.Net  Mobile