Study on the Melt Blending Modification of Poly(Vinyl Chloride)

Author: LiLiuBin
Tutor: DongLiJie；XiongChuanXi
School: Wuhan University of Technology
Course: Materials Science
Keywords: Poly (Vinyl Chloride) Polyamide 6 VM Carbon nanotube fluids Melt blending
CLC: TB383.1
Type: Master's thesis
Year: 2008
Downloads: 244
Quote: 1
Read: Download Dissertation

Abstract


On the basis of consulting plenty of references about poly(vinyl chloride)(PVC) blending modification,surface function of carbon nanotubes(CNTs),ionic liquids and polymer matrix nanocomposites,two new ideas improving PVC by using the modified polyamide6(PA6)and carbon nanotube fluids are proposed.The main results can be summarized as follows:During the processes of PVC melt-blending modification by using PA6,firstly,the copolymer VM was synthesized by copolymerization of Vinyl Acetate and Maleic Anhydride.Then grafting copolymer VM-g-PA6 was obtained by melt blending of VM and PA6.Fourier transform infrared(FT-IR)spectroscopy demonstrated the successful grafting reaction of PA6 and VM.With the increasing amount of VM,the melting point of PA6 decreased gradually,and the minimum temperature fell down to 204℃.Blends of PVC and VM-g-PA6 were obtained by melt blending.Mechanical testing results of the blends showed that tensile strength increased with the increasing amount of VM-g-PA6,yet non-notched impact strength decreased at the same addition.Scanning Electron Microscopy(SEM)images showed that fracture mode of the blend samples were brittle fracture.Carbon nanotubes(CNTFs)were oxidized by using the mixture of concentrated sulfuric and nitric acids to introduce functional carbonyl and hydroxyl groups into the surface of CNTs.Subsequently,DC5700 and NPES reacted with the functional groups of the CNTs to yield a bilayer organic coating,namely the product of carbon nanotube fluids(CNTFs).The product was characterized by Fourier transform infrared(FT-IR), Thermo-gravimetric analysis(TGA),Differential scanning calorimeter(DSC)and Advanced Rheometric Expansion System(ARES)Rheometer.Results demonstrated successful chemical grafting of DC5700 and NPES into the CNTs structure and excellent fluidity of the CNTFs.The organic content of the CNTFs is about 84.8% with the remaining 15.2%attributed to CNTs.The nanocomposites of CNTFs/PVC were melting blended in a torque rheometer. The nanocomposites exhibit excellent mechanical properties attributed to addition of CNTFs.Compared to the tensile strength value 39.9MPa of neat PVC,it was improved up to 53.9MPa,which means about 35%increment.Meanwhile,the non-notched impact strength increased from 10.5MPa to the maximum value 14.8MPa,sum up to 40.6%.In addition,elongation also increased with the increasing amount of CNTFs.The rheological property of the composite was tested in a torque rheometer.After the addition of 5wt%CNTFs,the maximum torque decreased from 71N·m to 59.6N·m,and balanceable torque decreased from 35.6N·m to 30.1N·m. Results showed that CNTFs can be used as plasticizer of PVC.In a word,the CNTFs are excellent materials for plasticizing,reinforcing and toughening of PVC. Meanwhile,the CNTFs also increased the heat resistance properties of the composites and inhibited cross-linking of the resin effectively.

Related Dissertations

  1. Properties and Application Research of Multi-Antibacterial Polyamide Fibers,TQ342.1
  2. Study on the Spinnability of Semi-Aromatic Polyamide,TQ340.1
  3. Dendrimer stabilized bismuth sulfide nanoparticles synthesis , characterization and application of CT imaging,O614.532
  4. Novel sulfonated aromatic polyamide and aromatic polyamide of,TQ323.6
  5. Synthesis and Application of Polyamidoamine Dendrimer with a Triethanolamine Core,TB383.1
  6. Synthesis and Application of Novel Polyamide Resin,TQ323.7
  7. Malicious Code Detection and Auditing Based on Hardware Virtualization Technology,TP393.08
  8. Synthesis, Modification of Polyamidoamine Dendrime and Its Application in Fixing,TS529
  9. Study on Morphology, Properties and Toughening Mechanism of Sandbag Microstructure-Toughened PA6/EPDM/nano-CaCO3 Ternary Composites,TB332
  10. Surface Modification of Aromatic Polyamide Reverse Osmosis Membrane by Grafting 3-allyl-5, 5-dimethylhydantoin,TB383.2
  11. Study on Preparation and Application Performance of Boron Nitride Nano Materials,TB383.1
  12. Study on New Technique of Biodiesel Production and Its Value-increment from Chinese Tallow Kernel Oil,TE667
  13. The Study of Flame Retarded and Antistatic Polyamide-6 Composites,TQ323.6
  14. The Coagulating Performance of PMIA Serum and the Preparation of Dope-dyed PMIA Fiber,TQ340.6
  15. Modification Research on Reactive Blending of Poly (Β-Hydroxybutyrate-Co-Β-Hydroxybutyvalerate),TQ316.33
  16. The Preparation of Modified Melamine Cyanurate and Study on the Flame Retardant Polyamide 6,TQ323.6
  17. Study on Preparation and Functionalization of Self-cleaning Glass,TQ171.7
  18. The Research of Key Techniques of Trusted -Application Execution Mechanism Based on Virtual Machine Technology,TP309
  19. Studies on Preparation and Performance of Polyamide Composite Forward Osmosis Membrane,P734
  20. Preparation and Characterization of Composite Nanofibers Based on PA6 Nanofibers,TQ342.11
  21. Synthesis, Characterization and Catalytic Activity of Polyamidoamine-salicylaldehyde Schiff Base Dendrimer Palladium Complex,O634

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile