The Preparation of Aluminum-Ammonium Cationic Starch and Its Application in Papermaking

Author: ChenMeiYan
Tutor: ZuoYongXiang
School: Changsha University of Science and Technology
Course: Applied Chemistry
Keywords: Aluminum-ammonium cationic starch (ACS) dimethyl-diallyl ammonium chloride aluminum sol graft copolymerization retention agent
CLC: TS727
Type: Master's thesis
Year: 2011
Downloads: 13
Quote: 0
Read: Download Dissertation

Abstract


Cationic starch can be widely used in papermaking, medicine, sewage treatment and other industries, and the performance of a single property cationic starch is limited, and does not apply to the modern development of new technologies, new processes and new equipment requirements. The aluminum ammonium cationic starch (ACS) we developed has higher charge density, and its transparency is better than ordinary gelatinized starch. So it is a solution to these problems above.We studied the preparation of the ACS in this paper. We used the ordinary starch, dimethyl-diallyl ammonium chloride and aluminum sol as the raw material, cerium ammonium nitrate as initiator, synthesized the three graft copolymer. By single factor analysis and orthogonal experiments, detailed study the influences on the nitrogen content of the product, such as the initiator, monomer amount, aluminum sol amount, H2O: St, reaction temperature and reaction time. and Experiments show that the best preparation conditions are: the amount of initiator is 0.54%, the monomer is 50%,the aluminum sol is 3.5%, reaction temperature is 55℃, reaction time is 3h, H2O: St = 2:1. Its molecular weight is low, and it has higher charge density and a moderate degree of substitution. And its transparency is better than ordinary cationic starch; its nitrogen content is about 0.58%, higher than the ordinary cationic starch (CS) (0.30%).Charge density analysis shows that the charge density of ACS is higher than the ordinary cationic starch; We use UV spectrophotometry to analysis the aluminum content of ACS; scanning electron microscope analysis shows that the graft copolymerization of ACS both happen in the surface and the within cationic starch granule; infrared spectrum analysis shows that the structure of DADMAC exists in the grafts. All the above shows that the monomer is successfully introduced into the CS, and make it into a cationic starch with higher nitrogen content, thus confirming the feasibility of wet preparation of ACS.We discussed the effect on the physical properties of the paper when ACS were respectively used in deinking pulp, bleached reed pulp and unbleached eucalyptus pulp in different amount, it investigated the application effects of ACS, and were compared with CS. Application results show that, ACS made a good retention effect in DIP and unbleached eucalyptus pulp, and its retention effect on the bleaching of chemical wood pulp is general, the addition which with the best retention effect is 0.75% to 1.0%. The minimum white water turbidity respectively were 5.2NTU, 4.2NTU and 3.0NTU when it used in the three above, and the highest ash content was 23.27%, 10.83% and 11.48%. When compared ACS by adding the same amount in the three pulp with CS, we found that, ACS has better flocculation and retention effect than CS regardless of what kind of slurry. ACS went with dual role of retention and enhancement, it can simultaneously improve the paper strength and the retention of fine fibers.

Related Dissertations

  1. The Preparation of Chitosan Grafted with Maleic Anhydride and Itaconic Acid and the Research of the Inhibition Performance,TQ085.4
  2. The application and research of carboxymethyl cellulose-based water-based fracturing fluid thickener,TE357
  3. Synthesis and Performance Study of Chitosan Surfactant,TQ423
  4. Study on the Preparation and Application of Super Absorbent Polymer Made from Corn Starch-acrylic Acid Graft,TQ324.8
  5. Study on Preparation and Properties of Polymer Ceramic Dispersant,TQ174.4
  6. Research on Solid-phase Grafting Modification of Pp with Binary-monomer,TQ325.14
  7. Effect of Floc Characteristics on Disinfection by-products Precursors Removal,TU991.2
  8. Preparation of Cellulose Based Oil Absorption Materials and Research of Its Property,TQ324.8
  9. Improvement of Anticoagulation Behaviour of Catheter via Grafting Copolymerization of Hydrophilic Monomers,R318.08
  10. Environmental protection and water emulsion function Latex Characterization and Application of,TQ316.334
  11. Preparation of Poly (Vinylidene Fluoride) (PVDF) Hydrophilic Membranes by Ozone-Induced Graft Copolymerization,TQ320.721
  12. Study on Raft Agent Assisted Graft Copolymerization of Methyl Acrylate onto Chitosan and RAFT Polymerization of Methyl Methacrylate,O631
  13. The Study of Modification of Concentration Bioflocculant,X703.5
  14. 60Coγ-ray Irradiation Lead to the Preparation of Starch Graft Copolymer and the Nature of the Research,TQ324.8
  15. Study on the Synthesis and Adsorption Properties of Modified Palygorskite,O611.3
  16. Study of Super Absorbent Polymer Prepared by Cotton Waste,TQ324.8
  17. The Application Study on Using Recycled Polypropylene in Wood Plastic Composites,TQ320.7
  18. Synthesis, Characterization and Performance Study of Ethyl Cellulose Graft Poly (L-lactic Acid) Copolymer,O631.3
  19. Synthesis and Evaluation of the Thinner for Drilling Fluid,TE254
  20. The Toughening Investigation of PVC Blending with Modified CPE and Blending Reaction with Nonelastomer,TQ325.3

CLC: > Industrial Technology > Light industry,handicrafts > Paper Industry > Raw materials and auxiliary materials > Auxiliary materials
© 2012 www.DissertationTopic.Net  Mobile