Fabrication and Characterization of Nano-ZnO by PLA in Liquid Solution

Author: FangHe
Tutor: TangWeiHua
School: Zhejiang University of Technology
Course:
Keywords: pulsed laser ablation surfactant nano-ZnO Zn/ZnO core/shell structure defect photoluminescence
CLC: TB383.1
Type: Master's thesis
Year: 2011
Downloads: 31
Quote: 1
Read: Download Dissertation

Abstract


We applied a novel method called pulsed laser ablation in liquid (PLA) to synthesize nano-ZnO. We mainly studied the effects of different solution, ablation time and solution concentration on structure, morphololy, size, optical and photoluminescence properties of nano-ZnO, and also investigated formation mechanism and defect photoluminescence. The results can be summarized as follows:1. ZnO nanoparticles were synthesized by ablating zinc target in deionized water. The mean diameters of ZnO nanoparticles are 43 nm and 19 nm, respectively, after ablating the zinc target for 2 and 4 hours in deionized water. The longer-time ablation may lead to the interaction of the ablating laser beam with the ZnO nanoparticles, resulting in the decrease of the mean diameter of ZnO nanoparticles.2. Zn/ZnO core/shell structured nanoparticles were synthesized by ablating zinc target in 0.005mol/L sodium dodecyl sulfate (SDS) solution. The formation of this core/shell structured nanoparticles was due to the enwrapping of SDS to part of the Zn clusters. The bilayer of SDS molecules which could inhibit reaction between Zn clusters and liquid solution were formed on Zn clusters surface.3. The uneven Flake-like nano-ZnO was synthesized by ablating zinc target in different concentration cetyltrimethylammonium bromide (CTAB) solution. The uneven Flake-like nano-ZnO was formed by self-assembly,which is attributed to electrostatic repulsion between CTAB molecules and nano-ZnO. In the process of self-assembly, the small nano-ZnO self-attach to build a bigger nanostructured assembly by self-adjusting and by lattice fusion.4. The photoluminescence property of the uneven Flake-like nano-ZnO was investigated. A violet photoluminescence peak at about 411 nm was due to zinc interstitials in lattice. Blue photoluminescence peaks from 450 nm to 436 nm was due to derivative zinc interstitials in lattice. And a green photoluminescence peak at about 558 nm was due to oxygen vacancies. We also investigated the different concentration of CTAB that affect on the defects of uneven Flake-like nano-ZnO, and thouht the best concentration of CTAB that could passivate the defects of zinc interstitials was critical micell concentration. But CTAB could not passivate the defects of oxygen vacancies. A blue shift of blue photoluminescence peak from 450 nm to 436 nm was due to the increasing of Zni(?)、Zni(?)(?) with the increasing of Zni.

Related Dissertations

  1. Research on High-performance Silicone Resins for LED Packaging,TQ324.21
  2. Preparation and Research of the PbSe Quautum Dot Doped PMMA Fiber Materials,TB383.1
  3. Synthesis of Uniform Magnetite Nanoparticles Via W/O Interface System Applied as Bio-Labels,TB383.1
  4. An Approach to Study the Protective Performance of Nano ZnO, TiO2 Modified Bamboo,TS652
  5. Hydrothermal Preparation and characterization of nano - ZnO and yttrium aluminum garnet,TB383.1
  6. The Study about Bottle-shaped and Rod-like Nano ZnO Photo-catalytic Different Soluble Dyes,TB383.1
  7. Preparation and Recycling Nano-ZnO Composites,TQ426.81
  8. Synthesis of Some Pyrimidine Compounds in Aqueous Media,O621.3
  9. Study on the Preparation and Antibacterial Activity of Nano-ZnO and ZnO-Ag Heterostructure,TB383.1
  10. The microemulsion prepared nano ZnO their study of the performance,TB383.1
  11. Synthesis and Characterization of the amino acid surfactant,TQ423
  12. Study on the Preparion and Photo-catalytic Capability of Metal Ion Doped Nano Zinc Oxide,O643.36
  13. Study on Synthesize and Properties of Non-Stoichiometric LiFePO4 via Hydrothermal Method,TM912.9
  14. Study on Surfactant Assisted Synthesis of Lithium Iron Phosphate,TM912.9
  15. Biomimetic Synthesis and Assembly of Inorganic Nanoparticles in the Presence of Metal (Ca, Mg) Dodecyl Sulfates,TB383.1
  16. Study on the Corrosivity and Desulfurization of Light Oil,TE624.5
  17. Study on Electric Conductive Properties of Silk Fabric Treated with ZnO Sol,TB383.1
  18. Synthesis and Properties of APG,TQ423
  19. Synthesis and Properties of octadecyl dimethyl hydroxyethyl ammonium bromide,TQ423
  20. Assembly and Magnetic Research of In-situ Modified Nano-YBCO Prepared by Pulsed Laser Ablation in Gas,TB383.1
  21. Improved Performance of Microbial Fuel Cell and Treatment of Antibiotic Wastewater,X787

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile