Optimization Reasearch on Strength and Toughness of Low Carbon Mn-series Air Cooling Bainitic Steel

Author: WangYongWei
Tutor: BaiBingZhe
School: Tsinghua University
Course: Materials Science and Engineering
Keywords: bainite risidul stress strength and toughness thermal deformation micro-alloyed
CLC: TG142.15
Type: PhD thesis
Year: 2009
Downloads: 769
Quote: 1
Read: Download Dissertation

Abstract


Mn-series banitic steels with carbon content 0.07wt%-0.30wt% have been selected as the test materials in this paper. The methods of optimization on the strenghth and toughness of the steel have been systematically studied. The microstructures of Mn-series banitic steels of different carbon content and Si content and the changing of properties of the steels after air cooling and tempering have been studied. Phase transformation and the morphology of islands of granular structure were studied. The steels with the carbon content of about 0.08% were tested on Gleeble thermal-mechanical simulator machine, and the microstructures of non micro-alloyed and micro-alloyed steels were investigated after deformation at different temperature. The researching results were verified well by means of control rolling on testing rolling mills. The main conclusions of the paper are drawn as follows:1. Si almost has no influence on the microstructures of the steels with the carbon content 0.07～0.08%, but can improve the hardenbility of the steels with the carbon content 0.17%.2. The morphologies of M/A islands in the granular structure are two types: irregular and regular. The parallel islands are sensitive to form when the matrix grow in ledgewise mechanism. The islands parallelly or irregularly distributing are not the criterion of granular bainite and granular structure. The transformation of granular structure can be efficiently inhibited by Cr, so there are no islands in the proeutcoid ferrite.3. The huge macro residual stress will be remained in Mn-series bainitic steels after air cooling, result in low yield strength, and the stress will be efficiently eliminated after tempering at low temperature and the optimum temperature is about 400℃. The strength and toughness of the high Si content of the steels can match better after tempering at low temperature.4. The content of ferrite in low carbon Mn-series increases with the deformation temperature decreased, and the grains and toughness are refined and improved. The microstructures of the Nb micro-alloyed steel are more refined on the same deformation process, and the ferrites keeps a relatively stable content when the deformation temperature decrease to about 760℃. However the grain refined further and the transformation of ferrites turns to nucleation dominated process. The strength and toughness of Nb Micro-alloyed Mn Series Bainitic Steels are more sensitive to the finishing rolling temperature, and the properties of Nb Micro-alloyed steels can be improved more effectively with decreasing the finishing rolling temperature.5. The reinforced bar with the yeild strength 930MPa has been developed and the microstructure is B/M dual phase, the process is simple and cost is low, and successfully industrialized. The non-moderating medium plate with high strength and toughness has been developed, and the microstructure includes FGBA、intragranular ferrite、granular bainite, the properties are: R0.2﹥600MPa, Rm﹥800MPa, AKV(0℃)﹥150J after control rolling and air cooling。

Related Dissertations

  1. A508-3 nuclear power transformation plasticity of steel forgings and Numerical Simulation,TL341
  2. Study on Controlling of Transverse Corner Crack Occurrence for CC Slabs at Pansteel,TF777
  3. The PQ600 high strength engineering machinery steel hot rolling process research,TG335.11
  4. 10CrNi5Mo steel special plate of the relationship between the organization and the performance,TG142.1
  5. Micro- alloying elements in the hot rolling process numerical simulation of elution,TG335.11
  6. Research on Transformation Mechanism of Bainite and Martensite in Steel of 35CrMo Ect.,TG111.5
  7. Research on Squeeze Casting Technology for High Strength and Toughness Aluminum Alloy Parts,TG249.2
  8. Bainitic Cold strengthen non- quenched and tempered steel microstructure and mechanical properties of,TG142.1
  9. PQ600 low alloy high strength steel welding HAZ microstructure and properties,TG457.11
  10. Microstructure and metallurgical quality on the micro- alloying non-quenched and tempered steel cycle fatigue properties of,TG142.15
  11. Research on Double-wire Saw Technology and Microstructure Behavior of the Welded Joint of 10Ni3CrMoV Steel,TG445
  12. A Study on CGHAZ Microstructure and Properties of High Strength Copper Bearing Steel,TG457.11
  13. Development of Low-carbon Boron Alloyed Steel,TG335
  14. Study on Rolling and Heat Treatment Processing of Low-carbon and Low-alloy Plastic Mould Steel,TG161
  15. Eirich Intensive Mixer Parts Home-made,TQ051
  16. Hot Deformation Behaviors and Heat-treatment Technology of Biomedical Ti-6Al-7Nb Alloy,R318.08
  17. Composition Design and Optimization of Controlled Rolling and Cooling Process for Q460C Steel,TG335
  18. Influence of Additives on Comporsite Phase Al2O3-ZrO2 Ceramic Sintering and Mechanical Properties,TQ174.1
  19. Study of the Microstructure and Properties of Wear-Resisting Lining Boards at Home and Abroad,TG142.1
  20. Study of the Obdurability of 20CrMnTi Cutting Picks Treated by Lye Quenching after Hard Soldering,TG156.3
  21. Study on Effection of Cerium Content on Mechanical Properties of Steel Contained Tin,TG142.15

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metallic materials > Steel > Microstructure and properties of steel > Analysis of the steel test
© 2012 www.DissertationTopic.Net  Mobile