Low-Frequency Magnetic Pulsing Effect as Well as EET Study of Amorphous Alloy Fe43Co43Hf7B6Cu1

Author: YinLiJuan
Tutor: ZuoYueSheng
School: Northeastern University
Course: Materials Physics and Chemistry
Keywords: Fe(Co)-Hf-B-Cu amorphous alloy low frequency pulse magnetic field microstructure soft magnetic properties EET BLD method
CLC: TG139.8
Type: Master's thesis
Year: 2009
Downloads: 18
Quote: 0
Read: Download Dissertation

Abstract


FeCo-based nanocrystalline soft magnetid materials have perfect magnetics, such as high permeability, high magnetic induction intensity, low coercive force, low dissipation, high Curie temperature and so on. Therefore, the research on the formation and properties of the FeCo-based nanocrystalline soft magnetid materials has attracted widespread attention in recent years and become a focus in high temperature soft magnetid materials.Firstly, chemical constituents of Fe(Co)-Hf-B-Cu alloys were designed in this paper, and then Fe43Co43Hf7B6Cu1 alloy ribbons were prepared by melt spinning of single roll casting method. The obtained thin tape in 30～40μm, width in about 3 mm. The composite characterization of prepared sample by XRD, Mossbauer spectrum and DSC. The results indicate that alloy ribbons are amorphous state, Tg=379.80℃, TX=472.99℃,Tp1=509.95℃, Tp2=620.72℃,Tp3=712.03℃etc.The amorphous thin ribbons were treated by low-frequency magnetic pulsing:pulse magnetic field from 148Oe to 379Oe, pulse frequency from 10-40Hz and processing time from 60-240s. Experimental results showed that the maximum temperature risingΔt in the LFPMF treatment process is no more than 10℃, and the internal and external temperature rising did not show significant difference. There did not exist high temperature or transient high temperature and temperature uniformity was good. The microstructures of treated samples were examined by XRD and Mossbauer spectra:The low frequency magnetic pulse can lead to the initial crystallization of Fe43Co43Hf7B6Cu1 amorphous alloys, The crystallized quantity varied from 2.249～10.969%. With the increasing of the pulse magnetic field or the processing time the amount of the crystallization present increasing trentency, There is not linear relationship between the crystallized quantity and pulse frequency, but is increasing at beginning then reducing. Preliminary research on the soft magnetic property of the treated and untreated alloys by LFPMF indicate thatσs and Hc of the treated alloys were pushed compared with as-quenched, Mr of the treated alloys were reduced, The soft magnetid properties of samples treated by LFPMF were improved. The soft magnetic property is optimum when crystallized quantity is 5.057%, corresponding H=222Oe, f=40Hz, t=240s.The covalence electronic structures of amorphous and crystalline phases before and after LFPMF treatment were calculated using the bond length difference (BLD) method in the empirical electron theory (EET). According to the atoms proportions and the contribution of each cell iron and cobalt atoms to the magnetic moment of the Fe43Co43Hf7B6Cu1 alloy. The magnetic moment per unit mass of amorphous phase was calculated as 159.7978emu/g, and that of crystallized phase was 184.2174emu/g. Then the magnetic moment of the double-phase alloys after the crystallization by LFPMF treatment was calculated, and compared with experimental values. The error of these two is less than 10%.

Related Dissertations

  1. Reactive Hot-Pressing and Mechanical Properties of （ZrB2-ZrO2）/BN Composites,TB332
  2. Microstructure and Mechanical Properties of Mg-Zn-Y-Zr Alloys,TG146.22
  3. Investigation on Microstructure and Properties of Cadmium-Free Silver-Based Intermediate Temperature Filler Metals,TG425.2
  4. Research on Technology and Mechanism of Joining Cemented Carbide to Carbon Steel,TG454
  5. The Investigations on the Characteristics and Mechanism of NIR Emission from Bi-doped Silicophosphate Glasses,TQ171.1
  6. Preliminary Study on Salt-Tolerant Mechanism of the New Pennisetum Purpereum Schumach Variety-Sumu No.2,S543.9
  7. Study on the Fine Structure of Intestine and Intestinal Mucosal Barrier in Zebrfish (Brachydanio Rerio),Q95-33
  8. Studies on the Aggregation and Microstructure of Imidazolium Ionic Liquids in Solutions,O645.1
  9. Study on Stock Price Behavior Around Periodical Reports Based on Asymmetric Information,F832.51
  10. Rolled Mg-Zn-Ce-Zr (Mn) alloy microstructure and mechanical properties of,TG339
  11. Research on prefertial Tax Policy of the Occupational Pension in China,F842.6;F812.42
  12. Mn doping Preparation of Ga_2O_3 films , structure and optical properties of,O484.1
  13. Pressure Extrusion Formation and Soft Magnetic Properties Study of Composite Magnetic Powder Cores,TF124.39
  14. Study on High Silicon Coating by Dc-Plasma Jet Surface Metallurgy,TG174.4
  15. Research on Microstructure Evolution in Pre-heat Treatment and Cold Ring Rolling,TG142.15
  16. Containing the scandium aluminum-magnesium alloy cold-rolled deformation and annealing organization of and texture,TG146.22
  17. Tribological Properties and Corrosion Resistance to Molten Steel of （ZrB2-ZrO2）/BN Composites,TB332
  18. Study on Characteristics of Morphology Anatomy and Physio-Biochemistry of Two Ecotype Varieties Cucumber Leggy Seedilings,S642.2
  19. Study on Surface Structure of High-Modulus Carbon Fiber and Interfacial Properties of HM-CF/TDE-85,TB332
  20. Simulation for Electromagenetic Shielding Effectiveness and Electromagnetic Scatterign Perfrmance of Microsturcture Materials,TB303
  21. The in situ synthesis of composite particles enhanced laser cladding of nickel-based layer,TG174.44

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > The alloy learn with a variety of properties of alloys > Other special nature of the alloy > Amorphous alloy
© 2012 www.DissertationTopic.Net  Mobile