A Study on Stable Protection Technology and Application of Typical Combustible Agent

Author: TianQingSong
Tutor: LiYan; GeRuiRong
School: Nanjing University of Technology and Engineering
Course: Chemical Engineering and Technology
Keywords: boron Silane coupling agent KH570 lithium fluoride coating ignitionsensitivity burning rate
CLC: TQ560.4
Type: Master's thesis
Year: 2013
Downloads: 22
Quote: 0
Read: Download Dissertation

Abstract


In this paper, silane coupling agent KH570and lithium fluoride as coating agent were used to coat surface of boron power, Silane coupling agent coating use the method of direct coating, lithium fluoride use the method of deposition, then characterized them with SEM, FT-IR, TG, particle size analysis and XPS.(1) The influence of pH, reaction time and reaction temperature of silane coupling agent KH570coating boron powder were investigated. The results showed that optimum coating conditions were:the boron powder mass4.0g, KH570the mass fraction of5%, a pH value of4, the reaction time was1.5h, and the reaction temperature was45℃.(2) The influence of coating amount, a coupling agent pretreatment, the stirring speed and the concentration of the bottom liquid of Lithium fluoride coated boron powder were investigated. The results showed that the optimum coating conditions were:the boron powder mass4.0g, the coating amount was3%, a coupling agent pretreatment, the stirring speed was about700r/min; the concentration of the bottom liquid is5%.The change of ignition sensitivity of B/KNO3ignition composition (ratio for50/50) and the burning rate of B/BaCrO4(ratio for10/90) delay composition with coated and uncoated boron powder was compared. The results showed that the sensitivity of ignition composition with boron powder through the surface coating was reduced, the sensitivity of boron powder coated by coupling agent was reduced more significant than LiF coated. In the aging test, the stability of the ignition composition and delay composition increased after boron powder coated and deterioration speed reduce. The results showed that the long storage stability of pyrotechnics compositios used boron coated by coupling agent improved more significant than that by LiF.

Related Dissertations

  1. Preparation of Micro-Arc Oxidation Ceramic Coating on Mg Alloy and the Research of Galvanic Corrosion,TG174.453
  2. The Effect of Current Density and Electric Field on Ni and Its Alloy Electrodeposition for Copper Crystallizer,TQ153.2
  3. A Study on the Electrodeposition of Zn-Co and Zn-Ni Alloys in the Reline Room Temperature Ionic Liquid,TQ153.1
  4. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  5. Preparation and Performance of V2O5-WO3/MOx/Cordierite Catalyst Modified with Cu、Mn、Ce for DeNOx,X701
  6. LSGM electrolyte thin films and electrochemical properties of,TM911.4
  7. Anti-corrosion Property of Flake Zinc Epoxy Coating Doped with Rare Earth in SRB,TQ630.1
  8. Research on PSA/Cotton Blend Fabric of Coatinging of Water Resistance and Moisture Permeability,TS195.6
  9. Study on Chitosan-Based Composiate Nano-Coating Dope and Its Effect of Fresh-Keeping for Coated Egg,TS253.2
  10. Development and Application of Biological Seed Coating Formulation for Soybean,S565.1
  11. The Etiology of Cracked Stem Disease and Its Control Technologies in Broccoli (Brassica Oleracea L) Production,S436.35
  12. RF Microwave Multilayer ceramic capacitors Development,TM53
  13. Research on the Effect of Microwave Modification on Pulverized Coal Combustion Properties,TF538.63
  14. Creation and Application of Trichodema Bio-Seed Coating Agent,S435.131
  15. Research on High-temperature Oxidation Property of Calorized Coatings on GH907 Superalloys,TG174.44
  16. Preparation of polyaniline nanostructures , characterization and biomedical applications,TB383.1
  17. Preparation of BCN Fibers by Boronation of PAN Fibers,TQ342.6
  18. The Study of Preparation Electrochemical Properties and Surface Modification of Boron-doped Diamond Thin Film,TB383.2
  19. Non-oriented silicon organic - inorganic composite coating on very thick insulation,TG174.4
  20. Nano zirconia thermal barrier coatings prepared by plasma spraying and Properties,TG174.442
  21. Silica / poly (vinylidene fluoride) Hydrophobic Coating and drag reduction performance,TB383.1

CLC: > Industrial Technology > Chemical Industry > Explosives industry, match industry > General issues. > Raw materials and auxiliary materials
© 2012 www.DissertationTopic.Net  Mobile