Detection and Evaluation of the Plastic Deformation of Weld Joint by Nonlinear Ultrasonic Technique

Author: LiQun
Tutor: XuanFuZhen
School: East China University of Science and Technology
Course: Mechanical Design and Theory
Keywords: Welded joint Nonlinear ultrasonic technique Life prediction Plasticdeformation Nondestructive evaluation (NDE)
CLC: TG441.7
Type: Master's thesis
Year: 2012
Downloads: 95
Quote: 0
Read: Download Dissertation

Abstract


Welded joints are widely applied in petrochemical industry and nuclear power, etc. How to keep welded components operating safety is a challenging task. It’s important to establish effective methods for evaluation of the healthy state of materials and prediction of their remaining life. The nonlinear ultrasonic technique has been found recently to evaluate to the performance degradation of materials or components in the early working-time.Continuing and interrupted tensile tests were conducted for A17009.The measurement results show little differences, but with a similar trend. The nonlinear parameter increases with increasing the plastic strain.The welded joint of30Cr2Ni4MoV steel was studied in terms of nonlinear ultrasonic, velocity and attenuation measurements. These results show:(a) The nonlinear parameter is increase with increasing the plastic strain. Among the measurement locations, the nonlinear parameter displays a maximum change at the middle position of the welding line.(b)There is no obvious repeated relationship between the ultrasonic velocity and the plastic strain.(c)There is no obvious repeated relationship between the attenuation and the plastic strain,(d) Comparing with conventional ultrasonic methods, the nonlinear ultrasonic method is more suitable for evaluating the performance degradation of30Cr2Ni4MoV welded joint.Moreover, the microstructures of the welding line were analyzed based on metallographic studies for interpreting the relationship between the nonlinear parameter and the plastic deformation.

Related Dissertations

  1. Studies on Changes of Quality Characters and Prediction Model of Postharvest Tomato Fruit,S641.2
  2. Research on the Accelerated Fatigue Test Method for Rubber Isolator,TB535.1
  3. Durability Study of Concrete Structures Based on Chloride Ingress,TU528
  4. Study on Uniaxial Tensile Performances and Durability Damage of HPC Under Cyclic Load,TU528
  5. Chinese Environmental Zonation Based on Durability of Concrete Structure,TU375
  6. Time-Dependent Reliability Assessment of Concrete Continuous Beam Bridge Based on Real-Time Monitoring Information,U448.34
  7. The Mechanism of Fatigue Damage and Fatigue Life Prediction of High-speed EMU Welded Bogie Frame,U260.331
  8. The Application and Research of NDT in the Welding Quality Testing of Steel Structure,TG441.7
  9. The Study of 6082 Al-Mg-Si Alloy Joints’ Mechanical Properties and Microstructure by Ar Arc Welding,TG407
  10. Life Prediction of Cylinder Head under the Creep-Thermal Fatigue Interaction,TK403
  11. Simulation and Analysis on Aluminum Alloy Bodywork of Metro,U270
  12. Strength Analysis and Fatigue Life Estimation of Weld Line on the Parts of Freight Car Wheels with Heavy Axle Load,U272.6
  13. Study on Fatigue Life Prediction of Rubber Elastic Absorber,TB535.1
  14. Research of Fretting Fatigue on Railway Wheel-Axle Assembly,U270.33
  15. Inhomogeneity and Application in Corrosion Resistance of Microarc Oxidation Coatings on Al Alloy Welded Joints and Structure,TG174.451
  16. The Research of Corrosion Friction and Wear Properties and Life Rediction of KFRP under Salt Water,TB332
  17. Study on the Waterproofing and Anti-Erosion Effect of Chloride Ion for Integral Water Repellent Concrete,TU528.1
  18. A tracked vehicle steering failure analysis and reliability of the planetary life prediction,U472
  19. Research on the State of Health Compregensive Evaluation and the Life Prediction of a Certain Servo Actuator,V249.1
  20. Corrosion Resistance of GF/VE Composites in Distilled Water and Sulfuric Acid Solution,TB332
  21. Rolling Contact Fatigue Life Prediction Based on the Surface Integrity Induced by Grinding Process,TG580.6

CLC: > Industrial Technology > Metallurgy and Metal Craft > Welding, metal cutting and metal bonding > Welding process > General approach > Welding defects and quality inspection
© 2012 www.DissertationTopic.Net  Mobile