Influence of Sintering Temperature on Zirconia/Veneer Interfacial Adhesion
Author: GongQingZuo
Tutor: SuXiaoZuo
School: Guangxi Medical University
Course: Prosthodontics
Keywords: zirconia/veneer sintering temperature Shear bond strength thethermal shock resistance
CLC: R783.1
Type: Master's thesis
Year: 2012
Downloads: 81
Quote: 0
Read: Download Dissertation
Abstract
|
Objective:To investigate the Influence of sintering temperature on zirconia/veneer Shear bond strength and the thermal shock resistance; and to observe the interface characterization of zirconia/veneer.Methods:Use Cercon zirconia ceramics to manufacture the core cermic substructures, and use Cercon ceram kiss to firing the veneering surface layer according to 7 different sintering temperatures:(1) 800℃group (2) 810℃group (3) 820℃group (4) 830℃group (5) 840℃group (6) 850℃group (7) 860℃group.70 samples were divided into 7 groups to shear bond tests, another 70 samples were divided into 7 groups to the thermal shock resistance tests,14 samples were divided into 7 groups for SEM observation and X-ray element energy analysis.Result:There were significant differences for shear bond strength between seven groups (P<0.05). Compared with the standard group 830℃group, the highest sintering temperature 860℃group and minimum sintering temperature 800℃group both have significant differences (P<0.05). Compared with the standard group 830℃group,810℃,820℃,840℃,850℃groups all have no differences (P>0.05).There were significant differences for the temperature of the thermal shock resistance between seven groups (P<0.05). Compared with the standard group 830℃group, except the 820℃group and 840℃group both have no differences (P>0.05),800℃,810℃,850℃,860℃groups all have significant differences (P<0.05).SEM showed the zirconia/veneer contacted tightly at the interface, while EDS detected the element of O/Na/Al/Si/Zr/K of the zirconia/veneer interface diffused into each other, sintering temperature can influence this penetration trend.Conclusion:The sintering temperature influences the shear bond strength and the thermal shock resistance of zirconia/veneer, too high or low sintering temperature decreases the shear bond strength and the temperature of the thermal shock resistance of zirconia/veneer. The element of the zirconia/veneer interface can diffused into each other, sintering temperature can influence this penetration trend.
|
Related Dissertations
- Research on the Bond Strength of the Tooth-colored Restorations on the Enamel and Dentinal of Primary Teeth,R783
- Microstructure and Properties of 9Cr-ODS RAFM Prepared by PM,TG142.1
- Study on Fabrication and Oxidation Behavior of 12Cr-ODS Fe-based Superalloys,TG132.32
- Study on the Stoichiometric Ratio of Material and Reducing- Reoxidation Technology of Laminated PTCR,TN605
- Boron carbide sintered diamond saw blades in the Applied Research,O474
- Simulation Model of Sinter Bed Temperature Field and Experts System of Sinter Quality Optimization,TF046.4
- Study on SBS Modified Asphalt Technical Performance Evaluation and Quality Control,U414
- Study on Preparation of high-performance -doped lanthanum lead zirconate titanate piezoelectric ceramics,TQ174.6
- Effects of Sintering Temperature and Calefactive Velocity on Properties of Diatomite-based Dental Machinable Ceramic,R783.1
- The Research of Biological Ceramics Producing with Cotton Stalks,TQ174.1
- Study on Ceramic Material of MgTiO3-CaTiO3 System in High Frequency,TQ174.1
- Research on Characteristics of Sintered Body Mixed with Sewage Sludge,TU528.0
- Effect of Different Silanization on the Shear Bond Strength of Fiber Posts in Vitro,R783
- The Effect of Sintering Process on Properties of Cu-Based P/M Friction Materials,TF125.9
- Studies of High-performance M-Type Strontium Ferrites by Wet Compacting,TM277
- Effect of Different Means for Tooth Surface Polishing on Rebond Shear Bond Strength of Orthodontic Brackets,R783.5
- Application of Silicone Rubber on Maxillofacial Defects and a in Vitro Study on Shear Bond Strength of Silicone Soft Liners to a Denture Base Resin,R782
- Effects of Various Conditioning Methods on the Bond Strength of Rebonded Ceramic Brackets with Different Base Designs,R783.5
- Effect of Er:yag Laser Irradiation on Conventional Dentin Bonding,R781.2
- Effects of Light-curing Units on Microleakage and Shear Bond Strength of Light-curing Orthodontic Adhesives,R783.5
- The LTCC the magnetic dielectric composite ceramic preparation and electromagnetic properties of,O482.5
CLC: > Medicine, health > Oral Sciences > Oral orthotics > Dental Materials Science
© 2012 www.DissertationTopic.Net Mobile
|