Isostatic graphite roasting and impregnation process research
Author: YangMeng
Tutor: XieGang
School: Kunming University of Science and Technology
Course: Metallurgical Engineering
Keywords: Isostatic pressing formed graphite Roasting Dipping
CLC: TQ127.11
Type: Master's thesis
Year: 2013
Downloads: 71
Quote: 0
Read: Download Dissertation
Abstract
|
Isostatic pressing formed graphite, also called Sangao graphite or special graphite, is a kind of graphite with high strength, high density and high purity, which is widely used in fields such as metallurgy, chemical industry, aircraft industry, electronic industry and nuke industry. Especially, large size isostatic pressing formed graphite with superior quality can be used in high-tech and new technique field and is honoured as the most promising material in the21th century because of its widespread application prospect.The paper prepared raw material for the last process of making isostatic pressing formed graphite, which was graphitization, by multi roast and dipping of isostatic pressing perform body and coal pitch. Through measuring methods including TG-DSC analysis, SEM analysis and XRD analysis, properties and both apparent structure and micro structure of products made in every stage were analyzed and compared to each other. In addition, the mechanisms of affecting properties of products were also discussed.It was proved by experiments that the coking value of preformed body could be efficiently raised by roasting under inert gas atmosphere. Moreover, changes of preformed body under different temperatures were revealed by analyzing TG-DSC curve. When the temperature was under200℃, the body only slightly swelled because of softening of it and thermal decomposition in it, while no significant change of its physical and chemical properties happened. When the temperature was between200℃to600℃, volume of the body shrinked most obviously because of the drasticly reacting complex reactions, which suggested the heating rate should be decreased. When the temperature was between800℃to1200℃, the body was gradually getting stable because coking of the body had completed essentially, which suggested remaining the highest temperature for some time and then cooling down under control to the room temperature. Finally, based on above analysis and conclusion, theoretical heating curve of single-pass roasting of isostatic press preformed body was fixed.Through single factor experiments one to ten, which were designed to study influences on properties of roasted products of cover, heating rate and roasting time, optimum conditions of single-pass roasting of isostatic press preformed body were obtained.Optimum values of three technological parameters of impregnation technology were obtained through orthogonal experiments. The dipping temperature should be200℃and the pressure should be1.5MPa keeping60minutes. In addition, it was also concluded that influences on dipping of temperature, pressure and pressure maintaining time successively diminished. Through analyzing TG-DSC curve of heating coal pitch, it was revealed that thermal properties of coal pitch were similar to that of isostatic pressing preformed body. After analyzing TG-DSC curve of coal pitch, the roasting heating curve of preformed body after dipping was fixed for the purpose of reducing cost and improving work efficiency.Properties of products such as density, mechanical strength and so on were improved as number of times of dipping and roasting increased, while the improving range decreased. On the basic of experiments, it was concluded that the best times for roasting and dipping were respectively4times and3times.
|
Related Dissertations
- Copper slag roasting modified experimental study,X758
- Research of the No.1 Blast Furnace Multi-objective Optimal Model and the Energy Analysis of Ore Beneficiation Process in JISCO,TD951
- Researches of the Excellent Methanical and Antiallergic Properties of Natural Rubber Latex and Commercially Production,TQ331.2
- Roasting Preprocessing of High Arsenic High Sulfur Gold Concentrate and Thiourea-Leaching Processes Research,TD953
- The Study on Pretreatment Refractory Gold Concentrate by Microwave Roasting,TD953
- Efficient use of high- arsenic sulfide gold ore resources Experimental Research,TD98
- Microwave roasting of high titanium slag preparing synthetic rutile new technology research,TQ164
- Guizhou the dustpan Tian Carlin-type primary gold beneficiation test,TD953
- Research on Preparation Technology of Polarity Polypropylene,TQ325.14
- Research on Supercritical CO2 Assisted Grafting Modification of Polypropylene,TQ325.14
- Research of Intensified Oxidative Roasting Process of Chromite Ore,TQ136.11
- Photocatalytic Hydrogen Evolution from NaCl Saltwater in the Presence of Electron Donors,TQ116.2
- Process of Refractory ore roasting microwave magnetic synchronous drop phosphorus,TD951
- Extraction and Micronization of Ginkgo Flavonoids from Ginkgo Biloba Leaves Using Supercritical Carbon Dioxide,TQ461
- Dynamic Synthesis of Zeolite UZM-5 and Templates Removal,TQ424.25
- A Thermodynamic Analysis of Hydrogen Production by Ethanol Reforming and the Preparation of Relative Catalysts,TQ116.2
- Study of Catalyst for Selective Reduction of NO at Low-temperature with NH3,TQ203.2
- Zinc Dipping Solution Containing Double Complexing Agents and Electroplating Coating for Mg-Li Alloy,TQ153
- From nickel-molybdenum ore smelting slag recycling of Nickel Compounds,TF803
- Study on Catalytic Cyanide Leaching of Gold from Gold Concentrate Containing High-Arsenic, Sulphur in Xinjiang and Comprehensive Utilization of the Slag,TF831
- Study on Abrasion Resistance Enhancement of Melamino-formaldehyde Impregnation Resin,TQ320.7
CLC: > Industrial Technology > Chemical Industry > Non-metallic elements and their inorganic compounds, the chemical industry > Part Ⅳ family of non-metallic element and its inorganic compounds > Carbon and its inorganic compounds > Carbon
© 2012 www.DissertationTopic.Net Mobile
|