Experimental Study of Concrete Tensile Fatigue Residual Strength in the Corrosion Condition
Author: ZhangYuXian
Tutor: ZhouJingHai
School: Shenyang University of construction
Course: Structural Engineering
Keywords: Concrete tensile strength Concrete corrosion fatigue Residual strength
CLC: TU528.0
Type: Master's thesis
Year: 2013
Downloads: 13
Quote: 0
Read: Download Dissertation
Abstract
|
In practical projects, a large number of concrete structure not only bear cycle fatigue loads, but also influenced by the various environmental corrosion factors, such as the bridge structure nearby salt lake area, highway and railway in area influenced by acid rain or snow removal agent in winter, marine oil production platform and port impacted and erosioned by seawater and so on. Fatigue failure problem of concrete structure in the corrosion conditions gradually aroused wide attention of all social sectors. The corrosion fatigue of concrete structure is mainly due to the initial defects after material erode and internal injury in the process of fatigue which lead to the decline of strength,so understanding the change rule of concrete tensile fatigue residual strength has practical significance. This paper mainly research mechanical property of concrete variable cross-section specimen corroded by sodium sulfate solution and sodium chloride solution, the specimen is made considering the principle of not eccentric by tension load and easy installation.This paper made27prismoid concrete variable cross-section specimen, among which9aren’t corroded,9is put in the sodium sulfate solution whose concentration is1.5g/L and9is put in the sodium chloride solution whose concentration is3g/L. According to the differentce of the corrosion solution and the fatigue number, study the residual strength of the prismoid concrete variable cross-section specimen. In conclusion, the research work of this paper mainly include the following aspects:(1) make reasonable selection of the corrosion solution, corrode the prismoid concrete variable cross-section specimen, determine the corrosion time scientificlly and reasonably, observe the change of corroded specimens in the process of the corrosion, analysis damage form of concrete after corroded, find out the influence factors of the concrete corrosion damage under the action of different corrosion medium.(2) Do the tension fatigue residual strength test on the concreted prismoid concrete variable cross-section specimen, compare with the concrete specimen which are not corroded,research shows that it can clearly reveal the degradation of the concrete fatigue residual strength according to the method of corroding the specimen firstly and then after a certain number of fatigue load. Plotted P-R-N curve according to the experimental data, this curve can explain the characteristic of "Sudden death" of the concrete fatigue residual strength under corrosion condition.(3) The tensile secant modulus of concrete material after corrosion will reduce with the increase of the fatigue cycle index, compared with the specimen which is not corroded, it is still accord with the semi logarithmic relationship between the fatigue number and residual secant model, it exist linear relationship between square root of the concrete residual strength and residual secant modulus.(4) Through the experimental study, establish attenuation model of concrete tensile fatigue residual strength under the condition of not corroded and corroded. Defines the damage expression D based on boundary concept and damage mechanics theory, the test proved that the corrosion of sodium chloride solution influence more serious to concrete fatigue performance, plotted damage curve of concrete fatigue test after corroding by different solution, reveals the development law of concrete corrosion fatigue damage.
|
Related Dissertations
- Corrosion on the impact strength of magnesium alloy AZ91,TG146.22
- Residual Strength Study of Corroded Pipeline,TE988.2
- The test wells barrel situation analysis and safety evaluation of the test oil technology research,TE353
- Reliability Assessment of Corroded Pipeline,U178
- The Analysis of the Corrosion’s Effects to the Submersible Pressure Cylindrical Shell’s Residual Strength,U661.5
- Study of Evaluation Method on Residual Strength of Warship Subjected to Explosion Loads,O383
- Highway Tunnel Fire damage concrete specimens lining Study,U454
- Mechanicalproperties of Foam Sandwich Composites with Low-Velocity Impact Damage,V214.8
- Analysis of Instability Failure of Landfill Along Geosynthetic Interface and Tension of Geomembranes Placed on Landfill Slope,TU43
- Study on the Failure Mechanism and Reliability Evaluation of Buried Pipelines,TU990.3
- Load Carrying Capacity Calculation of Brittle-Plastic Structures and Its Application in Engineering Practice,O342
- Weight Function Method for Aircraft Structure Ultiple Site Damage Analyses and Residual Strength Rediction,V215
- Residual Strength Analysis of Metal Thin-Walled Structures Reinforced by Bonded Straps,V214.4
- Residual Strength Analysis of the Damaged Cylindrical Shell,U661.43
- Application Study on Casing Strength Design of Deep Horizontal Well,TE355.6
- Study on Fully Softened Shear Strength of Loess,P642.22
- Experiment Study and Theoretical Analysis of SRC Columns under Fire Including Whole Process of Heating and Cooling,TU398.9
- Based on magnetic flux leakage testing data within long-distance oil and gas pipeline technology research evaluation,TE973.6
- Residual Strength Analysis of Structures with Multiple Site Damage Based on Crack Tip Opening Angel Criterion,O346.1
- Study on Elastic Modulus Method for the Residual Strength Measurement for Fatigue Damaged Materials,O346.5
- Study for New Structure Design of Warship Resisting Damage and Residual Strength,U674.7
CLC: > Industrial Technology > Building Science > Building Materials > Non-metallic materials > Concrete and concrete products > General issues
© 2012 www.DissertationTopic.Net Mobile
|