Study on Structure and Properties of Hot-wet Epoxy Resin Modified Systems

Author: ZhangXiaoZuo
Tutor: FengNa
School: Dalian University of Technology
Course: Materials Science
Keywords: Epoxy resin Silicone Modified systems Hot-wet property Opticalproperties
CLC: TQ323.5
Type: Master's thesis
Year: 2011
Downloads: 16
Quote: 0
Read: Download Dissertation

Abstract


In order to prepare and study on new hot-wet epoxy resin （EP） modification system,tracking and reference the latest research methods and results on hot-wet EP. EP modificationsystems were prepared by graft polymerization and sol-gel in-situ composition. The hot-wetresistance, optical properties, mechanical properties and micro-morphology were analyzed bythermogravimetric （TGA）, index analysis, ultraviolet analysis, infrared spectroscopy （FT-IR）and scanning electron microscope （SEM）. The EP-HTPDMS copolymers were applied toLED’s package, and its further optical properties were studied by luminous decay.EP-CAB copolymers were synthesized and prepared, and the effects of CABconcentration on the hot-wet resistance, optical properties, mechanical properties andmicro-morphology were analyzed. The results indicated that when CAB concentrationreached10%, the contact angle and water absorption of the copolymer were85.1°and0.213%, and the weight maintenance rate of EP-CAB copolymer at650℃was28%.Comparing with EP, the hot-wet resistance of EP-CAB copolymer was obviously improved.The optical properties were also enhanced. The hardness of the copolymer was decreased, andthe introduction of CAB made the copolymer exhibit the features of tough fracture.EP-HTPDMS copolymers were prepared, and the effects of HTPDMS concentration onthe properties were analyzed. The results showed when HTPDMS concentration was6%, thecontact angle and water absorption of the copolymer were80.7°and0.233%, and the weightmaintenance rate of EP-HTPDMS copolymer at650℃was11%. Comparing with EP, thehot-wet resistance of EP-HTPDMS copolymer was obviously improved. The index andtransmittance of the copolymer were1.5305and94.31%, and the optical properties wereenhanced. The introduction of HTPDMS made the copolymer exhibit the features of toughfracture.EP/SiO2composites were prepared by sol-gel in-situ composition, the effects of SiO2concentration on the properties were analyzed. The results indicated that when SiO2concentration reached7.5%, the contact angle and water absorption of the copolymer were 83.6°and0.485%. When the thermogravimetric was5%, the temperature was273℃.Comparing with EP, the hot-wet resistance of EP/SiO2composite was improved. The opticalproperties were enhancd to some extent.Comparing with the hot-wet resistance, optical properties and mechanical properties ofthe three systems, EP-HTPDMS copolymers were applied to LED’s package. The resultsshowed that when HTPDMS concentration was less than9%, the relative light output ofEP-g-HTPDMS copolymers were higher than that of unmodified EP and luminous decayreduces significantly.

Related Dissertations

  1. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  2. Prototype Development of Intimate Apparel Mannequin,TS941.2
  3. Study on Carboxyl Side Groups Containing Poly Aromatic Ether Sulfone Ketone and Modification of Epoxy,O631.3
  4. Study on Organic Silicone Modified Epoxy Resins Performance and Preparation of Adhesive,TQ323.5
  5. The Relationship Rearch between Bax and Pathogenetic of Complicated Cataract Associated with Silicone Oil,R776.1
  6. Risk Factors for the Development of Transient Hypotony after Sinlicone Oil Removal in Aphakia Eyes,R779.6
  7. The Analysis of the Growth Factor Related with the Secondary Glaucoma in the Anterior Champer of Silicone Oil-filled Eyes,R779.6
  8. Diabetic retinopathy OK vitrectomy surgery intraocular lens implantation in different periods of clinical observation,R779.66
  9. Silicone modified acrylic emulsion research,TQ633
  10. The Study of Synthesis and Application of the Low-yellowing and Hydrophilic Silicone Softener,TS195.23
  11. Preparation and Surface Modification of Silica Nanoparticle,TB383.1
  12. Study on Film Morphology, Surface Properties and Film Formation Mechanism of Amino Silicone Oils,TS195.23
  13. Modification of Thermosetting Resins by High Performance Liquid Crystalline Epoxy Resin,TQ323.5
  14. Novel Silicone Resin for C-class Vacuum Pressure Impregnation,TQ324.21
  15. Preparation of Oil-soluble Defoamers and Their Research and Application on the Seed Precipitation from the Sodium Aluminate Liquor,TQ423.95
  16. Research on High-performance Silicone Resins for LED Packaging,TQ324.21
  17. Effect of Viscosity of Silicone Oil on Surface Aggregation in C4F8 Plasma,O472.1
  18. Hydrophilic silicone softener Development and Application,TS195.23
  19. Modifed Research of UV Coatings,TQ637
  20. Preparation and Study on Monocomponent Heat-resistant Epoxy/Guanidinium Structural Adhesives,TQ433.437
  21. Study on Modification of Waterborne Polyurethane,TQ323.8

CLC: > Industrial Technology > Chemical Industry > Synthetic resins and plastics industry > Polycondensation resin and plastic > Epoxy resins and plastics
© 2012 www.DissertationTopic.Net  Mobile