Preparation and Investigation of High Absorption Property Cross-linking Non-crystalline Porous Starch

Author: WuShan
Tutor: XiaoJianMou
School: Nanchang University
Course: Chemical Engineering
Keywords: non-crystalline starch cross-linking starch reaction activity absorption
CLC: TQ914.1
Type: Master's thesis
Year: 2013
Downloads: 23
Quote: 0
Read: Download Dissertation

Abstract


Starch and modified starch have increasingly being used in the food, pharmaceutical, paper making, textile, chemical industry, environmental protection industry. Limited to the polycrystal system of starch, the modified efficiency is low. The non-crystalline process destroy the crystal area in raw starch. The internal original ordered arrangement in starch is disturbed. The modified chemical reagent can react with starch much more easily. The industrialization of non-crystalline starch has a wide development prospect.The non-crystalline modified porous corn starch with high adsorption performance was prepared through non-crystallization, esterification and enzymolysis process. The kinetics of raw starch and non-crystalline starch was studied through wet-crosslinking process. The effection of non-crystalline process on subsequent reation rate was investigated.The results showed that when reaction temperature was50℃, crosslinking agent dosage was5%, reaction time was2h, the settlement area of product was0.45mL, and the crosslinking degree was greatly improved. The conditions of dry esterification were as follows:the starch concentration was30%, esterification agent dosage was10%, urea dosage was5%, esterification temperature was150℃, reaction pH was5.0, reaction time was2h. Compared with raw corn starch, the degree of substitution of non-crystalline corn starch was greatly improved. After the non-crystallization and esterification process, the solubility of starch declined slightly, the specific volume increased, the particle was not broken, and the paticle size increased. The crystal area was destroyed with a certain degree decline of crystallinity.The non-crystalline modified porous corn starch was prepared through enzymolysis based on non-crystalline esterified corn starch. The results of single element and orthogonal experiments showed the best hydrolysis conditions were:15%starch concentration,2.0%enzyme dosage, reaction temperature45℃, pH4.4, reaction time12h.Under these conditions, the water adsorption was178%and the oil adsorption was134%. The water and oil adsorption of the product were more than twice as much as the raw com starch was. Compared with ordinary corn porous starch, the water absorption was increased by31%and the oil absorption increased by28%. Compared with raw com starch, the solubility, specific volume, bet surface area and paticle size of the product increased. There were many pores in different sizes on the paticle surface and extended to the interior paticle. The crystallinity degree almost unchanged after enzymolysis process.The wet process kinetics of cross-linking reaction were studied based on raw com starch, non-crystalline com starch, raw cassava starch and non-crystalline cassava starch. The contrast results of kinetics data showed that non-crystalline process can effectively improve the reaction activity.

Related Dissertations

  1. Methane Concentration Detecting Instrument Based on Infrared Absorption Theory,TP216
  2. Studies on the Preparation and Purification of Fumeol from Different Materials and Liquid Smoked Technology of Sausage,TS251.65
  3. Characterization and mechanism of the titanium dioxide surface envelope,TQ621.12
  4. Technology Study on Bricks of City Waterworks Sludge,X703
  5. Research on the Interface Modification of Epoxy Resin/Metallic Substrates and Epoxy Resin/Pigment,TQ630.1
  6. Optical Properties of Chlorphyll-a in Reservoir Water and Its Concentration Inversion Models by Remote Sensing,S127
  7. Acrylic acid - acrylamide superabsorbent properties of high-powered,TQ324.8
  8. Tetra-tert- butyl- perylene polyhedral micro-nano crystal with XANES and XEOL research,TB383.1
  9. Spectral and Molecular Modeling Method Studies on the Interaction of Small Organic Molecules and Proteins,R96
  10. Size-dependent Photochromic and Holographic Storage Properties of Ag/TiO2 Nanocomposite Film,TB383.2
  11. Synthesis and Study of Organic Compounds Based on NIR Spectral Response,O621.25
  12. Reflective Optical Fiber Temperature Sensor Based on Temperature-Dependent Optical Properties of ZnO Film on the Sapphire Prism Surface,TP212.11
  13. Study on Properties of the Modified Polyester Fibers and Knitted Fabrics,TS182.5
  14. Copper alginate fiber structure properties and antibacterial mechanism study,TS102.5
  15. Metal-Organic Frameworks of Tetrazolyl Derivative Ligands: Syntheses, Structures, and Properties,O621.13
  16. Regenerated cellulose fluorocarbon film on the substrate morphology, structure and properties of,TB383.2
  17. Optimization of Absorption Unit and Distillation Unit for Acetone Recovery,TQ224.223
  18. Synthesis and Properties Study of Bent-core Liquid Crystals and Unsymmetric Bent-core Azobenzen Monomers,O753.2
  19. Research of All-optical Ultra-wideband Signal Generation and Modulation,TN925
  20. Research of Absorbed Fiber-optic CO Gas Sensor Signal Processing,TP212
  21. Porphyrins Compound Synthesis and Terahertz Spectrum Measuring,O433.1

CLC: > Industrial Technology > Chemical Industry > Other chemical industries > Chemical processing industry of agricultural products > Chemical process and equipment > Chemical processing of agricultural products
© 2012 www.DissertationTopic.Net  Mobile