Research on the Different Loading Methods and Application of Photochromic Materials

Author: ZhouYueHua
Tutor: HouXin
School: Tianjin University
Course: Materials Science
Keywords: Photochromic compound Fatigue resistance In-situ polymerization Emulsion polymerization
CLC: TB34
Type: Master's thesis
Year: 2012
Downloads: 1
Quote: 0
Read: Download Dissertation

Abstract


Organic photochromic compounds with sensitive color changing property andbright color had extensive application prospect in textile and packaging. But thesecompounds were susceptible to be affected by oxygen, pH value, light, temperatureand other enviromental factors, which led to oxidation, influenced performance andrestrict applications. In this thesis, photochromic compounds and polymer were inte-grated to improve abilities of fatigue resistance and oxidation resistance and prolongservice life. Applications in textile and coating were also studied.In this thesis, photochromic microcapsules were prepared via in-situ polymer-rization, and solution of photochromic compound and DOP, melamine resin were usedas core, wall materials, respectively. It would reach absorbance maximum value whenquality fraction of photochromic compound was2%tested by UV. Influencing factorsto surface morphology and size distribution of photochromic microcapsule, such asmixing speed, emulsifying time, mass ratio of core materials/wall materials andacidification time were discussed in detail. Wall thickness of photochromicmicrocapsules was calculated to be1.4-2.6μm by secondary focusing method. Testdata indicated that photochromic microcapsule with sensitive color changing propertyand average size less than5μm could endure continuous UV for75h, when stirringrate, emulsification time, mass ratio of core materials/wall materials and acidificationtime were1000rpm,5min,1:1and0.5h, respectively.Uncross-linked photochromic PS microsphere with size less than1μm andcross-linked photochromic PS microsphere with size less than2μm were prepared viaemulsion polymerization. Influence of two kinds of initiators KPS and AIBN, reactiontemperature on the performance of photochromic microsphere were discussed indetail. Results showed that uncross-linked and cross-linked photochromic PSmicrosphere synthetized had sensitive color changing property and high fatigueresistance, when initatior, emulsification time, reaction temperature were AIBN,5min,60℃and warming at later period of polymerization.Loading performance of photochromic microcapsule in field of textile andphotochromic composite materials in field of nail polish and phone shell were studied.Result showed that both of them had great photochromism with bright color and highfatigue resistance.

Related Dissertations

  1. Preparation and Characteration of Composite Microspheres with Dual-, Triple- Responsive Properties,O631.3
  2. Studies on the Preparation of 20% Chlorpyrifos CS and Its Analytic Methods,S482.3
  3. Core-shell polymer microspheres synthesis, modification and application,O631.3
  4. Preparation and Research of the PbSe Quautum Dot Doped PMMA Fiber Materials,TB383.1
  5. Synthesis and Application of Biomedical Magnetic Nanoparticles,TB383.1
  6. Synthesis and Properties of Functional Waterborne Polyurethane Coatings,TQ633
  7. Improve SBR conversion rate of,TQ333.1
  8. Preparation and Application of Nonlinear Copolymer as Retanning and Filling Agent,TS529.2
  9. Study on Preparation and Properties of Pure Acrylic Emulsion Modified by Inorganic Nanoparticles,TB383.1
  10. Study on Preparation and Properties of SF/Hollow Glass Beads/Titanium Dioxide Composite Thermal Insulation Coating,TQ630.7
  11. PS/SiO_2 core-shell composite microspheres,TB383.4
  12. Organic acids control the synthesis of polyaniline satisfied / micron-sized structures,TB383.1
  13. Synthesis and Properties of Conducting Polyaniline-based Radar Absorbing Composites,TB34
  14. PMMA / SAN Blends,TQ320.1
  15. The New Proton Exchange Membrane Based on 5-Substituted Tetrazole Functional Group,TM911.4
  16. Preparation of PA6/Nano-Magnesium Hydroxide Composite by in Situ Polymerization,TB33
  17. Emulsion Polymerization of Methyl Methacrylate Initiated by Novel Initiator,TQ316.334
  18. The Preparation and Properties of Nano-SiO2/Polyacrylate Composite Emulsions,TQ630.7
  19. Modification of Pani and Its Application for Supercapacitor,TM53
  20. Preparation of Abamectin Capsule Suspensions and Research of the Physical Storage Stability,S482.2
  21. In Situ Polymerization of Aniline Intercalating α-Zirconium Phosphate and Its Characterization,TB383.1

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Functional Materials
© 2012 www.DissertationTopic.Net  Mobile