Research on Non-magnet Magnetic Liner Strengthen and Its Mechanism

Author: SongYanPing
Tutor: JinYunXue
School: Jiangsu University of Science and Technology
Course: Non-ferrous metallurgy
Keywords: high manganese austenite steel Thermo-calc micro-alloying carbide ageing
CLC: TG142.1
Type: Master's thesis
Year: 2013
Downloads: 1
Quote: 0
Read: Download Dissertation

Abstract


For the hardness of the magnetic liner protective layer material is low, and due to thelife of the magnetic liner is short. The subject is committed to improving the hardness ofhigh-manganese austenitic steel. This issue adjust the content of elements C, Cr, Ti, V traceelements while adding on the basis of the high manganese steel, solution heat treatment,diffusion aging treatment process parameters groping trial out of high strength and hardnessof the non-magnetic steel, as well as to study the mechanism and strengthening mechanismof trace elements. The results showed that:1) The equilibrium phases of the high manganese austenitic steel from200K~1600Kware calculated by using thermo-calc software, and using the result to draw up the progressof heat treatment. And test results show that the results are consistent with the experimentalresults, the Thermo-Calc software is a powerful tool for research on the high manganesesteel.2) The titanium element can refine the organization of high-manganese austenitic steel,thereby increasing the hardness of the material; The phases of super high manganesenon-magnetic steel after solution treatment are austenitic and TiC phase; after ageing at625℃~700℃, the M23C6phase precipitate from austenite, and the phase content increaseswith the temperature increasing until reach saturation at675℃, and the size of the phasehas been grown up at700℃. The titanium content varies between0to0.5%, the hardness ofhigh manganese austenitic steel after solution treatment and aging increase about15%. Thisshows that the role of titanium element in the aging process is not the main factor inincreasing the hardness, the aging treatment is mainly enhanced by precipitation of M23C6phase.3) Within the range of vanadium content from0.25%to0.97%, The phases of superhigh manganese non-magnetic steel after solution treatment are austenitic, and the phasesaging treatment are austenitic, M23C6phase and VC phase. With increasing vanadiumcontent, the inceasement of the high manganese austenitic steel’s hardness after solutiontreatment and aging is greater. V addition substantially enhance the high manganeseaustenitic steel’s hardness after ageing heat treatment, and the maximum hardness reach300HBW when the vanadium content is at0.97%. sizes of100nm~200nm M23C6particlesand sizes of10nm~70nm dispersed precipitated VC particles have been observed in austenitic steel. But the enhancement of hardness mainly depended on dispersed precipitatedVC particles. Finely dispersed precipitated VC particles have coherent orientationrelationship with austenitic. However, with growing up of the VC particles, the orientationrelationship don’t exit when the particles reach a certain degree size. And the content ofdislocation and stacking fault in high manganese austenitic steel increase with the vanadiumcontent increasing.

Related Dissertations

  1. Research on Technology and Mechanism of Joining Cemented Carbide to Carbon Steel,TG454
  2. The Research on Improvement of Rice Noodles Quality,TS213.3
  3. Preparation of Tungsten Carbide Loaded on Carbon Composite and Its Electrochemistry Performance,O614.613
  4. Research on Community Security Measures for Urban Resisdents through Active-Aging Perspective,D669
  5. Study on Hard Surfacing Materials of In-situ Carbide Reinforced High Manganese Steel,TG42
  6. China’s Urban Communities to Explore and Research the Family Pension,D669.6
  7. Research on Low-temperature Pressure Vessel Steel 07MnNiMoVDR Rolled and Quenched and Tempered Technology,TG156.6
  8. Study on Alloying of 2Cr13 Martensitic Stainless Steel for Oil Country Tube Goods Use,TG142.71
  9. The Fuzzy Temperature Control System of Sintering Furnace Based on OPC Technology,TP273
  10. An Analysis on the Method of Taking Care of Elderly during the Ageing Times,D669.6
  11. The Construction of Long Term Care Insurance in China,D922.284
  12. Effects of Acupuncture Pre-conditioning on Cerebral Ischemia-reperfusion Injury in Aged Rats,R245
  13. Experimental Investigation on New Style of Cemented Carbide Bits and Drilling in Hard Rock,TD421.25
  14. Study on Alloying and Ageing Hardening of Mg-Zn-Al-Ca Magnesium Alloy,TG156.92
  15. Research on Self-shielded Hard-facing Flux-cored Wire and Its Properties,TG422.3
  16. High-rise apartment interior public transport elderly humanized design space research,TU241.93
  17. X12CrMoWVNbN ferritic heat-resistant steel thermal processing of Microstructure Evolution,TG142.73
  18. Butyl rubber absorbing properties of boron carbide composites research,TB332
  19. Study on Microstructure and Properties of Copper Alloy Mould of Horizontal Continuous Caster,TF341.6
  20. Investigation of Ageing Technics and Microstructure Analysis of 6N01 and 7n01Alloys,TG156.92
  21. Investigation of High Strain and Low Cycle Fatigue Behaviors of Hot Rolled and High Strength H-beam Steels,TG335.11

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metallic materials > Steel > Microstructure and properties of steel
© 2012 www.DissertationTopic.Net  Mobile