Pitting corrosion behavior of 0Cr15Ni5Cu3Nb stainless steel in Cl~- medium and protection

Author: LiYuanSong
Tutor: YangShuHe
School: Yangzhou University
Course: Materials Processing Engineering
Keywords: 0Cr15Ni5Cu3Nb Martensitic precipitation hardening stainless steel Cl~-pitting Solid solution+adjust ten aging treatment
CLC: TG172
Type: Master's thesis
Year: 2013
Downloads: 33
Quote: 0
Read: Download Dissertation

Abstract


Chemical immersion method and electrochemical impedance technique, this paper studies the0Cr15Ni5Cu3Nb stainless steel in solution containing Cl" medium neutral corrosion behavior. On the basis of preliminary demonstration and test the0Cr15Ni5Cu3Nb6kinds of steel heat treatment process is determined. Using potentiodynamic polarization and cyclic sample of different heat treatment states Cl" pitting resistance was analyzed. Using SEM, EDS and XRD analysis of the microstructure and composition, and various organizations on the corrosion resistance after heat treatment are discussed in this paper. The influence of Chemical immersion test shows that after soaking wafer sample for macroscopic observation,6set sample are a little cavitation. Corrosion rate was calculated by the weight loss method,12h corrosion rate is very fast, but after72h, corrosion rate is leveling off, the corrosion rate is nearly four times. At the beginning of the pitting because Cl" concentration produces poor Cr area and uneven easily dissolved passivation membrane formation, in the center of the erosion hole edge will generate a new activation, new nuclear generation accelerates the iron substrate loss, also is the main reason for the initial corrosion rate is faster.0cr15ni5cu3nb corrosion of stainless steel based on Cl" environment, in the early stage is the focus of the protection. To avoid Cl" concentration, prevent to produce new activation center, speeds up the valve or piping containing Cl" liquid medium.Directly after solid solution aging due to C and Cr form Cr23C6phase, resulting in poor Cr area. Pitting nuclear priorities in the lean Cr23C6form around. Compared with the untreated sample, pitting corrosion resistance decrease. And adjust the processing after0Cr15Ni5Cu3Nb stainless steel Nb and C is preferred to generate Nb C phase in the organization, reduce Cr23C6phase formation, and makes the martensite structure small features, could improve the ability of resistance to pitting of Cl-. To adjust processing, with the increase of adjusting temperature, the precipitation of Nb C less gradually, increase the poverty degree of Cr in the region, there will be a small amount of lean Cr area, thus the corrosion resistance and reduced. Because when adjust the processing temperature, the solubility of Nb is reduced, the inhibitory effect on the phenomenon of poverty is Cr in steel decreases, thus resistance to pitting corrosion performance degradation. Eventually determine0Cr15Ni5Cu3Nb martensitic precipitation hardening stainless steel resistant to Cl" pitting the best heat treatment process is a solid solution (1050℃+1h, water-cooled)+adjustment (815℃(0.5h)+time (520℃by4h, air cooling).

Related Dissertations

  1. Plasticity Performance of OCr15Ni5WMoVNb Martensite Precipitation Hardening Stainless Steel,TG142.71
  2. The Experimental Investigation of Stress Corrosion for 34CrMo4 Alloy Steels in Wet H2S Environment,TG172.9
  3. The Research on the Corrosion of Lithium and Magnesium Cell Linings in Chloride Molten Salts,TG172.62
  4. Research on the Metal Erosion-corrosion Base on a Failure Analysis about the Elbow,TG172
  5. Electrochemical Corrosion Behavior of Carbon Steel Under the Combined Electrolyte Layer of Open and Confined Layer,TG172
  6. Study of Corosion Behavior of Magnesium Alloys in Commercial Engine Coolant,TG172
  7. Corrosion Behaviors of Candidate Materials for Supercritical Water Reactor,TG172
  8. Failure Analysis on Duplex Stainless Phosgene Reactor and Study on Corrosion Properity,TG172
  9. Erosion and Corrosion of Gas-solid Two-phase Flow in Pipes,TG172
  10. Corrosion Behavior of the Metal and Coating Systems in the Petrochemical Atmospheric Environment,TG172.3
  11. Research on Pitting Behaviors of X120 Pipeline Steel in HCO3- +Cl- Solution,TG172
  12. Corrosion Behavior Research of 7B04 High-strength Aluminum Alloy and Its Protective Coating in Marine Atmospheric Environment,TG172.3
  13. Research on Stress Corrosion Cracking and Corrosion Fatigue of ZL101 Aluminum Alloy,TG172
  14. Electrochemical Distribution Characteristics of Corrosion Behavior of Carbon Steel Immersed in Seawater,TG172.5
  15. 7B04 aluminum stress corrosion studies,TG172.9
  16. Effect of the Different PH Acidity to the Corrosion Behavior of X70Ce Steel in Different Soil Simulated Solution,TG172.4
  17. Corrosion Mechanism and Preventive Measurements of Sulfuric Acid Making Plant,TG172.6
  18. Corrosion of aluminum alloy 5052 seawater,TG172.5
  19. Effect of Sulphate Reducing Bacteria on Corrosion of Zn, Al Sacrificial Anode Materials in Marine Sediment,TG172.7
  20. Effect of Crevice and Hydrostatic Pressure on the Corrosion Behaviors of 316L Stainless Steel,TG172
  21. Study on the Corrosion Behavior of Oil Pipeline Steels in Carbon Dioxide and Hydrogen Sulfide Solution,TG172

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Various types of metal corrosion
© 2012 www.DissertationTopic.Net  Mobile