Microstructure and High Temperature Oxidation Behavior of Mn-Ni Coatings Fabricated by Electrodeposition

Author: ChenHong
Tutor: OuYangJiaHu
School: Harbin Institute of Technology
Course: Materials Science
Keywords: electrodeposition coating oxidation resistance ASR connection
CLC: TG174.4
Type: Master's thesis
Year: 2012
Downloads: 24
Quote: 0
Read: Download Dissertation

Abstract


In this paper, electroposition of Mn–Ni alloys on stainless steel surface hasbeen studied. The effects of different agent concentrations, current densities, saltconcentrations on the coating morphology and composition have been carried out.The morphology and composition were analyzed via Scanning electron microscopeand Energy spectrum characteriation. To increase the content of manganese ofcoating, double–complexing agents were applied. The optimized parameter wasachived by subsequent pre-oxidation. In this optimized process, content ofmanganese is up to30%. Oxidation performance test was done by weight gaincharacterization and the mechanism of oxidation was studied.The results showed that, to get homogeneous alloy coating, the concentration ofcomplexing agent must be higher than metal cation. Once the contentration is belowgoal concentration, the bath will be of instability. A substantial increase ofmanganese content in coatings can be got via the increase of intensity. As theincrease of current density, the manganse content will increase too.Electrodeposition process parameters were optimized through morphology andcomposition after the pre-oxidation experiment. In this process, this technology canget30%manganese content in the alloy coating. Then the coating sufferedsubsequent cycle high–temperature oxidation. This paper studied their oxidationresistances and their conductivities at high temperatures, and found that theoxidation resistances were significantly improved with the oxidation rate constant of3.2631×10–8g2·cm–4·h–1, SEM and X–ray diffraction analysis of oxide morphologyand micro–structure after cyclic oxidation were applied, the results suggested theoxide coating was mainly composed of the outside nickel–manganese spinel layerand the inner chromium oxide layer, The cross–section spectrum analysis of oxideshowed that the outside oxide did not contain chromium, this double oxide layer canprevent the volatilization of chromium to the surface, The area specific resistance ofoxide coating after200h oxidation was13Ω·cm2, and it was less than the fuel cellconnection material requirement under the high temperature oxidation. Ultimately,the studies above proved the Ni–Mn alloy coating by electrodeposition system canbe used as a connection material of the fuel cell.

Related Dissertations

  1. Preparation of Micro-Arc Oxidation Ceramic Coating on Mg Alloy and the Research of Galvanic Corrosion,TG174.453
  2. The Effect of Current Density and Electric Field on Ni and Its Alloy Electrodeposition for Copper Crystallizer,TQ153.2
  3. A Study on the Electrodeposition of Zn-Co and Zn-Ni Alloys in the Reline Room Temperature Ionic Liquid,TQ153.1
  4. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  5. Preparation and Performance of V2O5-WO3/MOx/Cordierite Catalyst Modified with Cu、Mn、Ce for DeNOx,X701
  6. Solid Oxide Fuel Cell ferrite connect the material properties of,TM911.4
  7. LSGM electrolyte thin films and electrochemical properties of,TM911.4
  8. Anti-corrosion Property of Flake Zinc Epoxy Coating Doped with Rare Earth in SRB,TQ630.1
  9. Research on PSA/Cotton Blend Fabric of Coatinging of Water Resistance and Moisture Permeability,TS195.6
  10. Study on Chitosan-Based Composiate Nano-Coating Dope and Its Effect of Fresh-Keeping for Coated Egg,TS253.2
  11. Development and Application of Biological Seed Coating Formulation for Soybean,S565.1
  12. Research on the Online Parallel Connection Examination and Approbation System,D630
  13. On Novel-Reading Teaching in Senior Middle School Based on the Education Connection,G633.3
  14. Preparation of Electrode by Electrodeposition and Study on Performance of Degradation Phenol Wastewater,X703
  15. Preparation of polyaniline nanostructures , characterization and biomedical applications,TB383.1
  16. Electrochemiluminescence Immunosensor Based on Nanocomposite Film of Surface Modified and Assembled CdS Nanoparticles,TP212.2
  17. Investigation of Plasma Sprayed NiCr-Cr3C2 Coating on Mould CrZrCu Alloy Plates,TG174.442
  18. A Study of Archetypes in E. M. Forster’s Short Stories,I561.074
  19. Connection of the Elective Module and the Compulsory Module in Teaching of the New National Geography Curriculum,G633.55
  20. Synthesis of Platinum-based Composite Catalysts and Their Electrocatalytic Properties for Methanol Oxidation,TM911.4
  21. Copper Electrodeposition from Non-Cyanide Alkaline Baths Containing Methylene Diphosphonic Acid as a Complexing Agent,TQ153.14

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile