The Study on Process of ZnO Varistors with High Voltage-gradient and High Surge Current Withstanding Capactiy

Author: WengJunMei
Tutor: JiangShengLin
School: Huazhong University of Science and Technology
Course: Microelectronics and Solid State Electronics
Keywords: ZnO varistors Pre-synthesis Oxidation treatment High voltage-gradient
CLC: TM54
Type: Master's thesis
Year: 2013
Downloads: 11
Quote: 0
Read: Download Dissertation

Abstract


ZnO varistors have been widely used in the field of power systems and electroniccircuits for its excellent nonlinear voltage-current properties and surge current adoptioncapacity. However, this field is still expecting to improve the surge current withstandingcapability as well as voltage-gradient. At present, the voltage-gradient of domestic factoryproduction is about200V/mm, and there is a big difference from foreign level, thus thisthesis focuses on the process and production of high voltage-gradient varistor with highsurge current withstanding capability while maintaining other electrical characteristicsincluding pre-synthesis and oxidation treatment.First of all, MgO and SiO2compounds were pre-synthetized and doped to improve thedensities. The results indicate that when MgO and SiO2compounds were pre-synthetized,the densities of zinc oxide varistors are improved significantly, but the breakdown electricalfield is reduced. The breakdown electrical field of the varistors is340V/mm whilenonlinear coefficient is89, and the leakage current density is0.07μA/cm2.Then, different proportions of Bi2O3and Sb2O3compounds were pre-synthetizedthrough solid-state reaction method to produce high voltage-gradient varistor with highsurge current withstanding capability, and the effect of the compounds on the densities,grain structure and electrical properties of zinc oxide varistors were studied. The resultsindicate that when the compound proportion of Bi2O3and Sb2O3is0.7:1, electricalproperties of zinc oxide varistors are the best, and uniformly dense grain structures areobtained. After wave surge current impulse of5KA current with a time length of8/20μs,the residual voltage ratio and breakdown voltage variation are2.6and2.5%respectively.The breakdown electrical field is361V/mm while nonlinear coefficient is86, and theleakage current density is0.07μA/cm2.At last, the varistors were treated with oxidation processing to reduce the residualvoltage ratio and improve its stability. The effect of different oxidation temperature on grainstructure and electrical properties of zinc oxide varistors were studied. The results indicatethat when the varistors are oxided under900°C, the comprehensive performance of varistors is improved. The breakdown electrical field is390V/mm while nonlinearcoefficient is95, and the leakage current density is0.14μA/cm2, and after wave surgecurrent impulse of5KA current with a time length of8/20μs, the residual voltage ratio andbreakdown voltage variation are2.2and2.1%respectively.

Related Dissertations

  1. Study on New Technique Manufacturing ZnO Varistors,TM54
  2. The Improvement of the Performance of the Low-voltage ZnO Varistors,TM54
  3. Electrochemical studies of single-walled carbon nanotubes modified electrode developed and cytochrome C on the modified electrode,O646
  4. Laowangzhai Gold Gold Extraction Process,TF831
  5. Activated carbon fiber paper and its function,TS761
  6. Electrical and Microstructure Properties of Y2O3-doped ZnO-based Varistor,O482.41
  7. Biocompatibility of Activated Low Modulus Ti-29Nb-13Ta-4.6Zr and Ti-Nb-Zr-Sn Alloy,R783.1
  8. Preparation, Transformation and Properties of Carbon-Encapsulated Metal Nanoparticles,TB383.1
  9. Effect of Pre-Oxidation Treatment on the Service Life of Thermal Barrier Coating,TG174.4
  10. Research on the Degradation of Surge Protector in Low Voltage Power System,TM862
  11. The Gudong of oilfield wastewater efficient processing technology research,X741
  12. Preparation of Carbon/Carbon Composites Using Mesocarbon Microbeads as Matrix,TB332
  13. The thermoluminescence acid cross -linking studies of CTP plate,TS802.4
  14. ZnO Varistor of High Volt-Gradient,TM54
  15. Improved Performance of ZnO Varistors,TM54
  16. Treatment for Bamboo Fibers and Yarns Using Ozone,TS959.2
  17. Study of the Techniques to Enhance Bonding Strength between Diamond and Matrix in Electrodeposited Diamond Tools,TQ164
  18. Growth and Characterization of PbWO4 Crystal,O734
  19. Improvement of ZnO Varistor Performance,TM54
  20. New high Cr hot work die steel surface Tufftride thermal fatigue and high temperature wear on the impact of,TG156.82

CLC: > Industrial Technology > Electrotechnical > Electrical > Resistor,potentiometer
© 2012 www.DissertationTopic.Net  Mobile