Study on the Preparation and Properties of Silane Grafting Polyphenylene Sulfide (PPS)

Author: DiZuoJun
Tutor: ZhouXiaoDong
School: East China University of Science and Technology
Course: Chemical Engineering
Keywords: Polyphenylene sulfide grafting modification silane crosslinking toughen
CLC: TQ326.56
Type: Master's thesis
Year: 2012
Downloads: 151
Quote: 0
Read: Download Dissertation

Abstract


This research developed a new method of toughening Polyphenylene sulfide (PPS) by silane grafting. Siloxane flexible group was grafted onto PPS by suspension grafting and silane crosslinking technique. The influences of silicone content, reaction time, reaction temperature and solvents on the graft reaction were investigated. The kinetics of thermal decomposition and crystallization of silane modified PPS were also investigated, and finally its rheological properties and impact toughness were studied.It was found that grafting degree increased with the increasing of silicone content, reaction time, reaction temperature. The degree of grafting and crosslinking of silane modified PPS could be controlled by adjusting these reaction conditions. Thermogravimetric analysis (TGA) result showed that the thermal decomposition of silane modified PPS was divided into two steps. First was the silane which was grafted onto PPS, follow by PPS main chain. The initial thermal decomposition temperature was much higher than processing temperature. The studies of thermal decomposition kinetics indicated that thermal decomposition reaction of silane modified PPS was first-order reaction and the activation energy of thermal decomposition reduced compared to pure PPS, but it was still a good thermal stable material. WXRD and PLM directly reflected that the crystallization degree of modified PPS decreased and grain size reduced. Differential scanning calorimetry (DSC) testing results and the studies of crystallization kinetics of silane modified PPS showed that its crystallization temperature reduced and crystallization rate decreased. The nonisothermal crystallization mechanism of silane modified PPS is predominately two-dimensional growth with heterogeneous nucleation mode. The effects of grafting ratio and content of silane modified PPS on modified PPS/pure PPS blends were investigated by using a haake torsion rheometer. Melt viscosity of PPS was not sensitive to shear rate. Although the melt viscosity of modified PPS increased with increasing of grafting ratio, it was still lower than that of pure PPS. The impact toughness of the blends increased with the increasing of grafting ratio and content of silane modified PPS. As the grafting ratio of modified PPS was 12.7% and its content in the blends was 35%, the impact strength was increased 26.7% compared to pure PPS.

Related Dissertations

  1. Polyphenylene sulfide (PPS) meltblown nonwovens Preparation and spinning properties,TS174
  2. Toughen and Manufacture of Shape Memory Epoxy Resin Composites,TQ323.5
  3. Preparation and Properties of PolyPhenylene Sulfide (PPS)/Inorganic Particles Composites and Fibers,TB332
  4. Modification of Immiscible HDPE/PA6 Blends Using Carbon Nanotubes,TB383.1
  5. Polyphenylene Sulfide Strong Based Anion Exchange Fiber: Synthesis, Characterization and Adsorption Properties,TQ340.1
  6. Research of New Nafion Composite Proton Exchange Membrane Used in Fuel Cells,TM911.4
  7. Study on Widely-used Adhesives and Coatings Prepared by Modified Waste Polystyrene Foam Plastics,X705
  8. Research of Layered Manganese Oxide Composite Electrode Materials,TM910.4
  9. The Preparation and Application of High-performanced Polyphenylene Oxide Alloy,TQ326.53
  10. Research on Modification Phenolic Resin of In-Situ Dispersion Nano Grafting Multi-elements,TQ323.1
  11. Study on the Mechanism of Polyamide Membrane Degradation and Grafting Modification with ADMH,X703
  12. CNT / polyphenylene sulfide fiber toughening Preparation and Properties,TQ340.6
  13. Study on Thermal Conductive Polyphenylene Sulfide Composite,TQ320.7
  14. PPS composites dispersed nature and topographic characteristics on system performance,TQ326.56
  15. Study of Morphology and Properties of PP/EPDM/Nano-CaCO3 Ternary Composites,TB332
  16. Study of the Construction of Sandbag Microstructure in PA6/EPDM/nano-CaCO3 Ternary Composite and Its Toughening Mechanism,TB332
  17. The Spinnability Study of Peek and Other High-Temperature Thermoplastic Polymers,TQ340.64
  18. The Research of Bag with PPS-ATY Processing Technology and Its Structural Performance,TQ342.73
  19. Fabrication of Superhydrophobic Surfaces and Applications in Selective Separation of Liquids Differing in Surface Tention,TQ028
  20. Milled carbon fiber reinforced polyphenylene sulfide / graphite bipolar plate material preparation and properties of,TB332
  21. Structure and properties of polyphenylene sulfide composites,TB332

CLC: > Industrial Technology > Chemical Industry > Synthetic resins and plastics industry > Polymer resin and plastic > Polyether > Polythioether
© 2012 www.DissertationTopic.Net  Mobile