Preparation and Performance Research of Long-shelf Life and Low Temperature Carbon Fiber/Epoxy Resin for Hot-melt Prepreg

Author: WuXiang
Tutor: WuWei
School: East China University of Science and Technology
Course: Materials Science and Engineering
Keywords: Hot-melt Epoxy resin Prepreg Low curing temperature Shelf-life
CLC: TB332
Type: Master's thesis
Year: 2012
Downloads: 238
Quote: 0
Read: Download Dissertation

Abstract


The traditional high and moderate temperature curing prepreg moulding can result in high internal stress in composites, high energy consumption, and the narrow selection range in auxiliary material such as mould, which eventually led to high-cost of composite moulding.The long-shelf life and low temperature prepreg can greatly reduce high-cost.On the other hand, it can further reduce energy consumption because of the long-shelf life, thus the long-shelf life and low temperature prepreg will be a very important development direction in cutting down the cost of advanced composite.In this paper, with the combination system of the solid and liquid bisphenol A epoxy reisn for resin matrix, MNA as curing agent, BTEAC commonly used for phase transfer catalyst and cationic surfactants as accelerator, carbon fiber as strength material, the long shelf life and low temperature prepreg was prepared by the hol-melt route. The effect of the content of curing agent and accelerator on the film property, the viscosity-temperature characteristics, curing temperature and shelf life at RT was investigated by the DSC and rotational rheometer.The results show that the formula involves epoxy resin/curing agent/accelerator with mass proportion of 100/48～51/1.5～2.The epoxy resin film prepared by this system can be cured at 85℃, have excellent film forming properties and shelf life at RT for 8days.The carbon fiber/epoxy resin prepreg was prepared by the carbon fiber and epoxy resin film obtained by optimized epoxy resin formula.The effect of hot roller temperature, pressing times and line speed on the prepreg impregnation were investigated. The results show that the impregnation effect was the best, and the physical properties of prepreg is uniform and stable when the hot roller temperature was 65℃～70℃, line speed was 3m/min-4m/min, pressing times was 13times～17times. The unidirectional composites laminates were prepared by the moulding process.The mechanical properties, water absorption, hygroscopicity and fracture morphology were studied.The results show that the composites had excellent mechanical performance, such as flexural strength was 1025MPa, interlaminar shear strength was 70MPa. The composites had good interface bonding performance, low water absorption and low hygroscopicity.

Related Dissertations

  1. The Research about the Processing and Performance of Waterproof Breathable Laminated Fabrics,TS195.6
  2. Recycling Technology of Wasted Fiberglass Reinforced Plastics,X705
  3. The Hot-melt Paint Used as a Primer of Bamboo Scrimber Flooring to Restrict the Appearence of Cracks,TU531.3
  4. Synthesis of Rosin-based Curing Agents and the Curing Behavior with Epoxy Resin,TQ351.471
  5. Research on High Thermal Conductivity Epoxy Casting Compound,TQ433.437
  6. Study on the Preparation and Performance of Epoxidized SIS HMPSA for Chinese Medical Extract Patch,TQ436.3
  7. Synthesis of Cyclotriphosphazene-Based Flame Retardant and Its Effect on the Flame Ratardance of Epoxy Resin,TQ323.5
  8. Research on Toughening Epoxy Resin and Its Damping Property,TQ323.5
  9. Synthesis of Doping Polystyrene and Polyacrylic Acid Ester Functional Materials,O631.3
  10. Study on the Two-Stage Curing Technology of a New Shape Memory Epoxy Resin,TQ323.5
  11. Synthesis of Epoxy Resin Model Compounds and Their Decomposition in Near-Critical Water,TQ323.5
  12. The Effect of Acid/Base Catalyst on Degradation Behavior of Epoxy Resin in Nearcritical Water,TQ323.5
  13. Preparation and Characterization of Microencapsulated Ethylene Diamine,TQ320.1
  14. Application of Ketone-Hydrazide and Blocked Isocyanates Double Cross-Linking System in Cathodic Electrodeposition Coating,TQ630.4
  15. Study on the Preparation and Properties of Carbon Fiber Prepreg,TB332
  16. Study on Properties of Epoxy Resins Modified by Inorganic Nano-particles and Polyurethane,TB383.1
  17. Preparation and Properties of Epoxy/SiO2 Hollow Spheres Nanocomposites,TB383.1
  18. The Effects of Reactive Carbon Nanotubes on Interface Bonding and Mechanical Properties of Fiber Reinforced Composites,TB332
  19. Accelerated Thermo-Oxidative Aging on Carbon Fiber/Epoxy Composite,TB332
  20. Manufacturing and Properties of Pultruded Carbon Fiber/Glass Fiber Coaxial Composite and Composites Reinforced by Functional Carbon Nanotube,TB332
  21. A Research on Curing and Deflation Behaviors and Properties of Micron-Al2O3/Epoxy Resin,TB332

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Composite materials > Non-metallic composite materials
© 2012 www.DissertationTopic.Net  Mobile