Technical Study on Chemical Mechanical Polishing of CVD Diamond Film

Author: WangKun
Tutor: JinZuoJi
School: Dalian University of Technology
Course: Mechanical Manufacturing and Automation
Keywords: CVD diamond film CMP Slurry Friction
CLC: TG175
Type: Master's thesis
Year: 2010
Downloads: 156
Quote: 1
Read: Download Dissertation

Abstract


Diamond is widely applied in many fields due to its excellent performance in mechanics, thermodynamics, optics, acoustics and semiconductor. Chemical vapor deposition technology has advanced the growing rate and quality of diamond and the price has been reduced significantly. However, because of the limit of growing theory and technology, CVD diamond film usually has rough surface and polishing is required ahead of practical application.Existing planarization technologies mostly are unable to achieve ultraprecise maching of diamond with low scathing resulted. CMP(Chemical Mechanical Polishing) is considered to be one of the most prospective methods. In this thesis based on the analysis about existing problems of CMP of diamond, a technology of combining lapping and CMP with heating partly was proposed. The main contents are as follows:(1) The technology of combing lapping and CMP with heating partly was used to process diamond film. The results show that the surface roughness can be reduced from Ra13.3μm to Ra40nm quickly, and CMP can not only process the diamond film precisely, but also avoid warp and wear of plate induced by heating globally.(2) Key components of slurry were optimized. Six kinds of slurry with six different oxidants were analyzed and tested. K2FeO4 turns out to be best. It is proved that mutual action of mechanical action and chemistry plays an important role in material’s remove through experiments.(3) Through single-factor experiments, effect of temperature, pressure and plate’s rotate rate on polishing was investigated. Proper technic parameters were settled:temperature 50℃, pressure 266.7 kPa, plate rotate rate 70r/min. With these parameters diamond film was polished for 7 hours and the surface roughness reached Ra4.5nm.(4) The setup was designed and made for friction measurement of diamond film. Online measurements about friction and its discipline versus pressure, rotate rate and so on were conducted. Mixed lubrication between film and plate could be deduced. The relationship between friction and material removal rate was analyzed to make preparation for study on mechanism of chemical mechanical polishing diamond.

Related Dissertations

  1. Study on Contact Fatigue Life Based on Grease Variation with Temperature,TH117.22
  2. Direct shallow trench isolation planarization technology research and application,TN305
  3. Study on Synthesis and Characterization of Flocculating Sedimentation Agent and Its Application,TE39
  4. Study on Surface Roughness and Anti-Oxidation Corrosion for Al-Mg Alloy Chemical Mechanical Polishing,TG174.4
  5. Design and Manufacturing of Bionic Polishing Pad and Research on Kinematical Analysis Base on Sunflower Seed Pattern,TN405
  6. Triboelectrostatic machine mineral particles dynamics research and analysis,TD457
  7. AC austenitic stainless steel surface pretreatment studies with low-temperature plasma nitriding,TG156.82
  8. Influence of Welding Conditions on Temperature Distributions and Quality of Friction Stir Welding Butt Joints,TG453.9
  9. Cu/QCr0.5 carrier friction and wear properties under study,TG115.58
  10. Al-Si alloy high-temperature friction surface silicon phase of refinement and spheroidization,TG453.9
  11. Biaxial friction observer based platform system controller design contours,TM341
  12. Worsted wool warp sizing in product processing Application Research,TS105.213
  13. NiTi alloy coated stainless steel surface preparation,TG174.44
  14. Valve material surface modification layer prepared a variety of techniques Study,TG174.44
  15. Endogenous iron-based composites and tribology research,TB331
  16. Polymer solar cell structure design and performance optimization,TM914.4
  17. Water-based casting Cordierite ceramic green sheet and its properties,TQ174.62
  18. The Study on Surface Crack and Performance of Brake Lining,U463.5
  19. The Research on a New Dynamic Ice-making Device,TB657.1
  20. Slurrying and Viscosity Characteristic of Coal-Oil Slurry with High Inertinite Content,TQ533.3
  21. Study of the Locked Hydraulic Soft-Start Equipment,TD528.1

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Metal electropolishing and chemical polishing
© 2012 www.DissertationTopic.Net  Mobile