Study on Extending the Life of Electroless Nickel Plating and Electroless Composite Plating Solution

Author: ZuoCui
Tutor: LiuJinYun
School: West China University
Course: Materials Science
Keywords: electroless plating Ni-P electroless Ni-P/Al2O3 composite plating deposition rate bath life
CLC: TQ153
Type: Master's thesis
Year: 2011
Downloads: 79
Quote: 0
Read: Download Dissertation

Abstract


The electroless plating Ni-P is surface treating technology using self-catalyze reduction, which has been applied in many industrial fields in recent half century. Based on this, by changing the matrix of metal and dispersed particles, to obtain good resistance to wear, self-lubricating ability, heat-resistant ability and special decorative ability etc., the electroless plating composite coating also has a wide range of applications.However, the key of electroless plating nickel and electroless composite plating is the formula of the bath and the way of maintenance. Extended the bath life can effectively decrease production costs and pollution releases. Therefore, the study on extending the life of the plating bath is great significance.The electroless plating Ni-P was taken through three different plating methods in this thesis, that including non-additive solution plating, adding directly addition liquid plating and interval fetching fluid method plating, the properties of the coatings were tested. According these properties, the bath life can be assessed. The electroless Ni-P/Al2O3 composite plating was taken using the interval method. The properties of the Ni-P/Al2O3 coatings were tested. The results show that:Taking the non-additive solution plating, the bath of the electroless plating Ni-P deterioration occurred with the organic acids decomposition, alkali metal ion and acid radical ion concentration increasing. The deposition rate of the coating decreased about 50% after plating three times.Taking adding directly addition liquid plating, the bath of the electroless plating Ni-P failure has alleviated in a certain degree. The rate of change of the coating thickness is small. But only plating 6 times, the deposition rate is from 12.2μm/h decreased to 3.9μm/h. Taking the interval fetching fluid method plating, the bath of the electroless plating Ni-P can be used continuously up to 10 times. The coatings have good properties. The rate of change of the thickness and the micro-hardness of the coatings is very small, the deposition rate steady at 12μm/h.Taking the interval fetching method plating, the bath of the electroless Ni-P/Al2O3 composite plating can be used continuously up to 10 times. The micro-hardness of composite coating can reach HV700, the rate of change of the coating thickness and micro-hardness is very small, the deposition rate is about 7μm/h and stable.The porosity of the electroless Ni-P coatings and the electroless Ni-P/Al2O3 composite coatings, taking the interval fetching fluid method plating, is very small, and the corrosion resistance of the coatings is good. In summary, taking the interval fetching fluid method plating to take the electroless plating Ni-P and electroless Ni-P/Al2O3 composite plating, can effectively extend the bath life, and the coating has good properties.

Related Dissertations

  1. Electroless Deposition of Ni-W-P Coating on AZ91D Magnesium Alloy,TQ153.1
  2. Properties of Silicon Nitride Thin Films Deposited by R.F Magnetron Sputtering,O613.72
  3. Electroless Nickel Plating on Mg-Li Alloy by Two-step Process,TG174.44
  4. Electroless Plating Ni-P(W) and the Coatings with a Chromium-Free Pretreatment on AZ91D Magnesium Alloy,TG174.44
  5. Research of the Influence of Rare Earth to the Technology of the Chemical Plating Ni-P and Performance of Coating,TQ153
  6. Preparation, Microstructure and Property of Electroless Ni-B Alloy Deposits,TQ153.1
  7. Research on Chromium-free and Low Cost Process of Chemical Plating Ni-P on Magnesium Alloy,TQ153.2
  8. Preparation of Coated Lysine and Its Effects on Growth Performance and Feed Utilization in Tilapia Nilotica and Approaching to Its Mechanism,S963
  9. Study on the Fabrication Technology of Amorphous Silicon Films by PECVD on Lowcost Substrates,TN304.055
  10. Sheyang modern sedimentation rate and its estuary Heavy Metal Pollution,X522
  11. Technology of Effective Trivalent Chromium Plating,TQ153.1
  12. Study on Ni-Cr Co-deposition on Polyurethane Foam,TQ153
  13. PECVD prepared amorphous silicon thin film and photoelectric properties of,TN304.055
  14. Study on Electroless Plating Ni-Co-P Alloy Protection Deposit of Sintered NdFeB Permanent Magnet Material,TG174.44
  15. Study on Electroless Ni-Zn-P Alloy Process and Coating Properies,TQ153.2
  16. Research on Electroless Plating and Corrosion Resistance of Ni-Co-P Coating on AZ31 Magnesium Alloy,TG174.4
  17. Electroless Deposition of Fe-Me-P Alloys and Their Performance Characteristics,TG174.44
  18. Research on the Model of Wax Deposition,TE832.3
  19. Research on Process and Properties of Hot Wire TIG Welding,TG444
  20. Circular magnetron sputtering deposition uniformity control and its impact on film quality,TB43
  21. Study on the Improvement of Performance of Ni-W-P Coatings after Heat Treatment,TG174.44

CLC: > Industrial Technology > Chemical Industry > Electrochemical industries > Electroplating industry
© 2012 www.DissertationTopic.Net  Mobile