Studies on Modification of Epoxy Resins

Author: WuZuo
Tutor: ZhuChuanFang
School: Central China Normal University
Course: Polymer Chemistry and Physics
Keywords: Epoxy resin Phenolic resin Acrylic resin Nano-silica Modify Solidification
CLC: TQ323.5
Type: Master's thesis
Year: 2011
Downloads: 190
Quote: 0
Read: Download Dissertation

Abstract


This paper introduced phenolic resin and acrylic resin to modify epoxy resin, and studied the synthesis and properties by adding nano-silica.The nano-silica modified phenolic resin pre-polymer was prepared by using bisphenol A and formaldehyde as basic materials and adding nano-silica.The nano-silica modified phenolic resin was obtained by copolymerization of the pre-polymer and epoxy resins. The product was investigated and characterized by IR, particle size distribution, scanning electron microscope and property test of the coating films. The results showed that the nano-silica dispersed in the copolymer uniformly and it indicated that the hydroxy groups of nano-silica took part in the copolymerization of phenolic resins. The addition of nano-silica had little effect on the structure of phenolic epoxy resins. The water boiling resistance, yellow temperature, hardness, water absortion rate and saline corrosion resistance of the coating film could be improved effectively by adding the nano-silica compared with the unmodifified phenolic epoxy resins.The nano-silica modified acrylate resin pre-polymer was prepared by using acrylic acid as basic materials and adding nano-silica. The nano-silica modified acrylic resin was obtained by copolymerization of the pre-polymer and epoxy resins. The product was investigated and characterized by SEM, DSC, TG and property tests of the coating films. The results showed that the nano-silica dispersed in the copolymer uniformly and it indicated that the hydroxy groups of nano-silica took part in the copolymerization of epoxy acrylate resins. The addition of nano-silica had improved the weatheability of the copolymer. The water boiling resistance, yellowing temperature, hardness, water absorption rate and saline corrosion resistance of the coating film had be heightened effectively by adding the nano-silica compared with the unmodified epoxy acrylate resins.The acrylate resin pre-polymer was prepared by using acrylic acid as basic materials. The acrylic modified epoxy resin was obtained by the copolymerization of the pre-polymer and epoxy resins, and crosslinked by aminopropyltriethoxysilane, 2,2’-(1,3-phenylene)bis(2-oxazoline), IPDI-trimer and IPDI-hybridtrimer. Compared the water logging and boiling resistance, water absorption rate, yellowing temperature, hardness, adhesive force and saline corrosion resistance of the coating film and selected the suitable curing agent and volume of addiction to solidify the acrylic modified epoxy resin.

Related Dissertations

  1. Preparation of Based on the Phenolic Resin of Activated Carbon and Adsorption-Photopcatalytical Character of Supported TiO2,TQ424.19
  2. The Preparation and Electrochemical Tests of Carbon Foam,O613.71
  3. Study on Carboxyl Side Groups Containing Poly Aromatic Ether Sulfone Ketone and Modification of Epoxy,O631.3
  4. Study on Organic Silicone Modified Epoxy Resins Performance and Preparation of Adhesive,TQ323.5
  5. Modification of Thermosetting Resins by High Performance Liquid Crystalline Epoxy Resin,TQ323.5
  6. Electrically Conductive Adhesives Based on Epoxy Resins Modified by Polyimide Powder with Carboxyl Groups,TQ433.437
  7. Preparation of Epoxy Resin Cured with Latent Curing Agent at Moderate Temperature,TQ323.5
  8. Preparation and Property Study of Glass Cloth Reinforced F Class Laminates Based on Halogen-free Retardant Epoxy Resin,TQ323.5
  9. Preparation of Unfired Bricks by Industry Sludge Solidified Cement and Analysis of Economy and Technique,X703
  10. Studies on Genotoxicity of Two Novel Contraceptive Materials,R114
  11. Molecular Genetic Analysis of One Chinese Family with Leber’s Heriditary Optic Neuropathy,R774.6
  12. Study of Composite Drive Shaft for an Automobile,U465.6
  13. Solidification/Stabilization Research of Hazardous Waste Containing Nitrobenzene,X703
  14. Phase-field Simulation of Forced Flow Effect on Solidification Microstructure,TG111.4
  15. Qrganic Molecular Chain Modification of Carbon Nanot-ubes and Their Application for the Epoxy Resin,TB383.1
  16. Synthesis and Application of new hyperbranched polymers,TQ323.5
  17. Study on the Cure Kinetics and Thermal Properties of Commercial Epoxy Resins Modified by Epoxy-POSS and NH2-POSS,O631.5
  18. Crystallization, Melting Behavior and Disorder-to-Order Phase Transtion of Poly(Lactic Acid),O631.3
  19. Numerical Simulation of Granulation and Waste Heat Recovery Process for Blast Furnace Slag,X757
  20. Synthesis and Properties of Styene-Acrylic Resin for Water-based Ink,TQ638
  21. Shougang Slab Continuous Casting Cold Water on the Dynamic Control of the Establishment and Implantation of Model,TF341.6

CLC: > Industrial Technology > Chemical Industry > Synthetic resins and plastics industry > Polycondensation resin and plastic > Epoxy resins and plastics
© 2012 www.DissertationTopic.Net  Mobile