Dissertation > Excellent graduate degree dissertation topics show

Preparation of WC-composited Wear-resistant Coating by Thermal Spray Methods

Author: CongDongFeng
Tutor: DuXiaoDong
School: Hefei University of Technology
Course: Materials Science
Keywords: arc spray argon shielded arc remelting microstructure wear resistance wear mechanism
CLC: TG174.4
Type: Master's thesis
Year: 2009
Downloads: 184
Quote: 0
Read: Download Dissertation

Abstract


WC composite wear-resistant coating were coated on the surface of 45# steel by means of the improved arc spraying technology, and then remelted by argon shielded arc remelting technology.The microstructure of the composite coating was investigated by means of metallographic microscope, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The microhardness of composite coatings was measured by the microhardness instrument. And changes in microhardness of the cladding layer were analyzed.The wear resistance of the composite was tested by an MM-200 friction wear testing machine under unlubricated condition. The friction surface morphology was observed by means of scanning electron microscopy (SEM), and the wear mechanism was investigated.The results show that the method of the improved arc spraying technology feasible in laboratory. Some WC composite coating samples with different WC content were prepared. The microstructures of composite coatings after argon shielded arc remelted are more homogeneous and refine than WC-steel composite coatings after arc sprayed. And in the coatings, the lamellar character of the microstructure disappeared, defects eliminated, the cladding layer and the substrate transition zone between the relatively has a gentle microhardness gradient. The composite coatings are mechanically bond after arc spraying, but metallurgical bond after argon shielded arc remelted to the base metal. The hardness and wear resistance of the WC composite wear-resistant coat can be greatly improved as a result of the generation of amounts of finer particles with appropriate WC content. As the WC content increased, the hardness of the coating will increase, but the wear properties to deteriorate after the first changed for the better. There is a best content of WC in WC-composite coating in order to improve wear resistance of materials. There are different wear mechanisms, with different WC content in composite coating. The dominant wear mechanism is adhesion and slight cutting for that with 10wt%WC content, heavy cutting for the clad with 15wt%WC content, slight cutting and spalling with 20wt%WC content, and spalling with 25wt%WC content.

Related Dissertations

  1. Reactive Hot-Pressing and Mechanical Properties of （ZrB2-ZrO2）/BN Composites,TB332
  2. Microstructure and Mechanical Properties of Mg-Zn-Y-Zr Alloys,TG146.22
  3. Investigation on Microstructure and Properties of Cadmium-Free Silver-Based Intermediate Temperature Filler Metals,TG425.2
  4. Research on Technology and Mechanism of Joining Cemented Carbide to Carbon Steel,TG454
  5. The Investigations on the Characteristics and Mechanism of NIR Emission from Bi-doped Silicophosphate Glasses,TQ171.1
  6. Research and Development of Wear Resistance for Physically Disabled Men Jackets,TS941.2
  7. Preliminary Study on Salt-Tolerant Mechanism of the New Pennisetum Purpereum Schumach Variety-Sumu No.2,S543.9
  8. Study on the Fine Structure of Intestine and Intestinal Mucosal Barrier in Zebrfish (Brachydanio Rerio),Q95-33
  9. Study on Characteristics of Morphology Anatomy and Physio-Biochemistry of Two Ecotype Varieties Cucumber Leggy Seedilings,S642.2
  10. Study on the Mechanism of Heat-Induced Gelation of Myofibrillar Proteins,TS251.1
  11. Studies on the Aggregation and Microstructure of Imidazolium Ionic Liquids in Solutions,O645.1
  12. Studies of Luminescence Characteristics of Eu3+-doped Rare Earth Borates REBaB9O16 （RE=rare Earth Ions and Y）,O627.3
  13. The Research on Extrusion Parameters Through the Plate Billet of Magnesium Alloy,TG379
  14. Study on Stock Price Behavior Around Periodical Reports Based on Asymmetric Information,F832.51
  15. Research on Processings and Microstructure and Properties of HRB400MPa,TG335
  16. Study of Performance of Cordierite Combined Mullite Products,TQ175.71
  17. Effect of Adding ZrO 2 Nanopowder on Microstructure and Mechanical Properties of Carbon Steel,TB383.1
  18. The Broussonetia papyrifera fiber structure and properties of microwave - assisted the degumming process parameters optimization,TS123
  19. Studies on the Influence of Rare Earth Ce on Microstructure and Properties of Huge Heat Input SAW Seam Metal,TG445
  20. Hexagonal boron nitride micro- structure and adsorption properties of,TB383.3
  21. Rolled Mg-Zn-Ce-Zr (Mn) alloy microstructure and mechanical properties of,TG339

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile