Synthesis and Application of Halogen-Free Flame Retardant Dawsonite and Melamine Phosphate

Author: FanLeiLei
Tutor: NingGuiLing
School: Dalian University of Technology
Course: Chemical processes
Keywords: halogen-free flame retardant dawsonite flaming-retarded EVA melamine phosphate fire-retardant coating
CLC: TQ314.248
Type: Master's thesis
Year: 2009
Downloads: 246
Quote: 0
Read: Download Dissertation

Abstract


The tendency to eliminate halogen-based substances to reduce smoke toxicity during combustion has promoted research on halogen-free flame retardant（HFFR）.Different HFFR should be used because of the properties of polymer materials are diversity.The use of metal hydroxides,i.e.aluminium hydroxide（ATH） or magnesium hydroxide（MH） has drawn tremendous attention due to their smoke-suppression,low-toxicity and low cost.Halogen-free intumescent flame retardants especially the melamine salts as alternative materials have gained considerable attention because they provide fire protection with minimum of overall health hazard and prefect compatibility.In this thesis,a novel dawsonite flame retardant whiskers was prepared by hydrothermal method and melamine phosphate was successfully synthesized by simple craft.The main research works have been done as follows:（1）NaAl（OH）2CO3 whiskers were synthesized by hydrothermal method using aluminium isopropoxide which was prepared in lab freshly and NaHCO3.The crystalline structure, morphology and thermal stability of synthesized samples were characterized by XRD,SEM, FTIR and TG-DTG.The results indicate that the NaAl（OH）2CO3 whiskers possess particle length of 10～20μm,aspect ratio（length to diameter） of 20～40 respectively,and good distribution.The influences of acidity of the reaction medium,starting materials,reaction temperature and reaction time on the phase composition and morphologies of NaAl（OH）2CO3 whiskers were discussed.The thermogravimetric analysis of the whiskers show the decomposition process in two stages,the chemical reactions for the thermal decomposition happened and release massive nonflammable gas which can absorb a large amount of heat.（2） NaAl（OH）2CO3/EVA compounds were prepared by melt-blending.The effect of the amount of NaAl（OH）2CO3 additive on the flame retardance and mechanical properties of the composites were discussed.The flame retardance mechanism of NaAl（OH）2CO3 was also studied by TG-DTG,SEM and FTIR.The results show that the improvement of flame retardance properties and tensile strength accompanied with increase of NaAl（OH）2CO3. When the content of NaAl（OH）2CO3 in EVA is 40%,the compounds have good performance.（3）Melamine phosphate was prepared directly with melamine and phosphoric acid in water.The effect of the reaction factors such as reaction temperature,reaction time and the amount of water were investigated.The production were characterized by chemical analysis, FTIR and TG.In the case of amount of raw materials used in this reaction the optimal conditions for preparation are gained as follows:temperature:100～120℃,water:250ml, time:3h,the mother solution could be recycled 4 times.The yield of production reaches 95.5%～96%,the phosphorus content is 13.5%,and the decomposition temperature is about 250℃.（4）The fire-retardant coatings with pure acrylic ester emulsion as binder,water as solvent, flame retardant additives and other assistants were prepared by ball milling process.The effect of different flame retardants systems and enhance fillers on charring foam layer were investigated.The flame retardance properties of the coating were tested by simulative big panel method and cone calorimeter（CONE）.The results show that the coating with melamine phosphate,pentaerythritol,aluminum hydroxide and boric acid is the best one,the retardant duration is 25min.The CONE analysis results demonstrated that the heat release rate peak reduce from 338.78kW/m2 to 275.49kW/m2 compared with pure coating.Furthermore,the smoke production rate and total smoke production decreased obviously.

Related Dissertations

  1. Preparation and Property Study of Glass Cloth Reinforced F Class Laminates Based on Halogen-free Retardant Epoxy Resin,TQ323.5
  2. Study of Flame-Retardant and Impact Toughening Modification for Poly (2, 6-Dimethyl-1, 4-Phenylene Oxide) Based on Synegstic Effects of Phosphate and Polysiloxane,TQ325.14
  3. Synthesis of Melamine Polyphosphate and Its Application in Low Density Polyethylene,TQ325.14
  4. Study on Preparation and Properties of Sebs-based Thermoplastic Elastomers Filled with Halogen-free Flame Retardants,TQ334
  5. Study on Dopo Derivatives Flame Retardant Unsaturated Polyester Resins,TQ323.42
  6. Study on the Processing and Properties of Halogen Free Flame Retardant Ethylene Propylene Diene Monomer,TQ330.1
  7. Synthesis of Halogen-free Flame Retardant and Research of Its Flame Retardancy Effect on Polycarbonate,TQ314.248
  8. Study and Preparation of Water-based Epoxy Modifying Acrylate Intumescent Finishing Fire Retardant Coating,TQ637.8
  9. Synthesis and Properties of a Flame Retardant Silicon-Containing Curing Agent of Epoxy Resin,TQ323.5
  10. Preparation and Properties of Halogen Free Flame Retardant and Thermal Conductive Silicone Encapsulant,TQ436.6
  11. Study on the Super-thin Fire Retardant and Anti-corrosion Coating for Steel Structure,TQ637.8
  12. Intumescent Waterborne Modified-amino-resin Fire-retardant Coating for Wood,TQ637
  13. Study on Halogen Free Flame Retardance and Toughening of ABS,TQ325.2
  14. Studies on Photo-crosslinking of Ethylene-vinyl Acetate Copolymers/Inorganic Fillers Blends and Halongan-free Flame Retardant Polypropylene,O631.3
  15. Halogen free flame retardant in the preparation and application of PA6, PP,TQ314.248
  16. Study on Preparation and Chemical Cross-Linking Kinetics of Halogen-Free Fire-Retardant Polyolefine Cable Materials,TM247.1
  17. THE STUDY OF PE NON-HALOGEN FLAME-RETARDANT SYSTEMS AND FORMULATION FOR CABLE APPLICATIONS,TQ325
  18. The Study of the Formulations and Processing Parameter of Silane Cross-Linked PE Specially for Pipe and Cable,TQ325.12
  19. This Research of Un-haloid Flmae-resistant Polyolefin,TM246
  20. Ultrafine encapsulated red phosphorus in halogen-free flame retardant polypropylene,TQ325.14

CLC: > Industrial Technology > Chemical Industry > Molecular compound Industries ( polymer industry ) > Raw materials and auxiliary materials > Synthetic polymer compound > Additives > Flame retardants
© 2012 www.DissertationTopic.Net  Mobile