Study on Preparation of Ni-Cu-P Matrix Electroless Plating and Treatment of Electroless Plating Bath

Author: DanChuanLi
Tutor: HuangXinMin
School: Hefei University of Technology
Course: Materials Science
Keywords: Electroless deposition Nano-TiO2 Photocatalysis Corrosion resistance Waste solution treatment Remove rat
CLC: TQ153
Type: Master's thesis
Year: 2009
Downloads: 82
Quote: 1
Read: Download Dissertation

Abstract


In this paper,Ni-Cu-P was deposited by electroless plating.The effects of bath composition and operating condition on composition,microstructure,morphology, wear & friction and corrosion resistance of Ni-Cu-P were investigated.And the nano-TiO2 particles were introduced into electroless plating bath based on electroless plating Ni-Cu-P coatings to make the nano-TiO2 particles and,Ni、Cu、P matrix co-deposit to obtain nano-TiO2 electroless composite coatings.The effects of bath composition and operating condition on nano-TiO2 content in electroless composite coatings were researched.At the same time,microstructure,morphology and composition of Ni-Cu-P composite coatings were characterized by XRD,SEM and EDS techniques.The properties of composite coatings,such as Micro-hardness, wear resistance and corrosion resistance were investigated.Photocatalytic performance of nano-TiO2 composite coatings was evaluated.Metal ions and phsphorus remove with comlexzation deposition oxidation heavery is used by oxidation-deposition methed to explore an effective technique for electroless waste concentration treatment in order to decrease environment pollution.The result shows that deposition rate of electroless Ni-Cu-P coating decreases with the increase of CuSO4·5H2O concentration in bath.Micro-hardness of Ni-Cu-P coating can reach the highest value with CuSO4·5H2O concentration 0.6g/L. Crystallization of Ni-Cu-P coating takes place after 400℃heat treatment.Ni-Cu-P coating after 400℃heat treatment takes on excellent micro-hardness and wear resistance.Wear resistance can reach the highest value with the CuSO4·5H2O concentration 0.6g/L.of Ni-Cu-P coating presents better wear resistance than Ni-P coating.N-Cu-P coating possesses of favorable corrosion resistance.Ecorr moved positively first and than negatively with the increase of CuSO4·5H2O concentration in bath.Icorr of Ni-Cu-P electroless coating is the lowest with the CuSO4·5H2O concentration 0.4g/L.It is found from Salt-fog test that corrosion resistance of electroless coating which was introduced Cu is much better than Ni-P coating and 45# steel.Nano-TiO2 content in Ni-Cu-P-nano-TiO2 composite coatings increases in the first and then decreases with the increase of nano-TiO2 concentration in electroless bath.Nano-TiO2 content can reach 7.75wt%when nano-TiO2 concentration in bath is 6g/L.The corrosion resistance of Ni-Cu-P-nano-TiO2 composite coatings is much better than Ni-Cu-P coatings and Ni-P-nano-TiO2 composite coatings.The photocatalytic performance of Ni-Cu-P-nano-TiO2 composite coating under optimized preparation process is slightly worse than Ni-P-nano-TiO2 composite coating uder the same condition.Nickel ions and copper ions remove rate under the treatment of electroless solution can reach 99.1wt%and 98.8wt%respectively with the addition of complexzation deposition oxidant H2O2 600ml/L,complexzation deposition time, complexzation deposition temperature 40℃,deposition pH 12 and deposition time 4h.Deposition rate,micro-hardness and corrosion resistance of the coating which is prepared using recycling electroless solution are little different from the coating prepared using original elecrroless solution.However,various aspects performances of the coating prepared using waste solution are inferior to the two formers.Phosphorus remove rate can reach 99.97%with the addition of potassium chloride 80g/L,deposition pH 6.0 and Settlement time 4h.

Related Dissertations

  1. The Preparation and Research of Magnetically Separable TiO2 Photocatalyst Nanofibers,TB383.1
  2. The Study of Preparation and Photocatalytic Activity of TiO2 by Electrospinning,O614.411
  3. First- principles calculations of doped anatase titanium dioxide photocatalytic properties,O643.36
  4. Iron, lanthanum -doped nano TiO \u003csub\u003e 2 \u003c/ sub\u003e Preparation and photocatalytic properties,O614.411
  5. Research on Electrochemical Synthesis and Application of Conductive Polyaniline,O633.21
  6. The Photocatalytic Degradation of Nitro-phenol by B-N-Er-TiO2 and F-N-Er-TiO2 Nanocrystal under Visible Light,O643.32
  7. Modification of Iodine Doped Titanium Dioxide for the Photodegradation of 2-chlorophenol,O643.32
  8. Visible oxide catalyst with high activity and mechanism of Design and Synthesis,O643.36
  9. Composite fiber BiVO 4 Preparation and visible light photocatalytic properties of dyeing wastewater,X791
  10. Supported Co-doped TiO 2 photocatalyst Preparation and Research,O643.36
  11. Electroless Ni-Pon the Bulk Nanocrystalline Ingot Iron,TQ153.1
  12. Preparation of Highly Reactive Anatase Titanium Dioxide and Its Application in Photocatalytic Hydrogen Generation,TQ116.2
  13. Hydrogen Evolution Process of Water Electrolysis Assisted by TiO2 Nanotubes and TiO2/ZnO Nanorodes Assembled on Ni Substrate,TQ116.21
  14. Study on Corrosion Resistance and Condensation Property of Ni-P/Nano SiO2 Composite Coatings,TG174.4
  15. Preparation, Characterization and Performance of the Bio-coatings on the Surface of Pure Titanium Based on Micro Arc Oxidation,R318.08
  16. Pulse Nanocomposite Coatings Preparation and Properties,TQ153
  17. Magnesium alloys and corrosion resistance of phosphating process,TG174.4
  18. Vacuum casting AZ91 Magnesium Alloy Corrosion Resistance,TG146.22
  19. Carbon steel liquid plasma electrolytic carbonitriding research,TG156.8
  20. ZA35 alloy elements Zr on Microstructure and Properties,TG131
  21. Modified polypropylene microcellular foam morphology and Control Research,TQ328

CLC: > Industrial Technology > Chemical Industry > Electrochemical industries > Electroplating industry
© 2012 www.DissertationTopic.Net  Mobile