Study on Preparation and Application of Activated Carbon Which Used Coking Fly Ash

Author: LiuFeng
Tutor: OuYangShuGuang
School: Wuhan University of Science and Technology
Course: Chemical processes
Keywords: Coking fly ash activated carbons KOH activation steam activation activated carbon non-woven fabric
CLC: TQ424.1
Type: Master's thesis
Year: 2011
Downloads: 41
Quote: 2
Read: Download Dissertation

Abstract


The coking fly ash from coking process in Coking Plant had caused serious pollution on the environment. In this thesis, this study was based coke powder as raw material which was developed to activated carbons, which were of high practical values. And through further study activated carbon non-woven fabric was prepared by activated carbon, non-woven fabrics and adhesive. In this way, not only the coking fly ash was used as the secondary resources, but the environment was also protected.By orthogonal design, the optimal preparation processes that the coking fly ash was made of activated carbons were determined by the chemical activation with KOH and the physical activation with steam activation. And various factors which may affect the performance of activated carbon were systematically analyzed. The experiments show clearly the feasibility of preparation of activated carbon with the coking fly ash. The results demonstrates that a better activated carbon can be obtained from KOH activation, and the iodine capacity arrived at 874.3774 mg/g, which the iodine capacity 490.5215 mg/g by steam activation method. However, there are high cost and serious pollution in KOH activation. So the activated carbon by the steam activation method were selected for further study.In this study, the surface appearance and the chemical property of the activated carbons were analyzed by FTIR, SEM and XRD. The result shows that the number of oxygen groups and nitrogen groups increases, and so surface polarity increases in the activation process. After the activation, the product is mainly graphite-like crystallite. Further discussed that active carbon-nonwoven fabric was made with the material of the optimum process by the steam activation which manufacturing process was studied. And then its performance was evaluated. The result indicates when 20% of activated carbon concentration, 30% of adhesive concentration, the carbon capacity was 65.36%, the iodine capacity was 291.3541mg/g.These results suggest that: The coking fly ash can be made of activated carbons, which were of high practical values, and can be further made of molded sorbing material - non-woven fabrics. This does not only has opened up a new way for coking resource utilization, also have huge environmental, economic and social benefits.

Related Dissertations

  1. Preparation of the Crop Stalk-Based Shaped Activated Carbons and Fibreboard,X712
  2. The Preparation and Adsorption Properties of Carbon Nanotubes,TB383.1
  3. Raw material coke the adsorption simulation the flue gas SO_2/NO characteristics experimental study,TK6
  4. Study on Preparation of Activated Carbon from Deoiled Asphalt,TQ424.1
  5. Petroleum coke -based high specific surface area of activated carbon preparation,TQ424.1
  6. Morphology Control and Chemical Properties of Carbon Spheres by Hydrothermal Treatment and Its Activation,O613.71
  7. Of inorganic membranes precipitator cement plant kiln inlet flue gas desulfurization mechanism,X701.3
  8. Experimental Study of Discharge Corona Plasma Desulphurization,X701.3
  9. Preparation of activated carbon from lignite technology and theoretical research,TQ424.1
  10. Discharge of low-temperature plasma flue gas desulfurization reactor research,X701.3
  11. Research on Porous Carbon Electrode Materials for Supercapacitors,TM53
  12. Study on Lncreasing Desulfuration Efficiency of Flue Gas Using Pulsed Discharge Plasma,X701.3
  13. Preparation, Characterization of Ti-ZSM-5 and Its Catalytic Application for Olefins Selective Oxidation and Phenol Hydroxylation,O643.36
  14. Studies on Recovery of MTA Residues,TQ245.12
  15. Preparation and Activation of SiC-C Fiber,TQ343.6
  16. Study on Bio-Electrochemical Wastewater of ABS Treatment Technology and Its Mechanism,X703
  17. Preparation, Structure and Properties of Carbon-Encapsulated Iron Nanocrystals,TQ424.1
  18. Study on Utilization of Chinese Bayberry (Myrica Rubra Sieb.et Zucc.) Stone,S667.6
  19. Studies on Preparation and Properties of HSAAC from Waste Foam Polystyrene,TQ424.1
  20. The Study on the Preparation of the Activated Carbon from Incinerated Medical Wastes,X799.5
  21. Preparation of Based on the Phenolic Resin of Activated Carbon and Adsorption-Photopcatalytical Character of Supported TiO2,TQ424.19
  22. Synthesis and Characterization of Carbonate Intercalated Layered Double Hydroxides and Their Structure Recovery Properties,TQ424.2

CLC: > Industrial Technology > Chemical Industry > Reagents and the production of pure chemicals > Adsorbent > Activated carbon
© 2012 www.DissertationTopic.Net  Mobile