An Laser-Raman Spectroscopic Investigation of Adhesion Modes of Different Luting Cements Bonding to Carbon-fiber Post

Author: LiuNa
Tutor: FengYunZhi
School: Central South University
Course: Clinical Stomatology
Keywords: Carbon-fiber post Laser- Raman microspec- troscopy luting cement
CLC: R783
Type: Master's thesis
Year: 2008
Downloads: 100
Quote: 0
Read: Download Dissertation

Abstract


Objective:To detect the reasons that result in the diference of those adhesion modes of the three kinds of cements,Carbon-fiber Post and the cement-post interface,and further to evaluate the mechanism and the retention’s factors of the cement-post interface by means of laser Raman microscopy,this study supplies more theory about the post adhesion mechanism and reference for the clinical choice of posts and luting cementsMethods:One kind of prefabricated Carbon-fiber post was cemented respectively with three representative luting cements（zinc phosphate,glass ionomer and resin cements）in some extracted intact human maxillary anterior teeth were used canal dentin after endodontic treatment.The Laser-Raman spectroscopy measure of cement and Carbon -fiber post before and after luting together were acquired to observe the raman spectra’s change.Results:Carbon-fiber post’s relative bands occur at 810cm-1、980cm-1、1115cm-1、1205cm-1、1300cm-1、1450cm-1、1622cm-1、1730cm-1。The bands associated with ZPC and GIC may occur at 1500cm-1 and 1400cm-1respectively,while resin cement’s spectra occur at 845cm-1、1113cm-1、1199 cm-1、1221cm-1、1400cm-1、1450cm-1、1600-1、1745cm-1。There are no evident raman spectra change cross the ZPC/Carbon-fiber post interface and GIC/ Carbon-fiber post interface,while cross the resin/Carbon-fiber post interface significant vibrations can be seen。Conclusion:（1）Laser-Raman microspectroscopy is a useful analytical technique for studying the composition of bonding interface between post and luting cements。（2）The bonding strength of resin cement is better than ZPC and GIC.Resin cement may interact with the collagen and composition of the Carbon-fiber post to shape an effectiveness of micro-machinery catch。

Related Dissertations

  1. The Contrasting Research on the Fracture Resistance of Endodontically Treated Premolar Incorporating Different Fiber Posts,R783
  2. A Study of the Relationship between Ultrasound Images of Masicatory Muscle and Caraniofical Morphlogy of Young Males with Nomal Occlusion,R783.5
  3. Experiments Study of BIO-OSS on PRP Composite Repairing Bone Defect around Metal Nail of Pure Titanium,R783.6
  4. Root Resorption of Upper Centre Incisor with Compensation in Skeletal Class Ⅱ and Ⅲ Malocclusions,R783.5
  5. Several Low Flat Mandibular Alveolar Ridge to Improve Denture Retention Methods of Clinical Experience,R783.6
  6. The Dual-phase Treatment of Skeletal Class Ⅲ Malocclusion.,R783.5
  7. The Combined Treatment of Complex Adult Angleclass Ⅱ Division 1,R783.5
  8. To Observe the Effect of Different Dental Filling Technologies on the Microleakage under Confocal Laser Scanning Microscope,R783
  9. The Clinical Evaluation on Gingival Aesthetics of Immediate Implant and Immediate Prosthesis of Maxillary Anterior.,R783.6
  10. Comparison of Differences on Osseointegration among Immediate Implant, Delayed Implant after Bone Graft and Delayed Implant at Different Time,R783.6
  11. Evaluation of between the Occlusal Force and the Tissues Health Surrounding Implant of ITI Implants with Zirconia All-ceramic Crown,R783
  12. The Experimental Study on Effect of Different Low-power Laser Irradiation on Osseointegration of Dental Implants,R783.6
  13. The Influence on the Dimensional Stability and Elastic Deformation Caused by Two Types of Disinfectant Solution to Different Impression Material,R783
  14. Expression of BMP-1 in Periodontal Tissues during Orthodontic Tooth Movement in an Animal Experimental Study,R783.5
  15. Micro-implant Anchorage in Adults with Type of Open Bite Treatment,R783.5
  16. Orthodontic Treatment in Adults with Class Ⅲ Malocclusion Combined Low Angle by Extraction Four Premolars,R783.5
  17. Extraction Orthodontic Treatment of the Low Angle Deep Overbite Malocclusion,R783.5
  18. Influence of Various PH and the Treating Time on Mechanical Property and Surface Structure of Ni-ti Orthodontic Wire,R783.5
  19. A Clinical Study of Simultaneous Implant Placements after Sinus Floor Elevation in Maxillae with Less Than 5mm of Residual Bone Height,R783.6
  20. An Analysis of Bacterium Adhesions on the Surface of Restorative Materials of RPDs in Vitro,R783.6
  21. Different Bottom Structure of Dental Brackets Affect the Adhesiveness-Three Dimensional Finite-element Analysis,R783.5
  22. The Reference Indexes of Clinical Diagnosis Preparation with the Skeletal ClassⅡ Malocclusion in Prepubertal Growth Periods in Dalian,R783.5

CLC: > Medicine, health > Oral Sciences > Oral orthotics
© 2012 www.DissertationTopic.Net  Mobile