Research on Brazing of Hydrogenated TC4 Titanium Alloy

Author: YangXiuJuan
Tutor: FengJiCai
School: Harbin Institute of Technology
Course: Materials Processing Engineering
Keywords: hydrogenated TC4 titanium alloy brazing interface structure shear strength
CLC: TG454
Type: Master's thesis
Year: 2007
Downloads: 142
Quote: 1
Read: Download Dissertation

Abstract


In this paper, the mechanism and technology of brazing hydrogenated TC4 titanium alloys were been studied according to its characteristic using three diffenent filler metals.The microstructure of the joints was analyzed by means of SEM、EPMA、XRD. At the same time, shear strength test was examined for the joints.The optimum brazing parameters for different filler metals were given to acquire the sound joints.When bonded at low temperture, binary or trinary inmermetallics composed of Al、Si、Ti apperaed in the interface, and Al-12Si eutectic structure apperaed in the center of the interface with Al-12Si filler metal. With increasing the joinning temperture, intermetallic became more and thick. The shear strength of this joint was lower because of thin aluminium layer between the intermetallic layer and eutectic structure.The interface structure of the joint was pure alunimiun and TiAl3 intermetallic when brazed in 45 min at 700℃with aluminium filler metal. The thickness of intermetallic grew and the shear strength descended with increasing the holding time. Transversal crack and shrinkage cavity appeared in the joint when the holding time was more than 90 min, which caused the joint mechanical property deteriorated.The commercial titanium based brazing alloy was used to joint the substrate. Holding the joining time 10 min, two conversion zones were found when the joining temperture was low. Fusional filler metal diffused into the base metal and the substrates dissovlved into the fusional brazing metal. The joint was consituted ofα+βdual structure at 950℃. When hydrogen content was less than 0.3wt%, the shear strength first increased, than had a maxmium value at 950℃, and at last decreased slowly. When hydrogen content is more than 0.3wt%, the shear strength increased slowly all the time and only got 324MPa at 980℃.

Related Dissertations

  1. Investigation on Microstructure and Properties of Cadmium-Free Silver-Based Intermediate Temperature Filler Metals,TG425.2
  2. Technology of Filling Clearance and Optimizing the Bonds during Ultrasonic Brazing,TG454
  3. Research on Operational Life Span and Applications of Coated Electrode Resistance Welding for Galvanized Steel,TG453.9
  4. Measurement of Geotechnical Properties for Sewage Sludge at a Disposal Site and Evaluation of Its Influence on Slope Stability of MSW Landfill,X705
  5. 2205 hot workability and mechanical properties of stainless steel clad plate and Prediction,TG142.71
  6. Nanotube modified carbon fiber reinforced composite material structure of the capacitor,TB33
  7. Aluminized steel dissimilar metal stud melting brazing technology Test Method,TG454
  8. Asphalt permanent deformation prediction model and the number of mobile,U414
  9. Si 3 N 4 ceramic vacuum brazing process and strengthen joint research,TQ174.6
  10. A certain type of high-temperature adhesives applied research and life assessment,TJ760.3
  11. Evaluation Methods of Tack Coat and Stress Absorbing Interlayer,U411
  12. Active Bridge Section Consolidation Method Increases,U445.72
  13. Development of High-performance Modified Asphalt Emulision for Ultra-thin Wearing Course Interlayer Bonding Materials,U414
  14. The Effect of Three Dentine Desensitizers on Bond Strength of Luting Agents,R783
  15. Microstructures and Properties of Brazing Joint of Al2O3 Ceramic and Q235 Steel,TG407
  16. Reasearch on Welding Process and Mechanism of 9Ni Steel for Large LNG Storage Tank,TG457.11
  17. Study Application of Welding Technique of Oxygen Lance Nozzle,TG457
  18. Research on the Interface Structure and the Infiltration-mechanism of SiC_p/AZ91D by Vacuum,TB331
  19. Study on Brazing Process and Mechanism of Si3N4 Ceramic Joint Brazed by Au-Ni-V-Pd High-temperature Filler Alloy,TQ174.6
  20. The Performance Analysis for Strengthening Concrete Column with Carbon Fiber Reinforced Plastic,TU375
  21. Experimental Study on the Seismic Behavior of the Walls Made of Sintered Shale Porous Bricks,TU364

CLC: > Industrial Technology > Metallurgy and Metal Craft > Welding, metal cutting and metal bonding > Welding process > Brazing
© 2012 www.DissertationTopic.Net  Mobile