Studies on Methacrylic Acid Salt Modified Natural Rubber

Author: ZhuZuoSuo
Tutor: TanHaiSheng
School: Hainan University
Course: Materials Science
Keywords: NR methacrylic acid salt CaCO3 mechanical properties strengthen
CLC: TQ330.1
Type: Master's thesis
Year: 2010
Downloads: 15
Quote: 0
Read: Download Dissertation

Abstract


Choose the conditions of vulcanization system as follows:2phrDCP,2phrS, 5phr ZnO. The NR modified by four kinds of methacrylic acid salt including ZDMA, MDMA, NaMA and KMA were prepared, the mechanical properties of modified NR vulcanizates were investigated. The results showed that with the increasing of ZDMA and MDMA, the swelling degree of NR vulcanizates were obviously decreased which means that the crosslinking degree of NR vulcanizates were obviously increased.In the presence of both sulfur and dicumyl peroxide (S/DCP) as a curing agent, the research do the single factor experiment at first. Including the dosage of DCP, S and zinc oxide(ZnO), they have effect on the vulcanizing properties of modified NR and the vulcanized properties of modified NR. The optimal technical conditions of vulcanized NR were as follows:the DCP contents was 1.5～2.5phr, the S contents was 2～3phr, the ZnO contents was 5～7 phr.The mechanical properties of vulcanized NR modified by ZDMA were obviously increased. When the ZDMA contents was 10phr, the vulcanized NR got the best mechanical properties. The mechanical properties of vulcanized NR modified by MDMA were obviously increased. When the MDMA contents was 10～15phr, the vulcanized NR got the best mechanical properties. Vulcanized NR modified by MDMA, NaMA and KMA could keep very good mechanical properties after the hot-air ageing(100℃×24h), which vulcanized NR modified by ZDMA couldn’tthe NR modified by ZDMA with calcium carbonate (ZDMA/CaCO3) and the NR modified by CaCO3 were prepared, the mechanical properties of modified NR vulcanizates were investigated. The results showed that the NR vulcanizates modified by ZDMA/CaCO3 could improve properties great and got higher strength, higher modulus than NR vulcanizates modified by CaCO3. The best contents of ZDMA/CaCO3 was 10/10, that the tensile strength increased 29.52% and tear strength increased 36.70%. That showed that ZDMA can improve the combination of CaCO3 with NR and the dispersion of CaCO3 in NR.

Related Dissertations

  1. Reactive Hot-Pressing and Mechanical Properties of （ZrB2-ZrO2）/BN Composites,TB332
  2. Research on Welding Characteristics of CO2 Laser-GMA Hybrid Welding for Ultra-Low Carbon Bainitic Steel,TG456.7
  3. Microstructure and Mechanical Properties of Mg-Zn-Y-Zr Alloys,TG146.22
  4. Study on the Recycling of Post-Consumer Polyester Textiles,X791
  5. Fabricationand Properties of SiC-AlN Multiphase Ceramics Prepared by Gelcasting,TQ174.62
  6. Synthesis of Polysulfones and Modification for Epoxy Adhesives,TQ433.437
  7. Bio-inspired Mineralization Process of TiO2 and CaCO3 in Agarose Gel Medium,O611.3
  8. Structure and Characterization of Room Temperature Self-crosslinked Acrylonitrile-butadiene-styrene,TQ325.2
  9. The Research on Extrusion Parameters Through the Plate Billet of Magnesium Alloy,TG379
  10. Modification of Talc Powder and Its Reinforcing and Toughening on Recycled Polypropylene,TQ325.14
  11. Effect of Adding ZrO 2 Nanopowder on Microstructure and Mechanical Properties of Carbon Steel,TB383.1
  12. Preparation of Surface-functionalized Graphene and Its Influence on the Mechanical Properties of Nanocomposite Materials,TB332
  13. Study on Kinetics and Morphology of Calcium Carbonate Precipitation Catalyzed by Bacterial Carbonic Anhydrase,O643.32
  14. Preperation of Low Friction and Wear Resistant High-Purity Alumina Ceramic,TQ174.1
  15. The Study of Forming Process and Properties of PTT/PET Skin-Core Composite Monofilament with Large Diameter,TQ340.64
  16. Research on Structure and Mechanical Property of Hook and Loop Fastener,TE931.2
  17. Rolled Mg-Zn-Ce-Zr (Mn) alloy microstructure and mechanical properties of,TG339
  18. Simulated lunar ambient temperature magnesium alloy microstructure and mechanical properties of,TG146.22
  19. Shanghai Comprehensive Test of mechanical properties of clay and constitutive modeling,TU411.3
  20. Triple-Wire High Speed GMAW Butt Joint Welding Process of Marine E Grade Steel,TG457.11
  21. Web service attack analysis and Security Research,TP393.08

CLC: > Industrial Technology > Chemical Industry > Rubber Industry > General issues > Basic theory
© 2012 www.DissertationTopic.Net  Mobile