Studies on the Preparation of Raney Ni Catalysts Modified with Fe and/or Mo and Their Hydrogenation Performance

Author: LiuWei
Tutor: LiXiaoNian;ZhangQunFeng
School: Zhejiang University of Technology
Course: Industrial Catalysis
Keywords: Raney-Ni catalysts modification glucose hydrogenation loss
CLC: O643.36
Type: Master's thesis
Year: 2010
Downloads: 55
Quote: 0
Read: Download Dissertation

Abstract


Raney Ni was one of the most widely used catalysts in industry for the characteristic of low cost and easy to prepare, which still had the disadvantage of poor reactivty and selectivity, especially poor stability. It was an effective way to improve the performance of Raney Ni catalysts by adding other metals to modify Raney-Ni. In the present thesis, Raney Ni catalysts modified by Fe and/or Mo were prepared. Glucose hydrogenation was used as a probe reaction, meanwhile the loss of metals used to modify Raney Ni was investigated systematically. The main content as follows.(1) Reaction conditions of glucose hydrogenation were optimized as follows: glucose amount used 100g, water amount used 100 ml, pressure 5 MPa, temperature 140℃, catalyst amount used 4 g(wet weight).(2) Raney Ni modified by Fe showed higher activity than Raney Ni in the reaction with new catalysts. However, In the probe reaction with Raney Ni modified by Fe, the loss of Fe was numerous and the loss of Al was more serious than that in the reaction with Raney Ni, which led to the decrease of surface area and activity for Raney Ni modified by Fe. There was no loss of Mo in the probe reaction with Raney Ni modified by Mo, less loss of Al than in the probe reaction with Raney Ni, and the activity and stability of Raney Ni modified by Mo was fairly good in the probe reaction. The decrease of activity was mainly due to the loss of Al and the growth of particle size .(3) Raney-Ni catalysts modified by Fe and Mo together dissolved in the same conditions had the characteristic of smaller particle size and less loss of Al in the reaction process, which were attributed to higher activity and stablity of the catalysts.(4) Phase and valence of Fe and Mo in the alloy and modified Raney Ni catalysts was investigated. The loss of the metals used to modify the Raney Ni catalysts in the dissolving process of alloy and the probe reaction process were systematically investigated according to the phase and valence in the alloy and Raney Ni catalysts modified by Mo or Fe, respectively.

Related Dissertations

  1. Optimizition of Compositions and Processing Parameters and Wear Properties of Cemented Carbides YG11R Modified by Nanosized Rare Earth,TG135.5
  2. Investigation of Turbine S2 Stream Surface Direct Problem Aerodynamic Optimization Design,V235.11
  3. Key Technologies of Dam-break Life Loss Risk Assessment Research,TV122.4
  4. Research of Irreversible Loss in Flow and Mexed Prosess,TK12
  5. Study on the Influence of Drive Strategies on the Loss in AC Permanent Magnet Motor,TM351
  6. Packet Loss Recovering Technology for Speech Transmission over Network,TN912.3
  7. Design and Processing of Hybrid Modulated HF Radar Waveform,TN958.93
  8. Research of High Speed Image Pre-processing System Based on FPGA,TP391.41
  9. Lijiang River,RS and GIS - based Soil Erosion Research,S157
  10. First- principles calculations of doped anatase titanium dioxide photocatalytic properties,O643.36
  11. Synthesis of Polysulfones and Modification for Epoxy Adhesives,TQ433.437
  12. Synthesis and Performance Study of Bisphenol AP-based Polybenzoxazines,TQ320.1
  13. Study on the Preparation of Polyethylene Naphthalate and Its Performance,TQ316.33
  14. Study of the Fabrics’ Thermal-Wet Comfort in Hingh Humidity Environment,TS101.923
  15. Research on the Laws of Nitrogen and Phosphorus Loss and Control Scheme in Eryuan Rural,X712
  16. Researcg of Local Government Credit Construction,D630.1
  17. Hydrophilic structure of different types of surface -modified polyurethane material and coagulation 12 factor nine peptide fragments,and fibrinogen P1 fragment of computer simulation of the interaction,O631.3
  18. The Effects of Exposure to Bisphenol-a between Adolescence and Early Adulthood on Behaviors in Mice and Its Molecular Mechanism,R965
  19. The Impact of Betrayal on Risky Decision Making,B84
  20. Self-discovery , self-realization and self- Lost,I561.074
  21. Acute low-tone sensorineural hearing loss clinical observation,R764

CLC: > Mathematical sciences and chemical > Chemistry > Physical Chemistry ( theoretical chemistry ),chemical physics > Chemical kinetics,catalysis > Catalytic > Catalyst
© 2012 www.DissertationTopic.Net  Mobile