Study on the Composite Volatile Corrosion Inhibitor (VCI) for Meatl Relics

Author: DingYanMei
Tutor: XuChunChun
School: Beijing University of Chemical Technology
Course: Materials Physics and Chemistry
Keywords: Iron relics Bronze artifacts Vapor phase corrosion inhibitor
CLC: TG174.42
Type: Master's thesis
Year: 2005
Downloads: 280
Quote: 0
Read: Download Dissertation

Abstract


In this study, through the use of gas screening method , weight loss and closed space volatile Reduction Act experiments screening single - component vapor phase corrosion inhibitor and complex experiments , respectively the prepared iron relics and bronze artifacts composite vapor phase corrosion inhibitor , iron relics composite vapor phase corrosion inhibitor I by organic amine A and the Wuluo off products to mass ratio of 1:1 , the inhibition rate was 96.5% , bronze artifacts composite vapor phase corrosion inhibitor II by BTA and phenolic W made to mass ratio of 1:1 , the inhibition rate was 94.5 % . Using scanning electron microscopy , Raman microscopy , atomic absorption spectroscopy , contact angle measurement , electrochemical polarization curves of these two composite vapor phase corrosion inhibitor performance test , compared with the blank sample , experimental the results show that both the corrosion resistance of the composite vapor phase corrosion inhibitor and water repellent performance . Composite vapor phase corrosion inhibitor I is a vapor phase corrosion inhibitor for inhibiting the anodic process , using X -ray photoelectron spectroscopy and X-ray diffraction study of of composite vapor phase corrosion inhibitor I , the results showed that the inhibition mechanism of the surface of the iron relics composite vapor inhibitor ⅰ nitrogen transition the unstable iron relics rust stable rust layer , can promote corrosion of the metal can be effectively suppressed . Observed by scanning electron microscopy and laser Raman technique to the the composite vapor phase corrosion inhibitor II copper surface generated branched self-assembly of Corrosion and film heritage has played a very good protection . The composite vapor phase corrosion inhibitor I applied to the wrapping paper , VCI paper prepared good corrosion can be applied directly in the packaging of heritage and transportation process .

Related Dissertations

  1. Research on Electrochemical Properties and Storage Life of Zinc Electrode in Reserve Zinc-Silver Battery,TM911.14
  2. Synthesize and Study of a Novel Vapor Phase Inhibitor,TG174.42
  3. Study on the Volatile Corrosion Inhibitor (VCI) for Metal Rust Proof Packaging,TG174.42
  4. Study of Inhibitors of Aluminum Anode in NaCl Solution,TG174.42
  5. Study on the Corrosion-Preventing Efficiency and Synergistic Action of PhAMT,TG174.42
  6. Synthesis and Inhibition Performance of Novel Dissymmetric Bisquaternary Ammonium Salt,TG174.42
  7. The Synthesize of a High Temperature Corrosion Inhibitor and Its Capability Research in the Acid Conditions,TG174.42
  8. Study on the Volatile Corrosion Inhibitor (VCI) for Metal Rust Proof Packaging,TG174.42
  9. Switching Imidazoline Corrosion Inhibitor and Performance,TG174.42
  10. Study on the Inhibiton Effect of Self-assembled Films for Copper Corrosion in 0.5 M HCl Solutions,TG174.42
  11. Studies on Corrosion Inhibition for Zinc in Nitric Acid Solution,TG174.42
  12. Synthesis and Application of linear alkenyl imidazoline,TG174.42
  13. Synthesis and Application of Aqueous Corrosion Inhibitors,TG174.42
  14. Synthesis of Cottonseed-oil Derivatives Corrosion Inhibitors and Study on Inhibition Properties,TG174.42
  15. Corrosion and Anti-Corrosion Techniques for Air Injection EOR Process,TG174.42
  16. Synthesis and Corrosion and Scaling Inhibition of Polyacrylic Acid,TG174.42
  17. Synthesize and Study of a Novel Vapor Phase Inhibitor,TG174.42
  18. Hydrochloric acid medium zinc corrosion inhibitor developed,TG174.42
  19. Research on the Optimization and Mechanism of Copper Electrochemical Mechanical Planarization,TG174.42
  20. Electrochemical corrosion inhibitor for carbon steel corrosion resistance role in the acidic medium,TG174.42

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology > Metal preservatives,corrosion inhibitors
© 2012 www.DissertationTopic.Net  Mobile