Synthesis of Mesoporous NaA Zeolite by Multiwall Carbon Nanotubes Templating

Author: YuanJingBin
Tutor: LiFuXiang
School: Taiyuan University of Technology
Course: Chemical processes
Keywords: multiwall carbon nanotube solid template mesoporous NaAzeolite silane coupling agent
CLC: O643.36
Type: Master's thesis
Year: 2012
Downloads: 60
Quote: 0
Read: Download Dissertation

Abstract


Zeolites with uniform microporous and pore size of molecular size are a class of sorbent or film-like material. Its diameter ranges from4A to12A, such as Y-type, ZSM-5zeolite. In petrochemical, fine chemicals and biochemical engineering areas, there are often some large molecules with their dynamics diameters larger than the pore size of zeolites, which make the reaction can’t proceed. Mesoporous zeolites improve the situation and expand the field of application of zeolites through changing the pore system to allow more large molecular to access the inner of zeolite.In this paper, the multiwall carbon nanotubes, which involve MWNTs-none, MWNTs-COOH and MWNTs-OH, was used as template agents to synthesize mesoporous NaA zeolite by hydrothermal method. The silane coupling agent was brought in to treat the MWNTs-OH, in order to improve the BET surface area. The conclusions are as follows:1. The crystallinity of mesoporous NaA zeolite is not varied with the different MWNTs-none amount. What’more, the mixing temperature and mixing time of MWNTs-none and Na2Si03does not affect the degree of crystallinity of the samples. The maximum BET surface area of sample is about10m2/g, which is larger than that of microporous NaA zeolite (about3.4m2/g). And, the pore size distribution ranges from5～50nm.2. The crystallinity of mesoporous NaA zeolite is not changed with the different MWNTs-COOH amount. What’more, the mixing temperature and mixing time of MWNTs-COOH and Na2Si03does not affect the degree of crystallinity of the samples. The maximum BET surface area of sample is about16.8m2/g, which is larger than that of samples by MWNTs-none templating. And, the pore size distribution ranging from10-30nm is more narrow than samples by MWNTs-none templating.3. The crystallinity of mesoporous NaA zeolite is not varied with the different MWNTs-OH amount. What’more, the mixing temperature and mixing time of MWNTs-OH and Na2Si03does not affect the degree of crystallinity of the samples. The maximum BET surface area of sample is about17.8m2/g, which is close to that of samples by MWNTs-COOH templating. And, the pore size distribution ranging from10-30nm is similar with that of samples by MWNTs-COOH templating.4. By contrast, it can be seen that the sample by MWNTs-OH templating has the largest BET surface area. It indicates the functionalized MWNTs can increase the sample BET surface area. The samples by MWNTs-COOH and MWNTs-OH templating have close BET surface areas, which suggests that the two have similar ability to make pores in zeolite. 5. The crystallinity is not affected for the amount of MWNTs-OH treated with KH-560and the mixing temperature or mixing time of MWNTs-OH and Na2SiO3. However, the sample BET surface area will be cut down with the increase of concentration of KH-560aqueous solution, and the maximal BET surface area is about13.7m2/g. That is maybe the alkoxy activity of KH-560is weaker than the surface hydroxyl of MWNTs-OH. So the more covered by KH-560on the surface, the weaker of the activity of MWNTs-OH. Finally, the BET surface area is deduced.6. The KH-660and the mixing temperature and mixing time of KH-660, MWNTs-OH and Na2SiO3almost don’t affect the degree of crystallinity of the mesoporous NaA zeolite zeolite. The KH-660does not affect the BET surface area, it is maybe the activity of KH-660is similar with that of MWNTs-OH, which make them have similar ability to form mesoporous.7. The crystallinity of mesoporous NaA zolite with polymer of KH-560and KH-660bridged MWNTs-OH as templates does not changed with conversion in mixing conditions. The maximum BET surface area of samples is about24.3m2/g, which is larger than that by KH-560or KH-660treating. That is because the KH-560and KH-660have reacted to enhance the binding force, so the MWNTs-OH can be encapsulated in zeolite crystal more.

Related Dissertations

  1. Nano LaFeO 3 Controllable Synthesis and TiO 2 bridged construct composite photocatalyst,O643.36
  2. Effect of Different Resin Cements and Silane Coupling Agents on Bond Strength of Glass Fiber Post to Root Dentin,R783
  3. Preparation and Surface Modification of Silica Nanoparticle,TB383.1
  4. Preparation and Performance Research for Carbon Fiber Reinforced Polyethylene Terephthalate Composite,TB332
  5. Research on Modification of Fly Ash Fibers and Enhancement of Tensile Strength of Paper Made from Fly Ash Fibers,TS71
  6. Study on the Synthesis and Properties of Organic Silicone Modified Waterborne Polyurethane,TQ323.8
  7. Research and Development on the Coated Fabric of Polyphenylene Sulfide Based on the Fabrics of Firefighters’ Chemical Protective Clothing,TS195.5
  8. AZ31 magnesium alloy surface corrosion Coating and Corrosion Resistance,TG174.4
  9. Preparation and Characterization of Organic-Inorganic Hybrid Coatings,TB304
  10. The Surface Modification of Aramid Fiber and the Compound Performance between Aramid and Rubber,TQ330.1
  11. Preparation and Studying of RTV-2 Silicone Adhensive for Aircraft,TQ433
  12. Properties of Solid Polymer Electrolytes Composite Modified by Sca/Inorganic Particles,O631.3
  13. The Study of Compatibility on Polypropylene/Intumescent Flame Retardant Composites,TQ325.14
  14. Preparation and Characterization of PDCPD/Nano-SiO2 Composite,TB332
  15. Effects of Multiwall Carbon Nanotube and Multiwall Carbon Nano-onion on the Protein Expression Profiles of Human Skin Fibroblasts,TB383.1
  16. Synthesis of Polyaniline/nano-Manganese Dioxide Composite and Applications in Supercapacitors,TM53
  17. Effect of Different Silanization on the Shear Bond Strength of Fiber Posts in Vitro,R783
  18. Experimental Research of New Anticorrosion Coating for Power Station Chimney after Desulphurization,X701.3
  19. Preparation and Properties Research of Flax/PLA Composites,TB33
  20. Synthesis Study on the Silance Coupling Agents with High Thermostability and Research on the Pretreatment of Copper Foil with Silane Coupling Agents,TB383.1
  21. The Surface Modification of Silica and Synthesis of MQ Resin,TB383.1

CLC: > Mathematical sciences and chemical > Chemistry > Physical Chemistry ( theoretical chemistry ),chemical physics > Chemical kinetics,catalysis > Catalytic > Catalyst
© 2012 www.DissertationTopic.Net  Mobile