Study on Direct-current Electro-deposition Ni-P-α-Al2O3Nano-composite Coatings

Author: ZhuYuQing
Tutor: ZhuFuLiang
School: Lanzhou University of Technology
Course: Non-ferrous metallurgy
Keywords: direct-current electro-deposition Ni-P-α-Al2O3nano-compositecoatings heat treatment micro-hardness
CLC: TQ153
Type: Master's thesis
Year: 2012
Downloads: 47
Quote: 0
Read: Download Dissertation

Abstract


In this paper，Ni-P-α-Al2O3nano-composite coatings were electrodeposited byadd nano-α-Al2O3particles to Ni-P plating solution, the impact of certain factors onthe co-electrodepositing process are discussed， and the properties ofnano-composites as well as their applications are described. The suspending stabilityof dispersive system was investigated through sedimentation experiment. Themicro-hardness of the composite coatings was analyzed by HX-1000TM digitalmicro-hardness tester. The corrosion resistance were measured by the immersion testand the anodic polarization curves.Nano-α-Al2O3particles are easily aggregative in the production and storedprocedure due to its small size, large surface area and high surface free energy. Afterthe surface treatment of nano-α-Al2O3particles, the influences of ultrasonicdispersion time and the concentration （CTAB, LAS, PEG6000） of the surfactant onthe dispersion properties of the nano-α-Al2O3particles in aqueous solution weresystematic study. The results show that these anion, cation and non-ion surfactantscan effectively inhibit the aggregative of nano-α-Al2O3particles. The optimumdispersion parameters are that the concentration of LAS and ultrasonic dispersiontime are0.8g/L and35min respectively. The lowest sedimentation volume is5.4ml,and the highest micro-hardness of composite coatings up to1207HV.The effects of the changes in the micro-structure of electrodepositedNi-P-α-Al2O3nano-composite coatings before and after heat-treatment onmicro-hardness and corrosion resistance were investigated to discover thecorrelation between the microstructure and performance of the coating. The resultsindicated that the as-deposited Ni-P-α-Al2O3nano-composite coatings had theamorphous structure, and it starts to crystallize when being held at200℃, producemetastable phases Ni(120P5and Ni5P2. When the heat treatment at350℃, themetastable phases were transformed to stable phases Ni3P and Ni, and grain growth.Only Ni3P and Ni were formed after heat treatment at400℃. After heat treatment,composite coatings had lager hardness than the amorphous coatings, the coatingswhich were heat treatment at300℃partially nano-crystalline of crystallizedprecipitation dispersed in the amorphous phase, and its had the maximum hardness968HV. When the heat treatment temperature exceeds300℃， the corrosionresistance of composite coatings rapidly reduce. The optimal process of Ni-P-α-Al2O3nano-composite electrodeposition wasdetermined by orthogonal experiments in which micro-hardness of compositecoatings was used as evaluation criteria. The optimal process conditions were asfollows: temperature was35℃, pH value was3.5, current density was4A/dm2,agitation rate was320r/min, nano-powder content in plating solution was16g/L,plating time was70min. Micro-hardness value obtained under the optimumconditions can up to1332HV.

Related Dissertations

  1. Study on Technics & Performance of Nano Electroless Composite Plating on 20~# Steel,TQ153
  2. Study on Key Technology and Its Physiological Basis of Virus Elimination and Rapid Propagation of Phalaenopsis,S682.31
  3. The Structure and Properties of Electronspun PSU Fibrous Membranes,TQ340.1
  4. The Effect of Tungsten on Microstructures and Properties of Wear Resistant Overlays Prepared by Plasma Cladding,TG174.4
  5. Study on the Subsurface Crack of Supporting Roller Made of Austempered Ductile Iron,TG156.3
  6. Thermophysics Research on Postharvest Spherical Fruit during Heat Treatment,S66
  7. Research on the Microstructures and Properties of Semi-solid ZL201 Alloy Die Forging,TG146.21
  8. The Research on Rolling and Heat Treatment Technology of AZ31 Magnesium Alloy Thin Sheet,TG166.4
  9. Effect of Heat Treatment and Alloy Composition on Microstructure and Properties of Wear-resistant Casting Steel,TG142.4
  10. Development of Cr-Mo Alloy Steels for Liner Applications and Assessment of Its Wear Resistance,TG335.5
  11. Research on Composite Hard Anodic Oxidation of Aluminum Alloys and Mechanism,TG174.44
  12. Effect of Ag and Er on Microstructures and Properties of Al-Mg-Si-Cu Alloys,TG146.21
  13. Study on the Properties of PLA Filament and Its Mixed Fabrics,TS101.923
  14. Influence of Ni-P Electroless Platting on 6063 Aluminum Alloy and Research on Modification of YG8 Hard Alloy after High Current Pulsed Electron Beam Irradiation,TQ153.1
  15. Preparation and Luminescence Properties of Sulfophosphate Glasses,TQ171.1
  16. Study on Extrusion and Heat Treatments of AJ and AE Series Cast Magnesium Alloys,TG166.4
  17. The Design and Implementation of Control System for Wire-steel Heat Treatment Direct-fired Furnace,TP273
  18. Study on Process Method and Parameter Optimization of the Remained-heat Treatment of Marine Heavy Forgings,TG316
  19. Study Continuous Glass Fiber Reinforced Polypropylene by Two-step Pultrusion,TQ327.11
  20. Study on the Preparation and Thermostability for Mechanical Properties Microstructure of Low Density MA/ ODS Nickel-Based Superalloy,TG132.32
  21. Research on Microstructures and Properties of Modified A356 Aluminum Alloy in Lost Foam Casting Process,TG249.5

CLC: > Industrial Technology > Chemical Industry > Electrochemical industries > Electroplating industry
© 2012 www.DissertationTopic.Net  Mobile