The Study of Corrosion Behavior of Typical Metals by Electric Speckle Pattern Interferometry

Author: YeMingYang
Tutor: DuZuo
School: Nanchang University of Aeronautics and
Course: Materials Physics and Chemistry
Keywords: Carbon steel Stainless steel Chronoamperometry EIS ESPI Cyclicvoltammetry
CLC: TG172
Type: Master's thesis
Year: 2011
Downloads: 32
Quote: 0
Read: Download Dissertation

Abstract


The technique based on Electric Speckle Pattern Interferometry （ESPI）,Chronoamperometry, Electrochemical Impedance Spectra （EIS） and linear sweepvoltammetry was applied to study the corrosion behavior of carbon steel inNaHCO3-NaCl-CaCl2solution. An ESPI based technique for in situ and accurateobservation of pitting susceptibility of304stainless steel in NaCl solutions is reportedin this paper. The main results are as following:The influence of carbon steel Corrosion behavior under the Ca2+ion of differentconcentrations was investigate by analyzing the average corrosion rate ofchronoamperometry, statistically analyzing the appearance of etch pits and analyzingthe Charge transfer resistanc of EIS. The results indicated that, the Ca2+ion on0640mg/L makes a inhibition effect of carbon steel corrosion, When Ca2+ionconcentration was640mg/L, Chronoamperometry measured average corrosion rate for3.253E-4A/cm2, electrochemical impedance measured the charge transfer resistancefor29.480kΩ·cm2, The degree of pit corrosion intensity is2.791, the corrosionbehavior of carbon steel is the slightest.Through analysis the Pitting corrosion inductions time to help identifyspecimens’ pitting resistant. When the solution without Ca2+ions, the induction time is88s and the pitting corrosion resistant was the worst. When Ca2+ions concentration is0640mg/L,the pitting induction time increases with the Ca2+ions concentration andthe pitting risistant increase gradually. When Ca2+ions concentration is2560mg/L,the pitting induction time is93s less than640mg/L which pitting induction time is104s. Explain that carbon steel pitting resistance is reduced, but stillis greater thansolution with no Ca2+ions.The pitting corrosion sensitivity of304stainless steel in NaCl solution underdifferent Cl-concentration、temperature and pH was studied by Eb′which wasmeasured by ESPI combining dynamic potential linear scanning and EIS. Researchshows that, Time constant τ as smaller as immersion time, Passivation membraneporosity greaten or passivation membrane thickness thin. the pitting corrosionsensitivity of304stainless steel is bigger with the higher Cl-concentration andtemperature, smaller with the higher pH. And when the Cl-concentration is0.01%1%,Eb′quickly move negative with the increase of concentration Cl-, Eb′moving negative slowing when the Cl-concentration is higher, so the influence had smaller with theincrease Cl-concentrations. when pH is2<pH<7, Pitting potential is moving range ofgentle, pitting sensitivity have a little change, when pH is1<pH<2、9<pH<14, pittingpotential is moving big movments, that is show that the influence of pitting sensitivityare mainly concentrated in this region.

Related Dissertations

  1. Study of Inhibitors of Aluminum Anode in NaCl Solution,TG174.42
  2. Environmental Effects of Poisonous and Harmful Substances in the Typical Industrial Solid Wastes,X705
  3. Biocompatibility Modification of Solid Materials Via Living Free Radical Polymerization,O631.3
  4. Study on the Microstructures and Properties of N-alloyed Low Carbon Martensitic Stainless Steel,TG142.71
  5. Effects of Environments on Fracture Toughness and Fracture Behavior of 304 Stainless Steel,TG142.71
  6. Development the High-Carbon Wire for Cutting Hard-Brittle Material and Research on the Organization and Performance of the Wire,TG356.46
  7. Study on Chemical Coloring and Sealing Processing of Stainless Steel,TG177
  8. Preparation of the Composite Coatings on the Carbon Steel Surface and Their Anticorrosion Properties in Seawater,TG174.4
  9. Investigations on Cyclic Deformation and Damage Behavior of AL6XN Super-Austenitic Stainless Steels,TG142.71
  10. Research on Preparation of Dopamine Composite Films on Stainlees Steel and Corrosion Resistance,TG174.44
  11. Research of the Design and Manufacture of REAC Lined Tube for Resisting Flow Induced Corrosion,TE932
  12. Study on Corrosion Behavior of Carbon Steel in Aqueous Solution of REAC System,TE986
  13. Microstructure and Mechanical Property of Clad Plate of Stainless Steel by Vacuum Composite Rolling,TG142.1
  14. Stainless Steel Bright Annealing Furnace with Waste Heat Recovery Energy-saving Technology Research,TG155.1
  15. Preparation and Characterization of Stainless Steel Hollow Fiber Support Membrane,TB383.2
  16. Prepaation of Hybrid Membrane on Carbon Steel and Anti-corrosion Properties Research,TG174.4
  17. Stainless Steel Smelting Refractories of Calcium with Magnesium,TQ175.7
  18. The Effect of Pre-strain Style on Bake-hardening for Ultra-low Carbon Steel,TG142.31
  19. Several Ladles Pouring Together for Large Super-low-carbon Stainless Steel Casting,TG260
  20. Failure Analysis on Superheat Section Connecting Pipe Flange of Ethylene Cracking Furnace,TQ221.211
  21. Study on the Dry Cutting Performance of Austenitic Stainless Steel 0Cr18Ni9,TG142.71

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Various types of metal corrosion
© 2012 www.DissertationTopic.Net  Mobile