Development of Cr-Mo Alloy Steels for Liner Applications and Assessment of Its Wear Resistance

Author: DingZhiMing
Tutor: LiuJing
School: Wuhan University of Science and Technology
Course: Materials Science
Keywords: ball mill liner chrome molybdenum alloy steels heat treatment process wear resistance
CLC: TG335.5
Type: Master's thesis
Year: 2011
Downloads: 102
Quote: 0
Read: Download Dissertation

Abstract


Mill was used in new building materials, refractory materials, chemical fertilizer, black and non-ferrous metal processing, cement, Portland products, as well as glass ceramics and other production industry widely. Liner was the primary wear parts of ball mill. Its consumption was tremendous and growing. the huge consumption was concerned very much. Making use of the ball mill liner with good wear resistance and long life was significant.In this paper, AΦ5.03×6.4m ball mill liner service life was 4,000 hours in Wisco group iron ore plant. Grinding efficiency was low and replacement liner frequently. Wear-resistant Cr-Mo alloy steels liner was developed. Composition, shape and smelting process of Cr-Mo alloy steels liner was designed. The relationship of organization and hardness, toughness , wear resistance was studied after quenching and tempering in different temperature. The reasonable treatment process was put forward. It was confirmed that the wear resistance of liner was better than the previous liner. Through the laboratory wear test and six-month industrial service test, the wear resistance of Cr-Mo alloy steels liner board and the iron ore previous liner board was compared, the two kinds of liner material wear-resisting mechanism were analyzed.In this paper, the composition of Cr-Mo alloy steels was 0.48 0.55% C, 2.0 2.5% Cr, 0.6 0.8% Mo, 0.8 1.2% Mn, 0.9 1.2% Si, 0.1 0.2% V, 0.15 0.2% RE. The Cr-Mo alloy steels had well hardenability, which thickness could reach 150mm. Its linear expansion coefficient is lower, which is 13.53×10-6 / K. Austenitizing temperature Ac3 is 854℃. the best liner material quenching heat treatment process was 920℃quench +350℃temper. After 920℃quenching + 350℃tempering, the microstructure of test materials was acicular martensite + carbide + dispersed residual austenite, which carbide were mostly spherical or short pole shape. Its strength was high and toughness was good.The alloy steels liner board in the study had been used DaYe iron oreΦ5.03 x 6.4 m of ball mill. Cr-Mo alloy steels had better service effect than the previous liner steels. Life expectancy of Cr-Mo alloy steels liner would reach 7000 hours. Martensitic of Cr-Mo alloy steels was thin. It mutually thrust. Its dislocation density was high, that was positive effect to wear resistance. The previous liner steels had main base structure of the bulky martensite. It flaked easily and was brittle. Mo, V carbon were formed in Cr-Mo alloy steels, that increased the strength of steels and toughness and improved abrasion resistance. Points or globular carbide dispersion distribution in internal crystal, that strengthened the matrix, enhance the wear resistance. The long strips of carbide was main in the previous liner steels, that was dissolved in the more grain boundaries separating. So its toughness was low.

Related Dissertations

  1. Research and Development of Wear Resistance for Physically Disabled Men Jackets,TS941.2
  2. Study on the Relationship between Different Formulations and Properties of Three-dimensional Non-woven Liner Material,TS176
  3. Study on the Molding Process of Three-dimensional Non-woven Bra Cup,TS941.4
  4. Preparation and Characterization of Luminescent Material SrWO4: Eu3+,TB383.1
  5. A Comparison of the Mid-term Results of Harris-Galante I and Reflection Cementless Acetabular Components,R318.17
  6. Structure and Performance of Fe-based Amorphous Coatings Prepared by HVAF and HVOF,TG174.4
  7. The Research on the Cost Controlling System of Trunk-liner Project Procurement,F817.12
  8. Fuel Surcharge Practices of Container Shipping Lines and Comparison with Fuel Cost,F552
  9. Research on Shipping Route Scheduling for Container Liner Under Emergency Situation,F224
  10. Study of Expandable Tubular Well Completion Technology in Tarim Oil Filed,TE257
  11. Reseach on Wear Resistance and Contact Fatigue Performance of Alloy Cast Steel for Roller,TG333.17
  12. The Influence of Probe Wanering to Testing Sheet Resistance of Large Silicon and Research on Simulation Technology,TN307
  13. The Research on Wear Behavior of High Chromium White Cast Iron and 7CrMnMoS Steel,TG143.1
  14. Study on High Wear-Resistant Alloy Steel Flux Cored Wires for Arc Spraying and Its Application,TG422.3
  15. 15Cr2Ni3MoW head steel oxidation behavior and performance of the organization of the oxide film,TG174.44
  16. Study on the Control of Empty Containers Shortage for Liners Base on Supply-chain Inventory Theory,F551;F224
  17. Research on Error Control of Network Video Communication Based on Network Coding,TN919.8
  18. High-energy ball milling copper alloy and anti-corrosion,TF123.111
  19. Application of Data Mining in the Preparation of the Ceramic Coating,TG174.453
  20. Research on the CNC of the Middle-convex and Varying Piston Processing,TG659
  21. Study on the Preparation and Photoconductivity of β-TiOPc,O626

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metal pressure processing > Rolling > Rolling process > Sheet, strip,foil rolling
© 2012 www.DissertationTopic.Net  Mobile