Study on the Preparation and Properties of the Electric Conductive Silk

Author: ShiJuan
Tutor: ChenGuoQiang
School: Suzhou University
Course: Textile Chemistry and Dyeing and Finishing Engineering
Keywords: silk fibers electrically conductive fiber electrical conductivity
CLC: TS146
Type: Master's thesis
Year: 2010
Downloads: 38
Quote: 0
Read: Download Dissertation

Abstract


Black electrically conductive material was formed on silk substrate by copper compound complexing with polar amino acids of silk. The effects of reagent concentration, reaction time, liquor ratio and pH value on the experiment were studied. The optimum process was obtained through a series of reaction:pH of solution=3, consentration of copper ions was 9%, liquor ratio was 1:50, reaction time was 2.5 hours. Under this condition, the electrically conductive properties of the treated silk fibers was the best. And the effects of the technological conditions on the weight gain of silk fiber were studied.It was found that the electrical conductivity of silk had good electrically conductive properties, and good electrical conductivity effect could be obtained under acidic conditions, and the distribution of copper sulfide was more even. Treated silk fibers remained the original good wearability, and the strength had no distinct decrease. X-ray diffraction and scanning electron microscope photos showed that fiber surface was evenly covered with a layer of black material, copper sulfide crystal.Moreover, silver electrically conductive silk was prepared using silver plating method. The effects of various factors on coating thickness and volume resistivity of silver electrical conductive silk was analyzed. The mechanical properties of fibers, fiber surface of the material structure and state respectively, washing performance, durability of electrically conductive fibers were measured by fiber strength tester, X-ray diffractometer and scanning electron microscope.The results showed that fiber surface was coated with a layer of metallic silver. X-ray diffraction and scanning electron microscope photos showed that metallic silver uniformly distributed on the fiber surface, and the desired results were achieved. The silver treated silk fiber had good washing performance and durability, relative humidity had little effect on it, even in very dry conditions it also had a very good electrical conductivity. It was also found that, after conducting treatment, strength of silk fibers decreased with the amount of Ag+ and ammonia concentration increasing, crystal structure of fiber had no change, which indicated that the surface chemical reaction mainly occurred in the amorphous region of silk fiber.

Related Dissertations

  1. Research on Mud Density Measuring Method Using Ultrasonic,TE256.7
  2. Research on Electrochemical Synthesis and Application of Conductive Polyaniline,O633.21
  3. Determining Suspended Sediment Concentration of Yellow River Delta Based on Electrical Conductivity,TV148.1
  4. The Research on Physical Chemistry Properties on Molten Salt of KNO3-NaNO2,O611.3
  5. Study on Improving the Property of Tire Shoulder Filled with Carbon Nanotubes,TB383.1
  6. The Preparation of Electrical Conductive Silk by Absorption Polymerization and the Study of Its Properties,TQ340.64
  7. Low concentrations of Cu-Ni-Si alloy microstructure and properties,TG146.1
  8. The Genetic Variation of Achnatherum Splendens Populations and Ecological Adaptation to Soil Salinity,Q948
  9. Effects of Rare Earth Elements on Microstructure and Conductivity of Pure Copper,TG146.11
  10. Chest wall defect bioremediation Materials and Experimental Research,R318.08
  11. Study on the Microvoid Building and Properties of Silk Fibers,TS102.33
  12. Graft Copolymerization of Cationic Compounds onto Silk Fibers,TS195.644
  13. Research on the Microvoids Formation,Structure and Properties of Silk Fiber,TS101.92
  14. Studies on Properties of Silk Fibers Modified by Metal Ions,TS102
  15. Research of Oak Silk Covering Yarn,TS144
  16. Preparation and Performance Research of Fe2O3-V2O5-P2O5 Semi-Conducting Glass,TQ171.73
  17. Structure and Properties of Silk Fibers Modified by Collagen Protein,TS195.6
  18. Develop and Performance Research about the Agricultural Soil-film of Non-woven Cloth with Cotton and Silk,S316
  19. Plasma Treatment of Mulberry Silk Fibers and Its Weighting Properties,TS195
  20. Studies on Weighting Methods and Properties of Silk Fiber,TS195

CLC: > Industrial Technology > Light industry,handicrafts > Textile industry,dyeing and finishing industry > Silk textile > Spun from silk fabrics
© 2012 www.DissertationTopic.Net  Mobile