Diffusion Welding of TC4 Titanium Alloy and LY12 Aluminum Alloy

Author: ZengHao
Tutor: ZhangLianMeng
School: Wuhan University of Technology
Course: Materials Science
Keywords: TC4 LY12 diffusion welding intermetallic compound enrichment
CLC: TG453.9
Type: Master's thesis
Year: 2010
Downloads: 160
Quote: 1
Read: Download Dissertation

Abstract


Diffusion welding of titanium and aluminum dissimilar alloy has broad applications in the area of the national economy and national defense and military fields. It also can exert the good properties of two alloys synthetically. And ti is significant for reasonably, efficiently and fully using titanium alloy and aluminum alloy.In this paper, TC4 titanium and LY12 aluminum alloy were welded together by vacuum diffusion welding, and TC4/LY12 welded joints were obtained successfully. TC4/LY12 optimal welding process parameters were obtained by the tensile strength, ultrasonic measurement of welded specimens. And we also adopted XRD, SEM, EDS and microhardness tester to get the mechanism of element diffusion and the interface formation of intermetallic compounds.The process system of TC4/LY12 diffusion welding is as follows:When welding temperature is 570℃, holding time is 60 minutes, welding pressure is 10MPa, the tensile strength of joint reaches its maximum at 31.70MPa. The fracture of the tensile specimen shows that the fracture occurred in the Al matrix and the diffusion interface. There are some small holes on TC4 side fracture surface while many small granular material on LY12 side fracture surface.The microhardness, microstructure, the phase and EDS analysis of tensile fracture show that, the a-Ti solid solution and a small amount of TiAl3 intermetallic compounds appear on the TC4 side fracture surface and the particulate matters on LY12 side are mainly TiAl3 compounds and a small amount of Al（ss, Ti） solid solution, in addition, Mg element enrichment appears on the granular material. Therefore, the joint fracture is mainly due to the appearance of intermetallic compounds TiAl3.Welded joints reaction layer products are decided by thermodynamics and kinetics factors. Growth models of reaction layers of TC4 titanium and LY12 aluminum alloy welding joints are divided into the following stages:effective physical contact,α-Ti and Al（ss, Ti） solid solution generating, TiAl3 intermetallic reaction layer generating, and intermetallic layer growing.

Related Dissertations

  1. The alkali fusion recovered from the glass fiber industry waste enrichment of platinum and rhodium metal,X781.5
  2. The Interaction of Fluroxypyr with the Green Alga Chlamydonomas Reinhardtii,S482.4
  3. Based magnetic fluid assembled hollow magnetic carbon microspheres and functional complexes,TB383.4
  4. Applied Research on Fast Detection of Corn Pathogens by the Technology Combining Magnetic Beads with PCR,S435.131
  5. Jiyang crude mechanism of gold enrichment,P618.13
  6. Electron beam welded joints under fatigue properties and residual stress of,TG405
  7. Enriched in arsenic speciation studies of water hyacinth,X173
  8. The quinoline degrading bacteria and diesel Nitrogen,X172
  9. Research of Crux Technology on Preparing Yoghourt Freeze-dry Starter Culture of Fermented Meet Product,TS251.5
  10. Experimental Study of Phase Interfaces in Ni/Sn and Ti/Sn Solid/liquid Diffusion Couple,TG111.6
  11. The Study on Preparation of Amphiphilic Nano-TiO2 Composite Particles and Their Application in PVDF Ultrafiltration Membranes,TB383.1
  12. Thermal Conductivity and Structure of SnInBi Low Melting Thermal Interface Material,TB34
  13. The Electronic Properties of MAlSi (M=Ca, Sr, Ba) at Different Pressure by First-Principles,O521.2
  14. Surface Quality Study on Ultrasonic Vibration Assisted Milling LY12 Aluminum Alloy,TG54
  15. Growth and Transformation Mechanism of Intermetallic Compounds at the Interface of Ti-6Al-4V/Al-12Si,TG457.1
  16. Study on Nonlinear Behaviour of Ultrasonic Interface Signals in Diffusion Bonding of 304 Stainless Steel,TG453.9
  17. Technology and Mechanism of Diffusion Bonding Hydrogenated TC4 Titanium Alloy and GH3128 Superalloy,TG453.9
  18. Investigation on the Preparation Method and Properties of SN-58BI Composite Solder,TG425
  19. Mechanism Research on Controlof TC4 Sheet Buckling Deformation with Impactingand Rotating Extrusion Method during Welding,TG404
  20. Research on the Electromigration Phenomena of Lead-Free Solder and Intermetallic Cu6Sn5 Phase in Lap Solder Joints,TG401
  21. Microstructure and Mechanical Properties of Dissimilar Metal Lap Joints of Al/Mg by Friction Stir Welding,TG453.9

CLC: > Industrial Technology > Metallurgy and Metal Craft > Welding, metal cutting and metal bonding > Welding process > Pressure welding > Other pressure welding
© 2012 www.DissertationTopic.Net  Mobile