Synthesis and Revisit of C-LiFePO4-PANI as Cathode Materials for Li-ion Battery

Author: WangXiaoHong
Tutor: HuangYunHui
School: Huazhong University of Science and Technology
Course: Materials Engineering
Keywords: Lithium ion battery Cathode material Polyaniline C-LiFePO4 Coating
CLC: TQ131.11
Type: Master's thesis
Year: 2013
Downloads: 19
Quote: 0
Read: Download Dissertation

Abstract


The olivine-structured orthophosphate LiFePO4has been viewed as the most popularand promising lithium-ion batteries cathode material owing to its high operatingvoltage（3.5Vvs Li/Li+）, good cycle performance, low cost, environmental friendly andsafety. However, pure LiFePO4shows poor reversible capacity and charging/dischargingperformance at high current density. In recent years, researchers have tried many methodssuch as controlling particle size,coating carbon and conductive polymer,doping metal ionand halogen ion to improve the performance of LiFePO4,and have achieved greatprogress.In this paper, conductive polymer polyaniline（PANI） and C-LiFePO4/PANIcomposite cathodes was successfully prepared by chemical oxidation.The synthesiscondition were systematically studied.The thermal stability of the as-prepared cathodeswere analysed by TG-DSC; The structure and morphology were characterized by XRD,FTIR spectra, SEM. Electrochemical performance was investigated by galvanosaticcharge/discharge cycling test and EIS.Experimental results show that the morphology and structure as well as theelectrochemical performance of PANI are greatly affected by the type and concentration ofthe protonic acid.PAIN shows good electrochemical performance when HCl with aconcentration of0mol/L is used as the doping acid. Its conductivity can be as high as2S cm-1.The conductivity and electrochemical performance of PANI can also be influenced bythermal treatment.PANI shows good conductivity(1.9S cm-1) and electrochemicalperformance when the temperature is about100℃.Its discharge capacity of the first cycleis107.3mAh g-1at0.5C and it maintains40mAh g-1when the current rises to5C.As thetemperature rises to200℃,the conductivity drops to10-7S cm-1,which is as low as anonconductor.The discharge capacity of the first cycle is only45.6mAh g-1and showsnearly no capacity at5C.PANI doped by HCl is very stable in the electrolyte.After being soaked in the electrolyte for about4weeks,the structure and morphology of PANI/HCl changes little.The same synthesis condition unsuits the preparation of well-performancedC-LiFePO4/PANI.By coating C-LiFePO4with PANI in this condition,the compositecathode shows poor electrochemical performance.The optimal synthesis condition of the C-LiFePO4/PANI composite cathode isobatained through orthogonal experimental design.When the molar ratio of aniline andammuonium persulfate is1to0.8,the pH of the reaction system is4and the reaction timeis4hours,the C-LiFePO4/PANI composite cathode shows the best performance.And pH ofthe reaction system affects greater than the other two factors.

Related Dissertations

  1. The Effect of Current Density and Electric Field on Ni and Its Alloy Electrodeposition for Copper Crystallizer,TQ153.2
  2. A Study on the Electrodeposition of Zn-Co and Zn-Ni Alloys in the Reline Room Temperature Ionic Liquid,TQ153.1
  3. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  4. Preparation and Performance of V2O5-WO3/MOx/Cordierite Catalyst Modified with Cu、Mn、Ce for DeNOx,X701
  5. Anti-corrosion Property of Flake Zinc Epoxy Coating Doped with Rare Earth in SRB,TQ630.1
  6. Polyaniline / short fiber reinforced natural rubber properties,TQ330.1
  7. Synthesis and Application of the Bright Polyacrylate,TQ630.4
  8. Effect of Hydrophobic Modification of the Flame Retardant on the Properties of the Water-borne Intumescent Fire Retardant Coatings,TQ637
  9. Study on the Rutile Titanium Dioxide Superfine Comminution and Surface Treatment,TQ621.12
  10. Research of Graphitized Needle Coke Coated by Phenolic Resin Pyrolytic Carbon as Anode Material for Lithium Ion Battery,TM912
  11. Preparation and Modification of Lithium Ion Battery LiNi0.8Co0.05O2 Cathode,TM912
  12. Antibacterial plastic with silver coating developed,TQ637
  13. The Development and Application of Spray Polyurea Elastormer Waterproof Material on High-speed Railway,TQ639
  14. Study on the Silicone Modified Acrylic and Water-borne Anti-corrosion Coatings,TQ637
  15. Study of Aluminum Foil Desiccant Coating of Finned Tube Heat Exchanger,TQ051.5
  16. Studies on Transform the Spent Bath of Electroplating Nickel-Phosphorus Alloy Plating to Electroless Plating Solution,TQ153
  17. Preparation and Properties of Environment-friendly Residual Rust Coating,TQ630.7
  18. Preparation and Studies on PANI-SiO2 Hybrid Transparent Conducting Films,TB383.2
  19. Bond Strength between the Epoxy Resin Coating and Steel Structure Pretreated with Sand Blasting,TG174.4
  20. Structure and Performance of Fe-based Amorphous Coatings Prepared by HVAF and HVOF,TG174.4
  21. A Study of Adhesive Thin-Film Layer Drying Process,TQ430

CLC: > Industrial Technology > Chemical Industry > Inorganic compounds, the chemical industry of the metal elements > First Ⅰ group metal elements of inorganic compounds > Inorganic compounds of the alkali metal ( Ⅰ A family ) elements > Inorganic compounds of lithium
© 2012 www.DissertationTopic.Net  Mobile