The Study on Ag Plating Graphene/Epoxy-acrylate Electrical Conductive Adhesive

Author: ZuoShuo
Tutor: YuChaoSheng
School: Northeast Forestry University
Course: Polymer Chemistry and Physics
Keywords: electrical conductive adhesive Ag planting graphene nano-conductive filler epoxy-acrylate shear strength
CLC: TQ426
Type: Master's thesis
Year: 2013
Downloads: 108
Quote: 0
Read: Download Dissertation

Abstract


As the development of science and technology nowadays, energy-saving and environment-protecting have became a common target of the whole world. In the area of electrical packing, the using of novel electrical conductive adhesive, which is low in energy consumption, environment-friendly, instead of traditional tin/lead solder, would be an irresistible trend in the future. In this paper, Ag-planting-graphene was used as conductive filler and epoxy-acrylate adhesive was used as matrix material to produce two novel electrical conductive adhesives with good mechanical and conductive properties as well as good thermal stability.The conductive filler of the Electrical Conductive Adhesive (ECA) in this paper was prepared from natural flake graphite, Graphite Oxide (GO) was obtained by Hummers method, and the GO was disposed with ultrasonic to get graphene oxide. After AgNO3was mixed with the graphene oxide, ethylene glycol and NaBH4were used to reduce the mixture corporately. Then the nano-conductive filler of Ag-planting-Graphene (Ag-G) was obtained. Epoxy-Acrylate (EA) was synthesized by epoxy resin with acrylate acid to be used as matrix material, then Methyl methacrylate as diluent, Benzoyl peroxide as curing agent, N,N-dimethylaniline as curing catalyst and other assistant agents were added to get two-component epoxy-acrylate adhesive (EA1adhesive); In addition, methyl methacrylate as diluent, benzophenone as curing agent and other assistant agents were added to get UV curing epoxy-acrylate adhesive (EA2adhesive). The Ag-G was mixed with the EA1adhesive to produce Ag-G/two-component Epoxy-Acry late Electrical Conductive Adhesive (Ag-G/EA1ECA) and with the EA2adhesive to produce the Ag-G/UV curing Epoxy-Acrylate Electrical Conductive Adhesive (Ag-G/EA2ECA), respectively.The characterization of Ag-G has been carried out by Transmission Electron Microscope (TEM), X-ray diffraction (XRD), Raman spectrum (Raman) and X-ray photoelectron spectroscopy (XPS). It could indicate that the conductive filler Ag-G has been produced successfully. The acid value detection and FT-IR analysis indicated that the optimal reaction time of the synthesis of epoxy-acrylate was3h.The shear strength (T) of the two kinds of ECA was tested by the universal testing device to get the relationship between the shear strength of ECAs and the content of conductive filler. It could be observed that the shear strength was decreased with the increasing of content of conductive filler. Moreover, the standard digital multimeter was used to estimate the resistance (R) of the two kinds of ECA. Through formula computing, the relationship between the electrical conductivity (ะบ) of ECA and the content of conductive filler were obtained. As the increasing of content of conductive filler, the electrical conductivity increased rapidly, but it changed a little when content of Ag-G reached to25wt%in the two kinds of ECA. The thermal stability was carried out through thermogravimetric analysis (TGA). From the curves of TG and DTG, the thermal property parameters were as follows:the initial temperature of thermal degradation (to), the maximum weight loss rate (Dm) as well as the temperature of maximum weight loss rate (tm), and the final carbon residue quantity (w) were obtained.Comprehensive analysis of the whole experiment results demonstrated that both the shear strength and electrical conductivity of Ag-G/EA1ECA were better that of Ag-G/EA2ECA. Meanwhile, both of the two ECA showed good thermal stability.

Related Dissertations

  1. Investigation on Microstructure and Properties of Cadmium-Free Silver-Based Intermediate Temperature Filler Metals,TG425.2
  2. Synthesis of Modified Epoxy Acrylate Resin and Application as Paper Wet Strength Agent,TS727
  3. Preparation and Application of Three Dimensional Reinforcements with Carbon Nanotubes Grown on the Fiber Surfaces in Situ,TB383.1
  4. Modification of Polyurethane Acrylates Coating with Cycloaliphatic Epoxy Resins,TQ630.4
  5. Measurement of Geotechnical Properties for Sewage Sludge at a Disposal Site and Evaluation of Its Influence on Slope Stability of MSW Landfill,X705
  6. Experimental Research on Shear Parameter of High Cut Slope Gravel Soil in Badong and Its Engineering Application,TV221.2
  7. The Finite Element Modelling on Anti-inrushing of Deep Foundation,TU473.2
  8. Evaluation Methods of Tack Coat and Stress Absorbing Interlayer,U411
  9. Preparation and Sheering Properties of High Thermal Emission Coatings on Ti Alloy,TG115
  10. Study on Surface Structure of High-Modulus Carbon Fiber and Interfacial Properties of HM-CF/TDE-85,TB332
  11. Investigation of Phosphating Treatment of Sodium Dihydrogen Phosphate and Adhesive Performance of AZ31 Mg Alloy,TG146.22
  12. Study on Self-piercing Riveting of Friction-heated Magnesium Alloy Sheets,TG938
  13. The Synthesis and Application of One Novel UV-curable Prepolymer,O631.3
  14. The Effect of Different Therapy of Desensitization on the Microscopic Characteristic of the Dentinal Surface and the Shear Bond Strength of Resin Cements,R783.1
  15. Application of the Triple Shear Unified Failure Criterion to Geotechnical Engineering,TU411
  16. Create Coating of High Emissiviy Titanium Surface Micro-Arc Oxidation and Sol-Gel,TG174.4
  17. Preparation of High Surface Adhesive UHMWPE Fibers,TQ342.61
  18. Research on Flocculation Kinetics Based on the Coagulationand Precipitation Integrated Process,TU991.2
  19. Research on Shear and Torsion Behavior of Concrete Filled Steel Tubular Members and the Application in National Standard,TU398.9
  20. Experimental Research on Nonlinear Rheological Characteristics of Expansive Soil,TU443
  21. Study on High Performance UV Curable Resin Systems,TQ320

CLC: > Industrial Technology > Chemical Industry > Reagents and the production of pure chemicals > Catalyst ( catalyst )
© 2012 www.DissertationTopic.Net  Mobile