The Synthesis and Property Study of a Novel UV-curable Prepolymer

Author: ZhouKuan
Tutor: HuangBiWu
School: Nanchang University
Course: Materials Engineering
Keywords: UV-curing Diethylene glycol diglycidyl ether epoxy acrylate nano-modification
CLC: TQ630.43
Type: Master's thesis
Year: 2013
Downloads: 48
Quote: 0
Read: Download Dissertation

Abstract


Bisphenol-A epoxy acrylate is widely used as prepolymer with its high curing rate, high hardness of curing film, high gloss, thermal stability and excellent corrosion resistance, however, the current synthesis method of bisphenol-A epoxy acrylate is taking addition reaction of the raw material all at once that reaction temperature was105℃. The shortcoming of the current synthesis is unevenly of relative molecular weight distribution, high viscosity of resin, a less convenient and needing quite more reactive diluent during the mixture of coatings. Thus, the current synthesis will result in increased costs, on the other hand, the technology will become complex.Diethylene glycol diglycidyl ether is a kind of low viscosity epoxy compound which can lower the viscosity of the system, and improves the physical properties of resin when it was added to bisphenol-A epoxy acrylate. As a result, the thesis is put forward that a new kind of photosensitive prepolymers was synthesized with epoxy resin and Diethylene glycol. The details are as follows:A new kind of photosensitive prepolymers was synthesized with E-51/JX-023mixture and acrylic acid(AA) as raw materials with triphenylphosphine as the catalyst, and with4-methoxy phenol as the inhibitor. This thesis studied the effects of reaction temperature, the dosage of catalyst and inhibitor. Experimental results showed that the best reaction temperature was105℃, the best mass fraction of the catalyst and the inhibitor was0.80wt%and0.3wt%. When the substrates were mixed on the scale of2.5:1, the viscosity of the system was very low. So the UV-curing coating was prepared with adding photoinitiator to the new kind of photosensitive prepolymers, the UV-cured film has good properties.Furthermore, Nano-SiO2which was treated by surface modification with cetyl trimethyl ammonium bromide and coupling agent with KH-570and was filled into the new kind of photosensitive prepolymers, and adding photoinitiator to make of nanocomposite coatings, and investigated the dispersion of nano-SiO2in the resin by microscope. The results showed that the dispersion of nano-SiO2which was modified was good. And hardness and physical properties of its cured film was investigated, the results showed that the addition of nano-SiO2can enhance the hardness.

Related Dissertations

  1. Synthesis of Modified Epoxy Acrylate Resin and Application as Paper Wet Strength Agent,TS727
  2. The Synthesis and Research of Cationic Photoinitiator-diphenyliodonium Hexafluorophosphate,O621.3
  3. Study on Durability of Ultra Violet Cured GFRP and Its Strengthened Concrete Beam,TU375.1
  4. Study on High Performance UV Curable Resin Systems,TQ320
  5. Study on the Synthesis and Modification of Epoxy Acrylate Adhesive for UV-curing,TG492
  6. Studies on Synthesis and Properties of Hyperbranched Photosensitive Polysiloxane Urethane Acrylate Oligomers,O634.41
  7. Research on Scratch and Abrasion Resistance Coating on the Surface of BOPET Film,O484.4
  8. Study on Synthesis and Properties of Uv-curable Epoxy / Polyurethane Powder Coating,TQ630.7
  9. Design and Research of UV LED Curing System,TN23
  10. Polyamide epichlorohydrin synthesis, modification and in the paper on the application,TS727
  11. Study of UV Curing of Bismaleimide,TQ323.6
  12. The Study on the Air System of Light Radtech for the Paper Dryer,TS803
  13. The Synthesis and Properties of UV-curable Unsaturated Polyester-Urea Resins,TQ633
  14. Synthesis and Properties Research of Photosensitive Fluoric Poly (Amic Ester),O633.2
  15. Studies on the Synthesis and Characterization of Photosensitive Coatings,TQ637
  16. Synthesis and Application of UV-curing co-Synergists p-Dimethylaminobenzamides,TQ246
  17. Photoinitiating agent , a pigment on the curing speed of ultraviolet (UV) curable inks .,TQ638
  18. Farther Study on Dental Fiber-reinforced Composite Post,R783
  19. Weather resistant UV Coatings,TQ637
  20. The chemical inkjet chip rapid prototyping technology research,TN405
  21. The Research of Transfer Pattern Layer and Stamp Imprinting and Curing Process Based on UV-NIL,TN23

CLC: > Industrial Technology > Chemical Industry > Paint Industry > General issues > Raw materials and auxiliary materials > Natural polymer and their derivatives
© 2012 www.DissertationTopic.Net  Mobile