Controlled Synthesis and Capacitance Performance of Polyaniline/Manganese Dioxide Composites

Author: JiangJianYan
Tutor: HuoYuQiu
School: Northeastern University
Course: Chemical Engineering
Keywords: polyaniline manganese dioxide controlled synthesis capacitance performance
CLC: TB33
Type: Master's thesis
Year: 2011
Downloads: 6
Quote: 0
Read: Download Dissertation

Abstract


Polyaniline/Manganese dioxide composites were successfully obtained on the Au line treated by4-ATP in situ chemical oxidation, using KMnO4as the oxidant. The PANI/MnO2composites were characterized by SEM, FT-IR and XRD, and the capacitance performance was studied by cyclic voltammetry and chronopotentiometry. The SEM results show that the composites were nano-particle (200nm diameter) with a trend to be rod. The characteristic absorption peaks of polyaniline and manganese dioxide were observed in FT-IR spectrum. XRD analysis results show that polyaniline and manganese dioxide were amorphous. The results of cyclic voltammetry and chronopotentiometry of PANI/MnO2composites indicated that the composites were with fine capacitance performance, and the single electrode specific capacitance was up to341F/g.The single-factor test was conducted to investigate the influence of concentrations of aniline,4-ATP concentrations, pH values, the ratios of aniline to HC1, the ratios of aniline to KMnO4and the reaction time to capacitance performance of composites. The results show that composites show fine capacitance performance under following condition:the concentration of aniline was0.15M, pH value was4, the concentration of4-ATP was1mM, the ratio of aniline to HC1was1:1, the ratio of aniline to KMnO4was1:1and the reaction time was10h. The single electrode specific capacitance was up to324F/g.Orthogonal experiment was performed with L18(36) orthogonal table. It was confirmed that concentration of4-ATP is of great influence on the capacitance performance of composites, according to the analysis of variance of orthogonal design experiments. And the optimal solution was choosed to conduct three parallel experiments, the capacitance performance of composite was fine, the single electrode specific capacitance was up to341F/g.

Related Dissertations

  1. The Preparation of Polyaniline-Metal Complex and the Study on Its Catalytical Property,O634
  2. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  3. Preparation and Property Study of Polyaniline/Polyester Composite Conductive Fabric,TS195.6
  4. Polyaniline / short fiber reinforced natural rubber properties,TQ330.1
  5. Flexible Electrodes Material Based on Polypyrrole Composites and Capacitance Properties for Supercapacitor,TM53
  6. New Methods for the Degradation of Phenolic Compounds,X703
  7. Study on DNPH and SSS Modified Polyaniline-based QCM Sensors in Cultural Relics Conservation Micro-environment,TP212
  8. The Preparation of Metallic Fabrics with PD-Free Activation and Research of Its Properties,TS106
  9. Preparation of LSMO/PANI(DBSA Doped)/Co/Pt Organic Spin Valve and Study on the MR Effect,O484
  10. Surface Modification of Attapulgite and Conducting Polyaniline Composite Materialss,TB332
  11. The Controlled Synthesis of Noble Metal Nanoparticles and Their Properties in Optic and Catalytic Field,TB383.1
  12. Preparation and Properties of Polyaniline, Polypyrrole and Its Composites,TB332
  13. Study on the Surface Modification of Polyaniline and Its Application in Anticorrosive Coating,TQ637
  14. Electrolyzing MnO2 and Mn in the Same Cell in the Chlorine Salt Medium,TQ151
  15. The Preparation and Characterization of Conducting Polymers with Electromagnetic Function,TB383.1
  16. Study on Fluorescent Hydrotalcite-like and Polyaniline Composite Materials,TB332
  17. Organic acids control the synthesis of polyaniline satisfied / micron-sized structures,TB383.1
  18. Preparation and Ammonia-Sensitive Properties Study of Polyaniline and Its Composite Materials,TB332
  19. Study on the Fibre Modified by Polyaniline and the Electrical Conductivity of That,TQ340.1
  20. Chemical Preparation of Hollow Silica Microspheres and Composition with Polyaniline,O633.2
  21. A1 -based Pb-PAN composite coatings electrodeposited Preparation and Properties,TQ153

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Composite materials
© 2012 www.DissertationTopic.Net  Mobile