Technology and Performance of Ni-based Coating Fabricated by Mechanical Alloying

Author: ZhangGuoZuo
Tutor: HuangWeiJiu
School: Chongqing University of Technology
Course: Materials Science and Engineering
Keywords: Mechanical alloying Ni-Al powder coating grinding speed grinding time
CLC: TG174.4
Type: Master's thesis
Year: 2013
Downloads: 15
Quote: 0
Read: Download Dissertation

Abstract


Metal powder are strongly squeezedor crashed by hard milling balls while themechanical-alloying happened inside the milling can and the crash-induced heat couldweld the metal powder to the can surface. Also the long-time squeezing and weldingreaction will generate a relative condensed coating layer. According to thismethodology, milling time, milling speed and powder categoryare discussed toillustrate the coating-form mechanism and the effects of the three elements arerespectively demonstrated as well.The chemical compositions and phases of Ni-Al based coating are analyzed viaX-Ray diffraction(XRD), Scanning electron microscope (SEM) and energy dispersiveX-ray spectroscopy (EDS) while the mechanical properties are assessed bymicro-hardness tests, thermal shock tests, high-temperature oxidation resistance tests,corrosion resistance tests and tribological experiments. Based on the mentionedexperimental methodology above, the main results are obtained as follows:Firstly, Ni and Al powder were mixed at a mass ratio of4:1and then the mixturewere grinded at speeds of200rad/min,400rad/min and600rad/min respectively.After the milling, conclusion that the coating thickness changed with milling speedsand a well-structured consensus layer which was surprisingly as thick as130um wasobtained at the speed of400rad/min were found. To further understand the coatingmechanism, Ni powder, Ni-0.1Al-0.1Cr powder, Ni-0.2Cr powder and Ni-0.2Alpowder at the milling speed of400rad/min were invested, and the conclusion was theseries Ni-0.2Al powder coating formed the most condensed and continuous. Thereforethe speed of400rad/min was closed with the Ni-Al powder system and effects ofballs/powder ratio(5:1and10:1, respectively) was discussed and the balls/powderratio of5:1could better coating construction in terms of consensuses.Also, Ni-Al based coating system was invested after according experimentalmethods with different Al-containing percentage of0.2,0.4,0.6, and0.8and withgrinding time of6h,12h,18h, and24at grinding of400rad/min. As results ofhardness tests, the hardness of coated layer showed an increasing tendency while themilling time prolonged. Additionally, the hardness of Ni-Al coating layers decreasedwhile the Al-containing percentage improved but the high percentage of Al mayenhance the corrosion resistance. Furthermore, the coating spelling resistance firstincrease then decrease in the Ni-Al system of powder with increasing milling time via thermal shock experimental results. High temperature oxidation test shows that longermilling time can reduce the high temperature oxidation resistance,After all, milling time, powder category and milling speed are invested anddiscussed to demonstrate the coating forming mechanism.

Related Dissertations

  1. Preparation of Micro-Arc Oxidation Ceramic Coating on Mg Alloy and the Research of Galvanic Corrosion,TG174.453
  2. The Effect of Current Density and Electric Field on Ni and Its Alloy Electrodeposition for Copper Crystallizer,TQ153.2
  3. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  4. Preparation and Performance of V2O5-WO3/MOx/Cordierite Catalyst Modified with Cu、Mn、Ce for DeNOx,X701
  5. Anti-corrosion Property of Flake Zinc Epoxy Coating Doped with Rare Earth in SRB,TQ630.1
  6. Study on Chitosan-Based Composiate Nano-Coating Dope and Its Effect of Fresh-Keeping for Coated Egg,TS253.2
  7. Studies of Plasma Spray Metal-Ceramic Compounds Coatings on Q245r Steels,TG174.44
  8. Preparation and Oxidation Resistance of SiC/γ-Y2Si2O7 Double-layer Coating on C/C Composites,TB332
  9. Optical Parametric Oscillator and Its Frequency Doubling to Achieve Three Primary Colors RGB Solid-state Lasers,TN248
  10. Research of Properties and Preparation Technology of Multiphase Ceramic Coating with Reactive Flame Spraying Process on AZ31B,TG174.44
  11. Cultivation of Aerobic Granule and Its Application in Treatment of Autombile Coating Wastewater,X734.2
  12. Antibacterial plastic with silver coating developed,TQ637
  13. The Study of Sodium Alginate Film Coating for the Fresh-keeping of Mango Fruit,TS255.3
  14. Manufacture and Property Research on FeAl Based Porous Material,TF124.5
  15. Structure and Performance of Fe-based Amorphous Coatings Prepared by HVAF and HVOF,TG174.4
  16. Dssc Light Anode Preparation and Performance Study,TM914.4
  17. A Study of Adhesive Thin-Film Layer Drying Process,TQ430
  18. Design and Optimize of LED Packaging Process,TN312.8
  19. Research on Bacterial-Cellulose Coating Small-Caliber Artificial Blood Vessel,TS106.67
  20. The Research on TEA CO2 Laser with Two Shift Output Coupling Mirrors,TN248
  21. Creation and Application of Trichodema Bio-Seed Coating Agent,S435.131

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile