Experimental Study on Thickening Mechanism of Blast Furnace Slag Bearing Titanium

Author: WangHua
Tutor: QiuGuiBao
School: Chongqing University
Course: Metallurgical Engineering
Keywords: BF slag bearing titanium Viscosity Low-temperature simulation Reduction Ti(C,N)
CLC: TF524
Type: Master's thesis
Year: 2013
Downloads: 100
Quote: 0
Read: Download Dissertation

Abstract


Panzhihua-Xichang Region in China is abundant in vanadium titanomagnetiteresource, the iron resource in which is extracted mainly by blast furnace smelting. Inview of making the most of the vanadium titanomagnetite resource and improving theeconomic competitiveness, increasing the proportion of vanadium titanomagnetite inraw materials for blast furnace would be imperative. However, the percentage of TiO2would inevitably increase consequently, which could deteriorate the slag properties,especially the viscosity, according to the experiences of blast furnace smelting. With thedevelopment of BF smelting technology, reviewing the previous achievements andresearching on the rheological property of BF slag bearing titanium would providereference for practice.The paper involving laboratory-scale experimental researches on low-temperaturesimulation and high-temperature measuring of the viscosity of BF slag bearing titanium,as well as the reduction of BF slag bearing titanium, on the basis of reviewing theprevious achievements about the rheological properties of BF slag in domestic andabroad, the specific information of which is as following:(1) In the low-temperature simulation experiment, the glycerol-PPS suspensionwas adopted to simulate the molten slag-Ti(C, N) solid-liquid system, and therheological property of the glycerol-PPS suspension was measured with the BrookfieldViscometer to investigated the influence of volume fraction and particle size of soliddispersion phase on viscosity of suspension. The results are as follows: the glycerol-PPSsuspension showed Binham behavior; the apparent viscosity of the suspension increasedwith the increase of the volume fraction and the decrease of the particle size of the solidparticle; the exponential type viscosity model best described the relation between theviscosity of suspension and the volume fraction of solid particles; variance analysisshowed that both the effects of volume fraction and particle size of PPS were significant,and the effect of volume fraction was more significant than that of particle size.(2) The viscosity evolution of BF slag bearing titanium was measured by rotationalcylinder method under high-temperature reduction condition. As demonstrated by theexperimental results, the TiO2content、reduction time and the basicity (CaO/SiO2)played significant role in the slag viscosity; the slag viscosity increased with theincrease of TiO2content and reduction time; after90mins’ and120mins’ reduction, the slag viscosity increased with the increase of basicity (CaO/SiO2) firstly and maximizedat (CaO/SiO2)=1.11, however, it decreased afterwards.(3) With respect to the experimental research on the reduction of the BF slagbearing titanium, the tube furnace was employed to control the reduction atmosphereand temperature, the influences of which were investigated on generation state of Ti(C,N). The results showed that: only TiC was found and produced at about1400℃underAr atmosphere; while under N2atmosphere, TiN was dominant in Ti(C, N), in whichTiN formed at some1350℃and TiC formed at some1500℃; Ti(C, N) mainly formedon the border between the slag and the graphite; the content of Ti(C, N) increased withthe increase of reduction temperature and dispersed into the slag body.

Related Dissertations

  1. Experimental Research on Influence of Coal Reburning Reaction Conditions on NO_x Reduction by Non-Catalytic Reduction of Ammonia,X701
  2. Experimentation Research for Deoxidize Reaction Process of NO_X Adopt Different Reburnning Fuels,TK227.1
  3. Study of Tin Alloy Carbon Composite Used for Lithium Ion Battery,TM912.9
  4. Research on Key Technologies of Automatic Steel Wire Galvanizing Production Line Based on Gas Reduction Method,TQ153.15
  5. Effect of Limestone Powder on Properties of Concrete Mixture,TU528
  6. Research and Implementation of the Conflict Resolution in Process Modeling of Magic Platform,TP311.5
  7. Study on Spinning of High Viscosity Polyamide-6/Rare Earth,TQ340.64
  8. Physical Fields’ Characteristic Study & Structural Optimization of a SCR Denitrification Reactor,X773
  9. Study on the Synthesis of the Polypyrrole-Cobalt Oxides and Their Catalytic Behavior for the Electroreduction of H2O2,O643.32
  10. Study on Properties of Ce、Co、Ni/V-W/TiO2 Modified by Composite Sol for Selective Catalytic Reduction,X701
  11. Applied Research of Emulsified Fuel on S195 Diesel Engine,TE626.24
  12. Theory of China’s Carbon Emissions and Strategy Research in Service Outsourcing,X321
  13. Research on Obviate Measures of Continuous Cropping Obstacles of Rehmannia Glutionsa,S435.672
  14. Synthesis and Properties of Novel Low Viscosity Difluorooxymethylene-Bridged Liquid Crystals Compounds,O753.2
  15. Reduction of Carbonyl Compounds with Ammonia-Borane in Water,O621.254.2
  16. Study on the Interactive Mechanism of Energy Conservation and Pollution Reduction between Government and Enterprises,D922.68
  17. Research on the Problems and Countermeasures of Low Carbon City in Chongqing,X321
  18. Open Reduction and Internal Fixation of Displaced Scaphoid Fractures,R687.3
  19. High-rise building under the jointed rock slope stability studies,TU457
  20. Sodium borohydride chiral hydroxy ( amine ) ester and oxazolidinone reduction Synthesis of,O621.25
  21. Study on No Biogolcal Removal Coupled with the Absorption by FeⅡ （EDTA）,X701

CLC: > Industrial Technology > Metallurgical Industry > Ironmaking > Raw materials > Slag
© 2012 www.DissertationTopic.Net  Mobile