Ce-Mn Mixed Oxides Supported on Glass-Fiber for Low-temperature Selective Catalytic Reduction of NO with NH3

Author: LiLe
Tutor: DiaoYongFa
School: Donghua University
Course: Heating,Gas Supply, Ventilation and Air Conditioning Engineering
Keywords: Ce-Mn mixed Oxides Glass-Fiber Low-temperature SCR by NH3 NO SO2poisoning
CLC: X701
Type: Master's thesis
Year: 2014
Downloads: 60
Quote: 0
Read: Download Dissertation

Abstract


NOx that emitted from coal-fired flue gas is one of the most atmospheric pollutants, so efficacious control is necessary to stop serious atmosphere environmental pollution caused by NOx. Low-temperature SCR device is arranged after the dust removal and desulfurization, it can be not only avoid the flue gas preheat energy consumption and reduce the operating cost, but also ease the congestion and the poison of dust and SO2. Based on the review of the current situation of SCR technology, Ce-Mn mixed oxides has widely paied attention to domestic and foreign researchers, but TiO2, Al2O3and Activated Carbon were the main support, this could not solve the problem of retrieve and particulate matter controling. In order to solve these problems, a new technology that cerium-manganese oxides supported on modified glass-fiber was proposed to achieve removing NO and particles in low-temperature.Firstly, high temperature inorganic glass fiber was selected as the catalyst carrier in this study, and the glass fiber was modified to reach the best effect of loading. In addition to the necessary grouping comparative experiments, the pretreatment experiments design of glass fiber fabric using response surface methodology was used to identify the optimal pretreatment conditions from the theoretical analysis of existing experimental theoretical analysis.Secondly, samples of cerium-manganese oxides supported on modified glass-fiber with different molar Ce/Mn ratios (Ce-Mn/GF) were prepared by an impregnation method and tested for low-temperature (80-180℃) selective catalytic reduction (SCR) of NO with ammonia. This brand-new technology could remove NO and particles matter from coal-fired flue gas. The surface properties of the catalysts were examined using Brunauer-Emmett-Teller (BET), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and scanning electron microscopy (SEM). The experimental results showed that the catalyst with a molar Ce/Mn ratio of0.2 obtained high activity of87.4%NO conversion at150℃under a high space velocity of50,000h-1. Deactivation poisoned by SO2still occurred, but the Ce-Mn/GF(0.2) catalyst performed desirable tolerance to SO2with decreasing50%in40min and then maintaining at about30%NO conversion. Characterization results indicated that the excellent low-temperature catalytic activity is related to the high specific surface area, pore structure, and amorphous phase.Furthermore, the effect of temperature, O2, NH3, NO and SO2on the SCR activity of Ce-Mn/GF(x) catalysts as well as its mechanism were investigated detailed. The influence of sulfur poisoning on the SCR performance of Ce-Mn/GF(x) was investigated at150℃for60min by adding550ppm SO2to feed gases. For the Mn/GF catalyst the NO conversion dropped from77.4%to3%during20minute, which means that a severe deactivation occurred to the catalyst after exposure to SO2. Clearly, sulfur resistance of the Ce-Mn/GF(x) catalysts strengthened with the increasing of Ce loading. The reason is that a portion of the Ce4+transformed into Ce3+ions as the SO2acted as a reducing agent on sample surface.On the basis of this study, it can be concluded that the Ce-Mn/GF(0.2) catalyst showed high activity without SO2existed. Above87%NO conversion was obtained at150℃under a space velocity of50,000h-1.Characterization results indicate that the catalytic activity is related to the specific surface area, pore volume, and the amorphous phase. In case of Ce-Mn/GF(0.2), BET surface area and pore volume were relatively high. It was known from XPS analysis that Mn valence state on the surface of the Ce-Mn/GF(x) catalysts(x≠0) were in Mn4+state. XRD showed that Ce-Mn mixed oxides were well-dispersed throughout the support structure. In future work, the regeneration of Ce-Mn/GF catalysts, the de-dusting capability, and the interaction between Ce and Mn oxides are worthy of detailed investigation.

Related Dissertations

  1. The Study of Silicon/Nitrogen Resin Containing Terminal Alkynyl Groups and Its Composites,TB332
  2. Microcellular Injection Molding of PP/GF Composites,TQ325.14
  3. Hydrodynamic Behavior & Meterial Optimization Research of Bridge Deck Pavement in Moist Heat Areas,U444
  4. Preparation and Research on Spectral Properties of Bi-doped Silica-based Glasses,TQ171.1
  5. Study on Properties of Glass Fiber Reinforced Gypsum Composite Material,TQ177.37
  6. Prestressed glass fiber reinforced concrete bending members mechanical properties of normal section bearing capacity study,TU377
  7. Study on Philosophy and Experiment of Reinforced Concrete Bridges Strengthened with Reiforced Materials,U445.72
  8. Study on Glass Fiber Reinforced Poly (3-hydroxybutyrate-co-4-hydroxybutyrate) and Glass Fiber Surface Modification,TQ327.1
  9. Research on Glass Fiber and Resin Wettability,TQ320.1
  10. Investigation of Laminated Veneer Lumber Performance Reinforced with Pre-compressed Veneer,TS653.3
  11. Preparation and Properties of Glass Fiber Reinforced Phenolic Molding Compounds,TQ323.1
  12. The Preparation of Glass Fiber Reinforced Flame Retarded Epoxy Composites,TQ323.5
  13. Analysis and Control Teehnology Research on the Stability of the Tunnel Face,U455.4
  14. Research on Advanced Pre-Reinforced Technology of Working Face for Liuyang River Tunnel,U455.49
  15. Study on the Properties of High Durability Bolt Underwater Retaining Wall,TU476.4
  16. Study on Laminationg of the Continous Glass Fiber Reiforced Theermoplastic PVC,TB332
  17. Research on Properties of Glass Fiber Textile Reinforced Submarine Composite by RTM Process,TB332
  18. Surface Treatment of Multi-component Phosphate Laser Glass,TQ171.1
  19. Experimental Research on Working Performance of Soil-nail with Mortar-bonded GFRP,TU472
  20. Study on Composition and Properties of Boron-fluorine-free Fiberglass,TQ171.1
  21. Study on the Material of Asphalt Overlay and Interlay on the Old Cement Concrete Pavement,U414

CLC: > Environmental science, safety science > Processing and comprehensive utilization of waste > General issues > Exhaust gas processing and utilization
© 2012 www.DissertationTopic.Net  Mobile