Dissertation > Excellent graduate degree dissertation topics show

In Vitro Evaluation of Zirconia Surface Treatments on the Shear Bond Strength of Veneering Ceramic

Author: LiuHongGuang
Tutor: ZhuHongShui
School: Nanchang University Medical College
Course: Clinical Stomatology
Keywords: zirconia sandblasting grinding veneering ceramic shear bondstrength
CLC: R783.2
Type: Master's thesis
Year: 2013
Downloads: 18
Quote: 0
Read: Download Dissertation

Abstract


Objective:To study different sandblasting conditions and different surface coarseningmethods affecting the shear bond strength between zirconia and veneering ceramic,provide suitable pretreatment method for technical processing zirconia.Method:1. The method of making zirconia test pieces:Zirconia ceramic block were cut, dense sintered into8mm×8mm×3mm（±0.02）186blocks, randomly divided into31groups, six blocks in each group.2. Groups:⑴Combined on condition that the sandblasting powder particles of different（A1=75μm、 A2=110μm、 A3=150μm）, the sandblasting pressure （B1=0.2MPa、B2=0.4MPa、B3=0.6MPa） and sandblasting time （C1=10s、C2=20s、C3=30s）,forexample A1B1C1、A1B1C2、A1B1C3、A1B2C1etc were divided into27groups, then27groups were sandblasted in different conditions.⑵According to different surface coarsening methods,the experiments dividedinto control group、grinding group、sandblasting group、grinding and sandblastinggroup.Control group:with no handling;grinding group:diamond bur grinding underwater-spray jet;sandblasting group:Al2O3sandblasting （110μm,0.4MPa,20s）;grindingand sandblasting group:diamond bur grinding under water-spray jet+aluminium oxidesandblasting （110μm,0.4MPa,20s）.3. Experimental determination:One block of each group was selected for observing the surface topographies byscanning electron microscope.The remaining specimens were processed by sinteringinto cylindrical veneering ceramic that was diameter of3mm and height of3mm onzirconia surface, then were made of standard shear bond test specimen（14mmdiameter,5mm height）.Used electronic universal dynamometer to measure maximum shear bond stress（N）, calculated the shear bond strength（MPa）, observed the interfaceshear damage of specimen and recorded the destruction form, analyzed the obtaineddata by using the statistical software SPSS16.0.Result:1. Analyzed the value of the shear bond strength test on different sandblastingconditions by three factors factorial analysis, the result shows:⑴The main effect of factor "particle" had statistical significance（P<0.01）,threekinds of sandblasting powder with different particle was significant on SBS（ShearBond Strength）.⑵The main effect of factor "pressure" had statistical significance（P<0.01）,three kinds of sandblasting powder with different pressure was significant on SBS.⑶The main effect of factor "time" had statistical significance（P<0.01）, threekinds of blasting powder with different time was significant on SBS.⑷There was interaction between the factor "particle" and the factor "pressure"（P<0.05）.⑸There was interaction between the factor "particle" and the factor "time"（P<0.05）.⑹There was interaction in the three factors （P<0.01）.2. Analyzed the value of shear bond strength test on different sandblastingconditions by One-way ANOVA and compared each two groups by LSD test.⑴To "particle" for the analysis factor, when the sandblasting conditions wereB2C3、B3C1、B3C2,the SBS of group A1was the maximum; when the sandblastingcondition was B2C2、B3C3,the values of SBS both group A1and A2were the same andmore than group A3; when the sandblasting conditions were B1C3、B2C1,the SBS ofgroup A3was the maximum.⑵To " pressure " for the analysis factor, when the sandblasting condition wasA3C3,the SBS of group B1was the maximum; when the sandblasting conditions wereA1C2、A1C3、A2C2、A2C3、A3C1、A3C2,the SBS of group B2was the maximum; Whenthe sandblasting condition was A2C1, the values of SBS both group B2and B3werethe same and more than group B1;when the sandblasting condition was A1C1,the SBSof group B3was the maximum. ⑶To " time " for the analysis factor, when the sandblasting conditions wereA1B3、A2B3、A3B3,the SBS of group C1was the maximum; when the sandblastingconditions were A1B2、A2B2、A3B2,the SBS of group C2was the maximum; when thesandblasting condition was A3B1,the SBS of C3was the maximum.3. The difference between4groups of blocks（P<0.01）,the shear bond strengthof sandblasting group was the maximum（P=34.10±0.97MPa）,and the shear bondstrength of grinding group was the minimum（P=24.84±0.21MPa）. Compared eachtwo groups by LSD,control group> grinding group（P<0.01）;sandblasting group>control group （P<0.01）; sandblasting group> sandblasting+grinding group（P<0.01）;sandblasting+grinding group> control group（P<0.05）.4. Failure mode was the main interface failure between zirconia and veneeringceramic.Conclusion:1. Shear bond strength was the maximum when zirconia be sandblasted for20swith75μm and110μm alumina at0.4Mpa pressure in this vitro study.2. The shear bond strength between zirconia and veneering ceramic was theminimum when sandblasted for30s with150μm alumina at a pressure of0.6MPa inthis vitro study.3. Grinding treatment decreased the shear bond strength between zirconia andveneering ceramic.Zirconia surface avoids grinding processing, if it have beengrinded then should be sandblasted.

Related Dissertations

  1. Ceramic Theramal Sterss Cleaving Technology Based on Laser,TQ174.62
  2. Studies on the Key Technology of the Grinding Device for the Polymer Particles,TQ315
  3. 12-Tungstophosphoric Acid Modified-Zirconia Aerogel as a Solid Acid for THF Polymerization,TQ316.314
  4. Different metal base and binder zirconia all-ceramic crowns on the color of,R783
  5. The Effect of Core:veneer Thickness Ratio on the Flexural Strength of Layered Zirconia and Porceplain Dental Ceramic Materials,R783.1
  6. Preparation and Performances of Aluminum Oxide Coated Zirconia Composite Powders,TB383.3
  7. Study on Optimum Design of Super-high Speed Hybrid Journal Bearing Parameters,TH133.36
  8. Study on Ultrasonic Grinding Mechanism for Engineering Ceramics,TQ174.1
  9. Steady-State Optimization of Grinding Process Based on NSGA Ⅱ Algorithm,TD921.4
  10. Study on Dressing Device and Process for Diamond Roller Wheel,TG743
  11. Study on the Rutile Titanium Dioxide Superfine Comminution and Surface Treatment,TQ621.12
  12. Steady-state Identification and Optimization of Grinding Process,TD921.4
  13. Research on Grinding and Classification Process Control of Sijiaying Concentrator,TP29-A1
  14. Parameters Optimization and Surface Quality Analysis on High-Precision Spherical Grinding,TG580.6
  15. Modified LaMnO 3 perovskites for catalytic combustion of low concentration methane,O643.36
  16. DEIPA, EDIPA synthesis and properties of the cement,TQ172.1
  17. The Effect of Tooth Root Grinding Form of Carburized and Quenched Gear on Bending Strength,TG580.2
  18. The Research of the Impact of the Pulp Viscosity on Grinding Efficiency of Exi High Phosphorus Oolitic Hematite,TD951
  19. Experimental Research of Beneficiation Process on the Recovery of Copper、Iron、Cobalt、Gold、Sliver from a Primary Ore in Hubei,TD913
  20. Yttria stabilized zirconia - Preparation of lanthanum composite oxide silicate ion conductor , and the conductive mechanism associated,TB383.1
  21. Kinetics Research on Desulfurization from Coal by Grinding and Chemical Method,TQ533

CLC: > Medicine, health > Oral Sciences > Oral orthotics > Oral Technology
© 2012 www.DissertationTopic.Net  Mobile