Preparation and in Vitro Degradation of Poly(propylene Fumarate)/(calcium Polyphosphate/calcium Sulphate) Composites

Author: XinYu
Tutor: YangDeAn
School: Tianjin University
Course: Materials Science
Keywords: poly(propylene fumarate) CaSO4 calcium polyphosphate in vitro degradation composites
CLC: R318.08
Type: Master's thesis
Year: 2012
Downloads: 1
Quote: 0
Read: Download Dissertation

Abstract


In this study, a two-part bone tissue engineering scaffold which consists of solidpoly（propylene fumarate）（PPF） matrix and calcium polyphosphate/calcium sulphate（CPP/CaSO4） filler was investigated. This new material can form pores in situ, andkeep enough compressive strength in a certain time after the pores formed.Poly（propylene fumarate）（PPF） was synthesized by a two-step method, andcharacterized with1H-NMR and GPC. We fabricated calcium polyphosphate powder,and then we investigated on the preparation of porous spherical CPP/CaSO4granules.PPF/CPP/CaSO4composites were formed by using N-vinyl pyrrolidinone （NVP） as acrosslinking monomer, benzoyl peroxide （BPO） as a radical polymerization initiator,N, N-dimethyl-p-toluidine （DMPT） as an accelerator, and CPP/CaSO4granules asfiller. The phase composition of CPP/CaSO4granules sintered at differenttemperatures and degradation product was analyzed by X-ray powder diffraction（XRD）; the degradation behavior of composites were investigated by weight loss,water absorption and swelling degree; the morphology change was observed by scanelectron microscope （SEM）.The phase composition of CPP/CaSO4granules was effected by sinteringtemperature and CPP/CaSO4ratio. All the armorphous CPP crystallized to β-CPP inthe CPP/CaSO4granules sintered at580℃. Yet, for the CPP/CaSO4granules sinteredat560℃, the more CaSO4content, the less β-CPP crystallization. Thus it can beconcluded that the addition of CaSO4could inhibit the devitrification of CPP.The in vitro biodegradation property of PPF/CPP/CaSO4composites wasexamined by using cylindrical specimens with length of5mm and diameter of6mm.The composite degradated faster with a higher CaSO4content or a higher NVP/PPFratio. The compressive strength decreased with the decrease of NVP/PPF ratio and theincrease of the CaSO4content.

Related Dissertations

  1. Study on Characteristics of Contiuous Fiber-Reinforced Metal Matrix Composites under Hypervelocity Projectile Impact,TB332
  2. Preparation and Tribological Properties of TZ3Y20A-SrSO4 Ceramic Matrix Composites,TB332
  3. Reactive Hot-Pressing and Mechanical Properties of （ZrB2-ZrO2）/BN Composites,TB332
  4. Closed thin-walled beams composite modal damping prediction,TB33
  5. Preparation, Characterization, and Application in Polymer Composites of Graphene,TB383.1
  6. B Academy \,F272
  7. Development of Bionic Lightweight Basalt Fiber Reinforced Wood Plastics Composite Materials,TB332
  8. Synthesis and Visible Light-Driven Photocatalytic Performances of Silver Halide/Conducting Polymer Nanocomposites,TB383.1
  9. Studies on the Preparation and Properties of CSM/Modified Compound K Composites,TB332
  10. Control of the Microstructure of Cu/ldpe Composites and Its Influence on Their Properties,TB333
  11. Formation of PVB-ZrO2 Hybrid Films for Laminated Glass,TB383.2
  12. Reaction Sintering Preparation of Titaniferous Compound Ceramic Composites by Two-step Method,TQ174.1
  13. Studies on Damping Modification of Fiber Reinforced Composites,TB332
  14. Synthesis of Hollow Glass-Ceramics Microspheres Via Template Method,TQ171.733
  15. A Study on the Environmentally Friendly Methods for Preparation of Graphene and Its Composites,TB383.1
  16. The Studies of the Magnetostriction in Double Perovskite Oxide,O614.411
  17. Studies on Genotoxicity of Two Novel Contraceptive Materials,R114
  18. Layered Ppy / CRGO Nanocomposites Preparation and Application in Supercapacitors,TM53
  19. Nitrogen oxide silicon nitride ceramic fiber reinforced ceramic matrix composites through the waves and Properties,TB332
  20. C / C composites MoSi 2 -Cr-Si/SiC based high temperature oxidation Composite Coating,TG174.4
  21. Research on Recogition Method of Acoustic Emission Signals from Composite Material Damage Based on Wavelet Neural Network,TB33

CLC: > Medicine, health > Basic Medical > Medical science in general > Biomedical Engineering > General issues > Biomaterial
© 2012 www.DissertationTopic.Net  Mobile