Preparation and Characterization of Stainless Steel Hollow Fiber Support Membrane

Author: BaiZuo
Tutor: XuZhenLiang
School: East China University of Science and Technology
Course: Chemical Engineering
Keywords: Stainless steel support membrane Hollow fiber membrane NIPS Preparation Characterization
CLC: TB383.2
Type: Master's thesis
Year: 2012
Downloads: 32
Quote: 0
Read: Download Dissertation

Abstract


In this paper, stainless steel support membrane precursor was prepared by non solvent induced phase separation (NIPS) method and was sintered to become stainless steel support membrane which was characterized by various methods including density, porosity, maximum diameter, mechanical properties, flux, SEM and so on. The effect of preparing process on membrane performance after sintering was also explored.Firstly, stainless steel powder casting solution with different polymer including polyacrylonitrile (PAN), polysulphone (PSF), polyethersulfone (PES) were prepared. The rheological property and stability of different casting solution were also studied and the result showed that the casting solution viscosity went down as the shear rate went up and grew up as the content of polymer increased. At last, PAN was chosen as the proper polymer of casting solution.Secondly, the shape of PAN system hollow fiber support membrane precursor prepared by using NIPS method was better when viscosity of casting solution was about 10000 mPas. The density and mechanical properties of support precursor went up as the content of PAN went up while the porosity went down. A little bit additive PVP could improve the density, porosity and mechanical properties of membrane precursor.Thirdly, stainless steel hollow fiber support membrane was prepared after the precursor was sintered. As the content of PAN increased, the microscopic structure of support membrane became compact resulting in the increase of density and mechanical strength and decrease of porosity, maximum diameter and pure water flux. As the temperature (1100 to 1350 C) grew up, the density and mechanical strength of the support increased while the porosity, maximum diameter and pure water flux decreased. As the content of H2 in the atmosphere became more, the density and mechanical strength of support membrane became less while the porosity, maximum diameter and pure water flux became more.At last, it is better to add 0.5%PVP to improve the compactness of support membrane after sintering which can also increase the density and mechanical performance. The mechanical strength of support membrane was obviously increased after adding 5% aluminum powder which was almost three times higher than that without aluminum powder, while the pure water flux was obviously lessened. The pore diameter of support membrane could be lessened a little after adding aluminum powder. The pure water flux of support membrane sintered in different conditions went down to a stable value as time flowed.

Related Dissertations

  1. Experiment Study on the Effect of Hybrid Coat in Closing of Dentinal Tubules,R781.2
  2. Preparation, Separation of Monascus Pigments and Structural Characterization of Monascus Yellow Pigment,TS264.4
  3. Crude oil loading system transformation project management research,F284
  4. New water-based whiteboard ink water development,TS951.23
  5. The legendary revolutionary history teleplays research,J905
  6. Intercultural Communication in the Media Construction of National Image,G206
  7. Studies on Isotretinoin Loaded Solid Lipid Nanaparticles Gel,TQ460.6
  8. Cloning, Overexpression and Characterization of Xylanase from Caldicellulosiruptor Bescii DSM 6725,Q78
  9. Preliminary Study on the Chemical Compositions and Bioactivities of Syringa Pinnatifolia Hemsl.Var.Alashanensis Ma Et S.Q.Zhou,R29
  10. Influence of Oil Droplet/Bubble Size on Dissolved-Air Flotation of Oily Wastewater,X703
  11. Development and Application of Oxygen Restoration Preparation on Polluted Water Body Sediment,X52
  12. The Preparation of Electrophoretic Display Microcapsules and the Building of Y-Shape Micro Channel Reactor,TB383.4
  13. Novel Functional Hexaarylbenzene Derivatives: Synthesis and Properties of Hexakis [3-(3’-Thienyl) Phenyl] Benzene Derivatives,TQ251.2
  14. Alginate / modified bacterial cellulose blend fiber preparation and properties of,TQ342
  15. Sea buckthorn seed proanthocyanidins comparative study of different degradation methods,S793.6
  16. Preparation and properties of heat-cured pigment dispersions,TS190.2
  17. Isolation and identification of Sal A Study on the Preparation and related substances,TQ463.2
  18. Mathematical Problem Solving for the Visual-Spatial Presentation and Instructional Strategy,G623.5
  19. Preparation and Evaluation of Aidi Lyophilized Powder for Injection,R286
  20. Solid base catalysts and their catalytic synthesis reaction of isophorone Performance,TQ224.2
  21. Studies on Pine Pollen Broken Technology and Development of Health Food,TS218

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile