Research of Graphitized Needle Coke Coated by Phenolic Resin Pyrolytic Carbon as Anode Material for Lithium Ion Battery

Author: ZhaoYue
Tutor: QiaoWenMing
School: East China University of Science and Technology
Course: Chemical processes
Keywords: lithium ion battery needle coke phenolic resin coating
CLC: TM912
Type: Master's thesis
Year: 2012
Downloads: 193
Quote: 0
Read: Download Dissertation

Abstract


Graphitized needle coke was used as anode material for lithium ion battery (LIB) in this paper. The LIB anode material with outstanding performance in capacity, efficiency and cycle abilities was prepared by phenolic resin coating, surface oxidation and oxidation-coating. The influence of the amount of resin, carbonization temperature and surface oxidation-coating on the composites’ microcrystalline structure and electrical performances were studied.The composite needle coke was prepared by solidifying phenolic resin on the surface. Then the influence of the amount of resin and carbonization temperature was discussed, and it turned out that the the first charge and discharge efficiency of the composite increased and then decreased along with the increasing amount of resin and temperature of carbonization. The results indicated that the composites’performance was best when it had 20% phenolic resin and then carbonized under 800℃, the first charge capacity and charge-discharge efficiency were 328.19mAh/g and 87.85%, the charge capacity after 50 cycles still remains 309.59 mAh/g, and the capacity retention rate was 83.06%.After surface oxidized by H2O2 and coated by phenolic resin, this new composites’ crystal structure and electrical performance was studied. It is found that surface oxidation can change the type of functional groups of the material and improve the compatibility of needle coke with the electrolyte. The results showed that the composite which coated 20% phenolic resin after surface oxidized by 30% H2O2 exhibited good electrochemical performance, the first charge capacity and charge-discharge efficiency were 358.26mAh/g and 90.56%, the charge capacity after 50 cycles still remains 340.66mAh/g, and the capacity retention rate was 86.04%. These researches were important to develop anode materials for lithium ion battery with low-cost and good electrochemical performance.

Related Dissertations

  1. Preparation of Based on the Phenolic Resin of Activated Carbon and Adsorption-Photopcatalytical Character of Supported TiO2,TQ424.19
  2. Preparation and Properties of Silicon Carbon Anode for Lithium Ion Battery,TM912.9
  3. The Effect of Current Density and Electric Field on Ni and Its Alloy Electrodeposition for Copper Crystallizer,TQ153.2
  4. A Study on the Electrodeposition of Zn-Co and Zn-Ni Alloys in the Reline Room Temperature Ionic Liquid,TQ153.1
  5. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  6. Preparation and Performance of V2O5-WO3/MOx/Cordierite Catalyst Modified with Cu、Mn、Ce for DeNOx,X701
  7. Research on PSA/Cotton Blend Fabric of Coatinging of Water Resistance and Moisture Permeability,TS195.6
  8. Study on Chitosan-Based Composiate Nano-Coating Dope and Its Effect of Fresh-Keeping for Coated Egg,TS253.2
  9. Development and Application of Biological Seed Coating Formulation for Soybean,S565.1
  10. Research on Microstructures and Properties of FeMnCrNiAlBSi/Cr3C2 Coatings,TG174.44
  11. Study on Single and Combined Toughening Phenolic Foam and Flame Retardant Properties,TQ328
  12. Research of Properties and Preparation Technology of Multiphase Ceramic Coating with Reactive Flame Spraying Process on AZ31B,TG174.44
  13. Study Report on Demolition and Enteric-coated Potassium Sodium Dehydroandroan Drographolide Succinate Pellets,R283
  14. Preparation and Modification of Lithium Ion Battery LiNi0.8Co0.05O2 Cathode,TM912
  15. Antibacterial plastic with silver coating developed,TQ637
  16. Needle Coke Powder Molding Process and Its Impact on the Performance of Carbonization Products,TQ127.11
  17. The Study of Microstructure and Performance of La2 O3+CeO2-Ni-WC Composite Coating by Vacuum Fusion Sintering,TG174.44
  18. Effect of Water Binder on the Electrochemical Performance of Graphite,TM912
  19. Structure and Performance of Fe-based Amorphous Coatings Prepared by HVAF and HVOF,TG174.4
  20. A Study of Adhesive Thin-Film Layer Drying Process,TQ430
  21. Study lithium titanate prepared from ilmenite,TM912

CLC: > Industrial Technology > Electrotechnical > Independent power supply technology (direct power) > Battery
© 2012 www.DissertationTopic.Net  Mobile