Study on the Thermal Insulation Porous Ceramics

Author: WuChaoQi
Tutor: WangZhongJian
School: East China University of Science and Technology
Course: Materials Science and Engineering
Keywords: Spinel porous ceramics pore structure foaming method thermal properties
CLC: TQ174.1
Type: Master's thesis
Year: 2012
Downloads: 109
Quote: 0
Read: Download Dissertation

Abstract


Thermal insulation porous ceramics require high porosity, small and uniform distribution of the pores and high compressive strength. In this paper,the porous ceramics were firstly prepared by slip casting process, and sintered at high temperature. Then, the thermal propertyies, crystalline phase, sintering and mechanical properties of the ceramics were characterized by XRD diffraction, Archimedes’s method and other analytical methods. In addition, the impact of mineralizer ZnO on MgO-Al2O3 system ceramics crystalline phase was investegated. MgO-Al2O3 system porous ceramics were prepared to study the mechanical properties and the structure of pore by compressive strength testing and microscopic image analysis. Finally, the relationship between the pore structure and the thermal properties of porous ceramics was discussed.The results show:(1) The ceramics was developed by sintering at 1500℃/3hrs. and composed of 50mol% MgO and 50mol% Al2O3, plus 3wt.% mineralizer ZnO. The crystalline phase of ceramics was MgAl2O4 phase. The density of the ceramic was 2.659g/cm3 and linear shrinkage rate was 2.45%.(2) The porous ceramics were prepared and composed of 50mol% MgO and 50mol% Al2O3, added 3wt.% Zinc oxide,0.5wt.% the foaming agent sodium dodecyl benzene sulfonate and 32wt.% of water, adjusted the slurry temperature and the PH value of the slurry. The pores of the porous ceramics were closed. Porosity was 59.77% and average pore size of the sample was 50μm. Compressive strength was 174.58MPA.(3) When the average pore size of the porous ceramics was same, the greater the porosity, the better the thermal insulation properties. When the porosity of the samples was same, the smaller average pore size, the better the thermal insulation properties.

Related Dissertations

  1. Rock-fill Concrete Experiments on Comprehensive Properties and Studies on Thermal Stress,TU528
  2. Study on the Synthesis and Properties of Copolyimides Derived from ODPA/Isomeric ODA,TQ323.7
  3. Fire Retardancy Performance of Poly (Ethylene Terephthalate) Containing Melamine Cyanurate,TB383.1
  4. Preparation of Activated Carbon from Tobacco Stems and Application for Low Concentration Phosphine Adsorption,X712
  5. Curing Mechanism and Properties of Fluorenyl Epoxy Resin,TQ323.5
  6. Preparation and Photocatalytic Properties of Semiconductor Oxides,O643.36
  7. Preparation and Properties of Filtering Ceramics for High Temperature Exhaust Gas,TQ174.6
  8. Preparation and Research of New Type Visible-light Active Photocatalyst BIVO4,O643.36
  9. Preparation and Properties of the New Glass Infiltrated 3Y-TZP All Ceramic Dental Materials,TQ174.75
  10. Study of Alpaca Modulation and Thermal Properties & Supplier Opening Optimization,TS102.31
  11. Processing and Property Study of Mg2TiO4 -based Microwave Dielectric Ceramics,TN04
  12. Study on Uncertainty of the Rock-soil Thermal Response Test in Ground-Coupled Heat Pump System,TU831
  13. Doped cobalt ferrite composites and their properties,TB383.1
  14. Study on Materials Composition Design Method and Performance Variation of Skeleton-pore Cement Stabilized Aggregate Base,U414
  15. Study on the Hydrothermal Synthesis of Spinel-type Lithium Ion-sieve and Ni-Cr Doping,P579
  16. Experimental study of Panzhihua Iron and Steel blast furnace slag foundation soil properties and thermophysical properties,TU411
  17. Phosphorus zinc germanium infrared crystal growth and properties of,O782
  18. An Experimental Study on Adsorption of NO and Adsorption of NO and SO2 Together Over Modified Activated Carbon Fibers,X701
  19. Study on the Nanocrystalline MgAl2O4 Spinel Powder Prepared by Microwave-assisted Low-temperature Combustion Synthesis Technology,TB383.1
  20. A Study of Spinel Ferrite and Its Composite Materials,TB383.1

CLC: > Industrial Technology > Chemical Industry > Silicate > Ceramic Industry > Basic theory
© 2012 www.DissertationTopic.Net  Mobile